Energy-saving kiln material and preparation method thereof

A kiln furniture and raw material technology, which is applied in the field of energy-saving kiln furniture materials and its preparation, can solve the problems of weak deformation resistance at high temperature, short service life, and low flexural strength at room temperature, and achieve strong deformation resistance at high temperature and flexural resistance at room temperature High strength and good thermal shock stability

Inactive Publication Date: 2013-03-20
GUANGDONG SHUNXIANG PORCELAIN
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing kiln furniture has poor thermal shock stability, unstable volume, low normal temperature flexural strength, and weak high temperature deformation resistance, resulting in short service life and poor use effect
Generally, after more than 2,000 times of kiln recycling, it will crack and damage, resulting in deformation, slag and other problems of porcelain. In severe cases, the kiln may even be inverted, which is a serious waste of resources and reduces production efficiency.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] An energy-saving kiln furniture material is composed of the following raw materials calculated by weight percentage: 35% aluminum oxide, 58% silicon oxide, and 7% magnesium oxide.

[0026] The preparation method of the energy-saving kiln furniture material includes the following steps:

[0027] (1) Mix and grind each raw material according to the proportion of the component formula, carry out wet ball milling, and fully mix;

[0028] (2) Sieve until 0.03% remains on the 10,000-hole sieve, and ball mill again to obtain slurry;

[0029] (3) Inject the slurry into the mold and cast it under the pressure of 90-100Mpa to form the blank;

[0030] (4) Place the blank in a hot-press furnace, slowly raise the temperature, and sinter at a temperature of 1400°C. The entire sintering process lasts about 8 hours and is kept for 0.5-1 hour;

[0031] (5) Cool it down to room temperature according to the set cooling curve to obtain the energy-saving kiln furniture material.

[0032]...

Embodiment 2

[0034] An energy-saving kiln furniture material is composed of the following raw materials calculated by weight percentage: 37% of aluminum oxide, 55% of silicon oxide, and 8% of magnesium oxide.

[0035] The preparation method of the energy-saving kiln furniture material includes the following steps:

[0036] (1) Mix and grind each raw material according to the proportion of the component formula, carry out wet ball milling, and fully mix;

[0037] (2) Sieve until the remainder is 0.02% through the 10,000-hole sieve, and ball mill again to obtain the slurry;

[0038] (3) Inject the slurry into the mold and cast it under the pressure of 90-100Mpa to form the blank;

[0039] (4) Place the blank in a hot-press furnace, slowly raise the temperature, and sinter at a temperature of 1300°C. The entire sintering process lasts about 8 hours and is kept warm for 0.5-1 hour;

[0040] (5) Cool it down to room temperature according to the set cooling curve to obtain the energy-saving ki...

Embodiment 3

[0043] An energy-saving kiln furniture material is composed of the following raw materials calculated by weight percentage: 41.5% of aluminum oxide, 50% of silicon oxide, and 8.5% of magnesium oxide.

[0044] The preparation method of the energy-saving kiln furniture material includes the following steps:

[0045] (1) Mix and grind each raw material according to the proportion of the component formula, carry out wet ball milling, and fully mix;

[0046] (2) Sieve until the remainder is 0.04% through the 10,000-hole sieve, and ball mill again to obtain the slurry;

[0047] (3) Inject the slurry into the mold and cast it under the pressure of 90-100Mpa to form the blank;

[0048] (4) Place the blank in a hot-press furnace, slowly raise the temperature, and sinter at a temperature of 1350°C. The entire sintering process lasts about 8 hours and is kept for 0.5-1 hour;

[0049] (5) Cool it down to room temperature according to the set cooling curve to obtain the energy-saving kil...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an energy-saving kiln material and a preparation method of the energy-saving kiln material. The energy-saving kiln material is prepared from the following intergradient in proportioning: 35-42% of alumina, 50-58% of silicon oxide and 6.5-8.5% of magnesium oxide. The preparation method comprises the following steps of ball-milling, screening, further ball-milling, casting molding, sintering and the like so as to obtain the energy-saving kiln material ultimately. The kiln material is high in normal temperature breaking strength and strong in high temperature non-deformability, and can be widely used in kiln furnaces with large bearing quantity and long service life; by utilizing the product, the output can be improved, and the consumption of raw materials and energy is reduced with high efficiency, energy conservation and production cost conservation; and the production process is simple, so that the energy-saving kiln material is applicable to large-scale production.

Description

technical field [0001] The invention relates to the field of kiln furniture materials, in particular to an energy-saving kiln furniture material and a preparation method thereof. Background technique [0002] Sintering ceramic blanks is one of the necessary steps in the production of ceramic products. Kiln furniture plays a role in supporting and protecting the blank during the firing process of ceramic products. Its performance is related to the quality of the fired product and the amount of energy consumed, thus affecting the firing cost. Therefore, the kiln The quality of furniture plays a decisive role. [0003] The existing kiln furniture has poor thermal shock stability, unstable volume, low normal temperature flexural strength and weak high temperature deformation resistance, resulting in short service life and poor use effect. Generally, after more than 2,000 times of kiln recycling, the kiln will crack and be damaged, resulting in problems such as deformation and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/66
Inventor 许名传
Owner GUANGDONG SHUNXIANG PORCELAIN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap