A far-infrared heating film and far-infrared heating technology, which is applied in the field of far-infrared blankets, can solve the problems of inability to arbitrarily cut, can not play a health care role, and fix the size, so as to eliminate the generation of static electricity and sparks, and facilitate folding and storage. Effects of transport, improved flexibility and tensile strength

Active Publication Date: 2013-03-20
SHANDONG LEKANG ELECTRICAL TECH
View PDF5 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the far-infrared heating film in the prior art and the heating equipment made of it all have the following deficiencies due to the limitations of materials and processes: 1. The electrothermal conversion rate is low, and the electric energy cannot be fully utilized, which wastes energy; 2. The emission of infrared rays is unstable, and the wavelength of far-infrared rays cannot be stabilized in the most beneficial wave band for human health, so it cannot play a role in health care; three, the hardness is too high, it is difficult to fold, making storage and transportation difficult; four, it cannot Random cutting, fixed size, small application range; five, prone to current leakage, easy to generate static electricity and sparks, low safety performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flexible far-infrared heating film, preparation method thereof and far-infrared blanket produced through same
  • Flexible far-infrared heating film, preparation method thereof and far-infrared blanket produced through same
  • Flexible far-infrared heating film, preparation method thereof and far-infrared blanket produced through same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] like figure 1 and figure 2 As shown together, a flexible far-infrared heating film includes a far-infrared heating layer 11, electrodes 14 are implanted on both sides of the far-infrared heating layer 11, and the extension direction of the electrodes 14 is consistent with the extension direction of the far-infrared heating layer 11. A flexible insulating layer 12 is attached to the front and back surfaces of the far-infrared heating layer 11, and a metal shielding layer 13 is attached to the outside of the two-layer flexible insulating layer 12; the far-infrared heating layer 11 is formed by mixing conductive ink and far-infrared emitting agent. The far-infrared emitting agent is carbon crystal, wherein the conductive ink=3 parts by weight, and the far-infrared emitting agent=1 part by weight. Since the far-infrared heating layer 11 is formed by mixing the conductive ink and the far-infrared emitting agent, and the conductive ink and the far-infrared emitting agent ar...

Embodiment 2

[0056] like figure 1 and figure 2 Commonly shown, a kind of flexible far-infrared heating film, its structure is basically the same as embodiment one, difference is: far-infrared heating layer 11 is mixed by conductive ink and far-infrared emission agent, and far-infrared emission agent is carbon crystal , wherein conductive ink=4 parts by weight, far-infrared emitter=2 parts by weight.

[0057] The preparation method of the above-mentioned flexible far-infrared heating film, its steps are basically the same as in Example 1, the difference is: the conductive ink in step 1) is mixed with the far-infrared emitting agent according to the ratio of 4:2 parts by weight, and stirred to form a liquid mixture spare.

[0058] like image 3 , Figure 4 and Figure 5 Commonly shown, a kind of far-infrared carpet that is made by above-mentioned far-infrared heating film, its structure is basically identical with embodiment one, difference is: the far-infrared heating film 31 that is ...

Embodiment 3

[0060] like figure 1 and figure 2 Commonly shown, a kind of flexible far-infrared heating film, its structure is basically the same as embodiment one, difference is: far-infrared heating layer 11 is mixed by conductive ink and far-infrared emission agent, and far-infrared emission agent is carbon crystal , wherein conductive ink=5 parts by weight, far-infrared emitter=3 parts by weight.

[0061] The preparation method of the above-mentioned flexible far-infrared heating film, its steps are basically the same as in Example 1, the difference is: the conductive ink in step 1) is mixed with the far-infrared emitting agent according to the ratio of 5:3 parts by weight, and stirred to form a liquid mixture spare.

[0062] like image 3 , Figure 4 and Figure 5 Commonly shown, a kind of far-infrared blanket that is made by above-mentioned far-infrared heating film, its structure is basically the same as embodiment one, and difference is: the far-infrared heating film 31 that i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a flexible far-infrared heating film, a preparation method thereof and a far-infrared blanket produced through same and relates to the technical field of heating films. The heating film comprises a far-infrared heating layer, wherein electrodes are arranged on two sides of the heating film, the extension direction of the electrodes is identical with the extension direction of the far-infrared heating layer, a flexible insulating layer is attached to the positive and the negative of the far-infrared heating layer respectively, metal shielding layers are attached to outsides of two flexible insulating layers, the far-infrared heating layer comprises, by weight, 3-5 parts of conductive ink and 1-3 parts of far-infrared emitting agent and the conductive ink and the far-infrared emitting agent are mixed to form the far-infrared heating layer. The technical problems that in the prior art, the far-infrared heating device is high in hardness, instable in emitted far-infrared heating rays and poor in safety performance are solved. The heating film and the far-infrared blanket produced through the heating film are good in flexibility, stable in emitted far-infrared heating rays and good in use safety performance.

Description

technical field [0001] The invention relates to the technical field of electrothermal film, in particular to a flexible far-infrared heating film, a preparation method thereof and a far-infrared blanket manufactured therefrom. Background technique [0002] Electrothermal film heating is one of the emerging heating methods in the world. It is a new heating method that uses electric energy as the source and conducts heat transfer through infrared radiation. Because of its excellent properties such as high pressure resistance, moisture resistance, wide temperature range, high toughness and low shrinkage, it has been more and more widely used. At present, the far-infrared heating film in the prior art and the heating equipment made of it all have the following deficiencies due to the limitations of materials and processes: 1. The electrothermal conversion rate is low, and the electric energy cannot be fully utilized, which wastes energy; 2. The emission of infrared rays is unst...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H05B3/34H05B3/10
Inventor 张敬瑶
Owner SHANDONG LEKANG ELECTRICAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap