A technology of polycarbonate and multiaxial impact, which is applied in the field of high multiaxial impact polycarbonate composition and its preparation, can solve the problem of no way to simulate the application field, and achieve good dispersion effect
Active Publication Date: 2014-10-22
SHANGHAI KUMHO SUNNY PLASTICS
View PDF4 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Although several companies have developed high-impact PC / ABS, this refers to notch impact, and there is no way to simulate real application fields, so it is important to develop polycarbonate compositions with high multiaxial impact
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0034] (1) Weigh each component by weight: PC is L1250Y:50, ABS is ABS839140, toughening agent EM50510, antioxidant 10100.1, antioxidant 1680.1, lubricant PETS 0.3.
[0035] (2) Divide the raw materials into two parts, part A includes PC, antioxidant, lubricant, part B includes ABS and toughening agent. Premix parts A and B separately in a high speed mixer.
[0036] (3) Add the premix into the twin-screw extruder, feed part A from the main feeding port, and feed part B from the side feeding port, melt and extrude at 200-280 ° C, screw extruder The rotational speed is 300rpm, the pressure is 2MPa, and the product is obtained through melt extrusion and granulation.
Embodiment 2
[0038] (1) Weigh each component by weight: PC is PC-200-3:60, ABS is ABS351335, toughening agent EM500A5, antioxidant 10100.1, antioxidant 1680.1, lubricant PETS 0.3.
[0039] (2) Divide the raw materials into two parts, part A includes PC, antioxidant, lubricant, part B includes ABS and toughening agent. Premix parts A and B separately in a high speed mixer.
[0040] (3) Add the premix into the twin-screw extruder, feed part A from the main feeding port, and feed part B from the side feeding port, melt and extrude at 200-280 ° C, screw extruder The rotational speed is 500rpm, the pressure is 2MPa, and the product is obtained through melt extrusion and granulation.
Embodiment 3
[0042] (1) Weigh each component by weight: PC is PC-200-3:60, ABS is ABS351335, toughening agent M5215, antioxidant 10100.1, antioxidant 1680.1, lubricant PETS 0.3.
[0043] (2) Divide the raw materials into two parts, part A includes PC, antioxidant, lubricant, part B includes ABS and toughening agent. Premix parts A and B separately in a high speed mixer.
[0044] (3) Add the premix into the twin-screw extruder, feed part A from the main feeding port, and feed part B from the side feeding port, melt and extrude at 200-280 ° C, screw extruder The rotational speed is 500rpm, the pressure is 2MPa, and the product is obtained through melt extrusion and granulation.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
particle diameter
aaaaa
aaaaa
melt flow index
aaaaa
aaaaa
melt flow index
aaaaa
aaaaa
Login to View More
Abstract
The invention relates to a high multi-axis impactpolycarbonate composition and a preparation method of the high multi-axis impactpolycarbonate composition. The composition comprises the following components in parts by weight: 50-70 parts of polycarbonate resin PC, 25-50 parts of polybutadiene-acrylonitrile-styrenecopolymer resin ABS, 2-10 parts of toughening agent, 0.1-1 part of an antioxidant and 0.1-1 part of a lubricant. The preparation method of the high multi-axis impact polycarbonate composition comprises the following steps of: dividing raw material into parts A and B, wherein the part A comprises the PC, the antioxidant and the lubricant while the part B comprises the ABS and the toughening agent; and respectively premixing the parts A and B in a high-speed mixer, subsequently adding the premixed materials into a double-screw extruder, feeding the part A from a primary feeding opening and feeding the part B from a secondary feeding opening, fusing and extruding at 200-280 DEG C with the rotation speed of the screw extruder at 200-600rpm and the pressure at 2-3MPa, then fusing, extruding and pelleting to obtain the product. Compared with the prior art, through the special toughening agent, PC and processing technologies, the multi-axis impact performance of the polycarbonate composition provided by the invention is improved.
Description
technical field [0001] The invention relates to the field of polymer materials, in particular to a polycarbonate composition with high multiaxial impact and a preparation method thereof. Background technique [0002] Due to the demand for environmental protection and energy saving, the trend of automobile development is lightweight and high safety performance. The lightweight of the car is to reduce the curb weight of the car as much as possible under the premise of ensuring the strength and safety performance of the car, so as to improve the power of the car, reduce the consumption of dyes, and reduce the exhaust pollution. In order to meet the demand for lightweight vehicles, both metal parts and plastic parts are reducing weight. Especially for plastics, when the thickness is reduced, it needs to meet the requirements of high safety performance, and the requirements for the strength of materials are becoming more and more stringent. Polycarbonate resin is widely used in...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More