Anticorrosive paint containing sepiolite powder

A technology of sepiolite powder and anti-corrosion coating, applied in the field of coatings, which can solve the problems of unstable paint film, poor erosion resistance, short anti-corrosion period, etc., and achieve the effect of good metal adhesion, strong corrosion resistance and enhanced quality

Inactive Publication Date: 2013-06-26
ANHUI MINGZHU PIGMENT TECH
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the current technology of anti-corrosion coatings for metals has problems such as short anti-corrosion period, poor erosion resistance, unstable paint film, and enviro

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A kind of anticorrosion paint containing sepiolite powder, it is made up of two components of A and B, and described A component is made up of the raw material of following parts by weight (kg):

[0029] Epoxy resin E44 90, high chlorinated polyethylene resin (chlorine content 65M) 15, titanium dioxide 15, sepiolite powder 3, carboxymethyl cellulose sodium 6, dimethyl sulfoxide 4, 1-methylpentanol 4 , ethyl acrylate 4, urea 3, polyacrylamide 2, diethylamine 3, tricresyl phosphate 3, tribasic lead sulfate 2, nano zinc powder 7, dimethylethanolamine 4, composite modifier 25, di Toluene 30, n-butyl acetate 15, 3-glycidyl etheroxypropyl trimethoxysilane 0.8, methyl silicone oil 0.5;

[0030] Described composite modifier is made up of the following raw materials of weight part:

[0031] 35-45 degrees Baume water glass 50, aluminum sulfate 100, nano diatomite particles 45, sorbitan monooleate 2, polyoxyethylene ether 2, sodium carboxymethyl cellulose 1, dodecylbenzene Sodiu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Flexibilityaaaaaaaaaa
Adhesionaaaaaaaaaa
Login to view more

Abstract

The invention discloses an anticorrosive paint containing sepiolite powder. The anticorrosive paint is composed of a component A and a component B, wherein the component A is prepared from the following raw materials in parts by weight: 80-90 parts of epoxy resin E44, 10-15 parts of high chlorinated polyethylene resin, 8-15 parts of titanium dioxide, 2-3 parts of sepiolite powder, 4-6 parts of sodium carboxymethylcellulose, 2-4 parts of dimethyl sulfoxide, 2-4 parts of 1-methyl anyl alcohol, 2-4 parts of ethyl acrylate, 2-3 parts of urea, 2-3 parts of polyacrylamide, 2-3 parts of diethylamine, 2-3 parts of tricresyl phosphate, 1-2 parts of lead sulfate tribasic, 5-7 parts of nanometer zinc powder, 2-4 parts of dimethylethanolamine, 18-25 parts of compound modifier, 25-30 parts of dimethylbenzene, 10-15 parts of n-butyl acetate, 0.8-1 parts of 3-glycidyl ether oxygen propyl trimethoxy silane and 0.5-1 parts of methyl silicone oil. A paint film prepared by the invention has the advantages of good adhesive force to metal, small structure pores, compact structure, good adhesive force, good flexibility, high impact strength and strong corrosion resistance, and plays an efficient protection effect on base metal.

Description

technical field [0001] The invention mainly relates to a coating, in particular to an anticorrosion coating containing sepiolite powder. Background technique [0002] With the advancement of industrial technology, the use of metal materials is becoming more and more extensive. The corrosion of metals and their components has spread to all fields of the national economy, causing huge losses to human society. In order to reduce the loss of corrosion, people have taken many protective measures, but so far the most common, economical and practical protective measures are coating protection. Among various anti-corrosion technologies, coating anti-corrosion technology is the most widely used. Coating anticorrosion is widely used because of its simple construction, economical application, and not being restricted by equipment area and shape; [0003] Among the many types of coatings, epoxy resin plays an important role in anti-corrosion coatings. It is widely used as a coating...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D163/02C09D123/28C09D5/08
Inventor 徐冉阳
Owner ANHUI MINGZHU PIGMENT TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap