Printing process of polyester fabric

A printing process, polyester fabric technology, applied in the field of textile printing and dyeing, to achieve the effect of promoting the degree of expansion, low energy consumption, and reducing high energy consumption

Inactive Publication Date: 2013-05-15
CHANGSHU QINDA KNITTING PRINTING & DYEING
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a printing process for polyester fabrics, realize continuous low-temperature steaming and color fixation of polyester fabrics with low energy consumption, and effectively solve the problem of high-temperature steaming required for the application of existing disperse dye printing processes to polyester fabric printing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A printing process for polyester fabrics, comprising the steps of printing, steaming, reduction cleaning, and setting and drying;

[0015] Adding low-temperature dyeing carrier in the printing process, the addition is 5% of the color paste weight;

[0016] In the steaming process, the steaming conditions of low temperature and normal pressure are used for steaming, the temperature is 110 ° C, and the time is 7 minutes; ??

[0017] The reduction cleaning solution includes the following components: sodium dithionite 1.5g / L, sodium hydroxide solution with a mass concentration of 35% 6mL / L, penetrant 3g / L;

[0018] The temperature of the reduction cleaning process is 50°C, and the treatment time is 18 minutes;

[0019] The setting and drying process adopts high temperature expansion setting, the temperature is 120°C, and the processing time is 40 seconds.

Embodiment 2

[0021] A printing process for polyester fabrics, comprising the steps of printing, steaming, reduction cleaning, and setting and drying;

[0022] Add low-temperature dyeing carrier in the printing process, the addition amount is 1% of the color paste weight;

[0023] In the steaming process, the steaming conditions of low temperature and normal pressure are used for steaming, the temperature is 90°C, and the time is 5 minutes; ??

[0024] The reduction cleaning solution includes the following components: 0.5 g / L of sodium dithionite, 4 mL / L of sodium hydroxide solution with a mass concentration of 35%, and 3 g / L of penetrant;

[0025] The temperature of the reduction cleaning process is 45°C, and the treatment time is 15 minutes;

[0026] The setting and drying process adopts high temperature expansion setting, the temperature is 110°C, and the processing time is 20 seconds.

Embodiment 3

[0028] A printing process for polyester fabrics, comprising the steps of printing, steaming, reduction cleaning, and setting and drying;

[0029] Add low-temperature dyeing carrier in the printing process, the addition is 7% of the color paste weight;

[0030] In the steaming process, the steaming conditions of low temperature and normal pressure are used for steaming, the temperature is 130°C, and the time is 10 minutes;

[0031] The reduction cleaning solution includes the following components: sodium dithionite 3g / L, sodium hydroxide solution with a mass concentration of 35% 7mL / L, penetrant 3g / L;

[0032] The temperature of the reduction cleaning process is 60°C, and the treatment time is 20 minutes;

[0033] The setting and drying process adopts high temperature expansion setting, the temperature is 140°C, and the processing time is 50 seconds.

[0034]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a printing process of a polyester fabric. The printing process comprises the steps of printing, evaporating, reduction clearing, and shaping drying, wherein a low-temperature dyeing carrier is added in the printing step, and the quantity of the added dyeing carrier is 1%-7% of the weight of color paste; an evaporation condition of low temperature and constant pressure is adopted in the evaporation step, the temperature is 90-130 DEG C, and the time is 5-10 minutes; a reduction clearing solution comprises the ingredients of 0.5g / L-3g / L sodium hydrosulfite, a 4mL / L-7mL / L sodium hydroxide solution with the mass concentration of 35% and a 3g / L penetrating agent, the temperature in the reduction clearing step is 45-60 DEG C, and the treatment time is 15-20 minutes; and high-temperature width expansion shaping is adopted in the shaping drying step, the temperature is 110-140 DEG C, and the treatment time is 20-50 seconds. The printing process of the polyester fabric can be used for implementing continuous low-temperature evaporation and color fixation of the polyester fabric with low energy, and can effectively overcome the defect of high-temperature evaporation needed by a conventional disperse dye printing process applied to polyester fabric printing.

Description

technical field [0001] The invention relates to the field of textile printing and dyeing, in particular to a printing process for polyester fabrics. Background technique [0002] In recent years, with the pursuit of personalization, diversification and functionalization of clothing, the application of multi-fiber composite fabrics has become more extensive, such as blending or interweaving of wool, silk, acetate fibers, etc. with polyester fibers, etc., have become a hot research topic. With the continuous progress of science and technology, the traditional dyeing and finishing technology of polyester fabric has not adapted to the development requirements of the times. Moreover, due to the excessive development and utilization of energy, the energy is exhausted and the price of energy supply is getting higher and higher. The traditional polyester fabric dyeing and printing process is greatly challenged. [0003] At present, printing factories generally use high temperature ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06P3/54D06P5/02
Inventor 黄琴生
Owner CHANGSHU QINDA KNITTING PRINTING & DYEING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com