Steel wire copper preplating electroplating solution
A pre-plating copper and solution technology, applied in the field of pre-plating copper electroplating solution, can solve problems such as poor stability, difficult wastewater treatment, affecting product quality and performance, and achieve good corrosion resistance and tensile strength, environmental protection and pollution-free performance. Reasonable formula effect
Inactive Publication Date: 2013-06-19
蔡成俊
View PDF0 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0002] In order to improve the corrosion resistance and electrical conductivity of the steel wire for electronic components, the steel wire needs to be copper-plated. Before copper-plating, the steel wire needs to be pre-plated with copper to improve the bonding strength and surface finish of the subsequent copper-plated layer. The pre-copper plating solution directly affects the quality and performance of the product. , the current pre-plating solution has poor stability and difficult wastewater treatment
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0009] A steel wire pre-plating copper electroplating solution, each composition is by weight percentage: KCu 2 150g / L, NaCN250-400g / L%, KCNS150g / L, complexing agent 30g / L%, stabilizer 20g / L%, balance water. The complexing agent is tripotassium citrate, and the regulator is potassium hydroxide. The process conditions are: the temperature of the copper plating solution is controlled at 50°C, the current density is 1.5-2A / dm2, the time is 30S, and the pH value is 10-11.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention discloses steel wire copper preplating electroplating solution. The steel wire copper preplating electroplating solution comprises by weight, 150-200g / L KCu2, 250-400g / L% NaCN, 100-200g / L KCNS, 25-50g / L% complexing agent, 10-25g / L% stabilizer and the balance water. The complexing agent is tripotassium citrate, and modifier is potassium hydroxide. According to the steel wire copper preplating electroplating solution, formulation is reasonable, corrosion resistance and tensile strength are good, the plating solution is environment friendly, pollution free and stable in property, and the produced products are high in quality.
Description
technical field [0001] The invention belongs to the technical field of steel wire electroplating solutions, in particular to a pre-plating copper electroplating solution. Background technique [0002] In order to improve the corrosion resistance and electrical conductivity of steel wire for electronic components, the steel wire needs to be copper-plated. Before copper plating, the steel wire needs to be pre-plated with copper to improve the bonding strength and surface finish of the subsequent copper plating layer. The pre-copper plating solution directly affects the quality and performance of the product. , The current pre-plating copper solution has poor stability and difficult wastewater treatment. Contents of the invention [0003] The purpose of the invention is to provide a pre-plating copper electroplating solution with reasonable formula, good corrosion resistance and tensile strength, and stable performance of the plating solution. [0004] Technical solution of ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): C25D5/36C25D7/06
Inventor 蔡成俊
Owner 蔡成俊