Multiple anti-fake carbon powder and its preparation method

A multiple, toner technology, applied in electrical recording, optics, instruments, etc., can solve the problems of low technical content of anti-counterfeiting toner, low anti-counterfeiting strength, easy imitation, etc. difficult effect

Inactive Publication Date: 2013-05-08
河北佳顺特科印刷有限公司
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to overcome the shortcomings of the existing anti-counterfeiting toner, such as low technical content, easy imitation, and low anti-counterfeiting strength, the purpose of the present invention is to provide a new type of multi-anti-counterfeiting toner with high anti-counterfeiting performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multiple anti-fake carbon powder and its preparation method
  • Multiple anti-fake carbon powder and its preparation method
  • Multiple anti-fake carbon powder and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0025]

[0026] 10 kg of anti-counterfeiting toner is produced in each batch, according to the proportion of the above formula components, and made according to the following steps:

[0027] (1) Evenly mix polymer resin, polypropylene wax, blue pigment, charge regulator and anti-counterfeiting material in a mixer to make a mixture;

[0028] (2) Then put the above mixture into the extruder, and slowly heat it, press the above mixture into tablets at a temperature of 100-155°C, and grind it into powder with a coarse powder machine after cooling:

[0029] (3) After that, use a fine powder machine to further pulverize the above-mentioned pulverized powder, and carry out classification, separation, and collection to obtain a primary product with a particle size of 5--12 μm:

[0030] (4) Add silicon dioxide, dimethyldichlorosilane and hexamethyldisilazane, and mix with a mixer to modify the surface so that the fluidity is greater than 20%.

[0031] (5) Screen with 150--250 mesh ...

example 2

[0034]

[0035]

[0036] 10 kg of anti-counterfeiting ink is produced in each batch, and the proportion of the above formula components is controlled, and the production is made according to the following steps:

[0037] (1) Evenly mix polymer resin, polypropylene wax, blue pigment, charge regulator and anti-counterfeiting material in a mixer to make a mixture;

[0038] (2) Then put the above mixture into the extruder, and slowly heat it, press the above mixture into tablets at a temperature of 100-155°C, and grind it into powder with a coarse powder machine after cooling:

[0039] (3) After that, use a fine powder machine to further pulverize the above-mentioned pulverized powder, and carry out classification, separation, and collection to obtain a primary product with a particle size of 5--12 μm:

[0040] (4) Add silicon dioxide, dimethyldichlorosilane and hexamethyldisilazane, and mix with a mixer to modify the surface so that the fluidity is greater than 20%.

[004...

example 3

[0044]

[0045] 10 kg of anti-counterfeiting ink is produced in each batch, and the proportion of the above formula components is controlled, and the production is made according to the following steps:

[0046] (1) Evenly mix polymer resin, polypropylene wax, black pigment, charge regulator and anti-counterfeiting material in a mixer to make a mixture;

[0047] (2) Then put the above mixture into the extruder, and slowly heat it, press the above mixture into tablets at a temperature of 100-155°C, and grind it into powder with a coarse powder machine after cooling:

[0048] (3) After that, use a fine powder machine to further pulverize the above-mentioned pulverized powder, and carry out classification, separation, and collection to obtain a primary product with a particle size of 5--12 μm:

[0049] (4) Add silicon dioxide, dimethyldichlorosilane and hexamethyldisilazane, and mix with a mixer to modify the surface so that the fluidity is greater than 20%.

[0050] (5) Scre...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a multiple anti-fake carbon powder in an anti-fake material. The multiple anti-fake carbon powder is prepared through adding anti-fake materials into a commercially-available polymer resin, polypropylene wax, a charge adjustment agent, a pigment, silica, dimethyldichlorosilance and hexamethyldisilazane, mixing, extruding, crushing, sieving and the like. The anti-fake materials comprise long and short wave ultraviolet excitation fluorescence, infrared excitation luminescence and chemical discoloration anti-fake materials, and sunlight excitation color-variable, DNA and intelligent spectrum anti-fake materials. The multiple anti-fake carbon powder is suitable for various documents, notes, files and analogues. The multiple anti-fake carbon powder has the advantages of multiple anti-fake functions, reaching of multiple anti-fake purposes through one-time printing, satisfying of different-layering identification requirements, high anti-fake capability, and effective improvement of the anti-fake difficulty.

Description

technical field [0001] The invention belongs to multiple anti-counterfeiting toner in anti-counterfeiting materials, that is, the anti-counterfeiting toner containing multiple anti-counterfeiting functions. Background technique [0002] With the improvement of office automation and informatization level, anti-counterfeiting technology and informatization are organically combined. The signing, use and management of important bills and vouchers need to strengthen anti-counterfeiting, and the signature and seal of archive documents are also automatically printed by laser printers. Instead of traditional manual operation, but the toner with anti-counterfeiting function used by laser printers on the market is single anti-counterfeiting function, low technical content, easy to imitate. Technical content and counterfeiting difficulty are imperative. Contents of the invention [0003] In order to overcome the shortcomings of the existing anti-counterfeiting toner, such as low tec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): G03G9/08G03G9/09
Inventor 不公告发明人
Owner 河北佳顺特科印刷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap