Method for producing holder blank with ether anhydride type polyimide molding powder composite material

A polyimide and composite material technology, applied in the field of bearing cages, can solve problems such as no related reports, achieve high tensile strength, high temperature resistance and excellent tribological properties, and improve tribological properties and high temperature resistance. Effect

Active Publication Date: 2015-01-28
LUOYANG BEARING RES INST CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The above-mentioned modified ether anhydride polyimide has good compatibility with polyimide pulp, and the resulting ether anhydride polyimide molding powder composite material can significantly improve the durability of the bearing cage. Thermal and friction resistance, and the tensile strength can still be maintained at a high value, but the method of making bearing cage blanks from ether anhydride polyimide molding powder composite materials has not been reported so far

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing holder blank with ether anhydride type polyimide molding powder composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] The invention is a method for making a cage blank from an ether anhydride type polyimide molding powder composite material. The method uses the ether anhydride type polyimide molding powder as a base material and adding polyimide pulp And lubricating modified materials polytetrafluoroethylene and carbon nanotubes, the ether anhydride type polyimide molding powder composite material is passed through the bearing cage mold and hot pressed on the program-controlled hot press to obtain the ether anhydride type polyimide mold The cage blank made of plastic powder composite material has the characteristics of light weight, high tensile strength, high temperature resistance and friction resistance after reprocessing.

[0029] The method of the present invention includes five steps:

[0030] The first step is to dry the ether anhydride type polyimide molding powder and polyimide pulp;

[0031] The second step is to pre-open the polyimide pulp;

[0032] The third step is to prepare eth...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
heat deflection temperatureaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

A method for producing holder blank with ether anhydride type polyimide molding powder composite material includes performing drying processing for ether anhydride type polyimide molding powder and polyimide pulp, performing pre-opening processing for the polyimide pulp, preparing the ether anhydride type polyimide molding powder composite material and bearing holder mold size constituting, and utilizing a stored program hot press and a bearing holder mold to make the holder blank. The ether anhydride type polyimide molding powder composite material utilizes the ether anhydride type polyimide molding powder as base material, the polyimide pulp, lubrication modified polytetrafluoroethylene and carbon nanotubes are added, the ether anhydride type polyimide molding powder composite material is pressed in the stored program hot press in a hot mode through the holder mold, the holder blank produced with the ether anhydride type polyimide molding powder composite material is obtained, and the produced holder blank after being processed has the advantages of being light in weight, high in tensile strength, resistant to high temperature and friction, and the like.

Description

Technical field [0001] The invention belongs to the technical field of bearing cages, and particularly relates to a method for manufacturing a cage blank from an ether anhydride type polyimide molding powder composite material. Background technique [0002] Ether anhydride type polyimide has good mechanical properties and excellent tribological properties, and is widely used in the field of ball bearing cages, but its glass transition temperature generally does not exceed 260 ℃, and its thermal deformation temperature does not exceed 250 ℃. Therefore, it cannot be applied to the requirements of bearing cages under high temperature conditions above 220℃. [0003] One of the effective ways to improve the heat resistance of ether anhydride polyimide is by adding metals or metal oxides, non-metallic or non-metallic nitrides, inorganic fibers, and nanomaterials, through the addition and modification of the above materials The increase in the heat resistance of the ether anhydride polyi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L79/08C08L27/18C08K7/00C08K3/04B29C43/02B29C43/36B29C43/34B29C43/58B29B13/06B29B13/00
Inventor 孙小波王子君葛世军王枫时连卫魏佳平
Owner LUOYANG BEARING RES INST CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products