Sealed amorphous alloy power transformer

A technology of power transformers and amorphous alloys, which is applied to transformer/inductor cores, circuits, electrical components, etc., can solve the problems of poor energy saving effect, no-load loss, large load loss, etc., and achieve the effect of reducing no-load.

Inactive Publication Date: 2013-04-03
JIANGSU YAWEI TRANSFORMER
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the iron core of existing transformers is still made of traditional silicon steel sheet materials. Compared with amorphous alloy materials, the no-load loss and load loss of traditional silicon steel sheet materials are relatively large, so the energy-saving effect is poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A sealed amorphous alloy power transformer according to the present invention, the iron core of the transformer is made of amorphous alloy material, and the basic elements of the amorphous alloy include iron, nickel, cobalt, boron and carbon, and its weight The percentages are as follows:

[0014] Nickel: 2%;

[0015] Cobalt: 3%;

[0016] Boron: 10%;

[0017] Carbon: 8%;

[0018] The balance is iron.

[0019] Because the amorphous alloy material is an isotropic soft magnetic material, the magnetization power is small, and there is no structural defect that hinders the movement of the domain wall, and it is proved by experiments that the load loss of the present invention is reduced by 15% on the basis of the GB / T6451 standard value , The no-load loss is reduced by 70% based on the GB / T6451 standard group I value, so the use of amorphous alloy materials reduces the no-load and load losses of the transformer, and has the characteristics of safety, reliability, environ...

Embodiment 2

[0021] A sealed amorphous alloy power transformer according to the present invention, the iron core of the transformer is made of amorphous alloy material, and the basic elements of the amorphous alloy include iron, nickel, cobalt, boron and carbon, and its weight The percentages are as follows:

[0022] Nickel: 6%;

[0023] Cobalt: 1%;

[0024] Boron: 5%;

[0025] Carbon: 2%;

[0026] The balance is iron.

[0027] Experiments have proved that the load loss of the embodiment of the present invention is reduced by 12.5% ​​on the basis of the GB / T6451 standard value, and the no-load loss is reduced by 50% on the basis of the GB / T6451 standard group I value.

Embodiment 3

[0029] A sealed amorphous alloy power transformer according to the present invention, the iron core of the transformer is made of amorphous alloy material, and the basic elements of the amorphous alloy include iron, nickel, cobalt, boron and carbon, and its weight The percentages are as follows:

[0030] Nickel: 4%;

[0031] Cobalt: 2%;

[0032] Boron: 6%;

[0033] Carbon: 7%;

[0034] The balance is iron.

[0035] Experiments have proved that the load loss of the present invention is reduced by 18% on the basis of GB / T6451 standard value, and the no-load loss is reduced by 60% on the basis of GB / T6451 standard group I value.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of a power equipment transformer, in particular to a sealed amorphous alloy power transformer. An iron core of the transformer is made of amorphous alloy materials, and the basic elements of amorphous alloy comprise ferrum, nickel, cobalt, boron and carbon. The materials are adopted, therefore the no-load and load loss of the transformer is reduced, and the transformer has the characteristics of safety, reliability, environmental protection, energy conservation and the like. In addition, the sealed amorphous alloy power transformer also has the advantages of inflaming retardance, self extinguishment, moisture prevention, crack resistance, no maintenance and the like, can be widely used for high-rise buildings, commercial centers, metros, airports, stations, industrial and mining enterprises and power plants, and is specially suitable for places with high requirements on fire protection such as inflaming, explosion and the like to install and use.

Description

technical field [0001] The invention relates to the technical field of power equipment transformers, in particular to a sealed amorphous alloy power transformer. Background technique [0002] At present, the iron core of existing transformers is still made of traditional silicon steel sheet materials. Compared with amorphous alloy materials, traditional silicon steel sheet materials have relatively large no-load loss and load loss, so the energy-saving effect is poor. Contents of the invention [0003] The object of the present invention is to provide a safe, reliable and environment-friendly sealed amorphous alloy power transformer which can reduce no-load and load loss. [0004] In order to solve the existing problems in the background technology, the present invention adopts the following technical solutions: a sealed amorphous alloy power transformer, the iron core of the transformer is made of amorphous alloy material, and the basic elements of the amorphous alloy inc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01F1/153H01F27/24
Inventor 杨立稳
Owner JIANGSU YAWEI TRANSFORMER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com