Flint clay compound type foaming agent

A composite foaming agent technology, applied in the field of foaming agent, can solve problems such as insufficient performance, no air purification, and failure to meet the needs of actual production and environmental protection. The effect of large bubble volume

Active Publication Date: 2013-09-04
黄万辉
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Although there are many types of foaming agents and wide applications, they have the disadvantages of insufficient performance and cannot meet the needs of actual production and environmental protection. The existing foaming agents do not have the function of purifying air.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0034] Below in conjunction with embodiment the present invention will be further described:

[0035] 1. The ingredients of the burnt gem compound foaming agent are composed of the following components by weight percentage: 72% of burnt gem compound foaming agent paste, 20.95% of hydrogen peroxide, 0.05% of polyether modified silicone oil and 7% of water.

[0036] The production method of the burnt gemstone composite foaming agent: input the ingredients of the burnt gemstone composite foaming agent into a high-speed mixer for stirring, the speed of the mixer is controlled at 1700-1800 rpm, the stirring time is controlled at 12 minutes, and the stirring is uniform Finally, it is the finished product of coke gem compound foaming agent.

[0037] The ingredients of the burnt gem compound foaming agent paste are composed of the following components by weight percentage: 30% of cooked burnt gem powder, 24% of attapulgite clay powder with air purification function, dodecyl dimethyl ami...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a flint clay compound type foaming agent. The key point of the technical scheme is that the flint clay compound type foaming agent comprises calcined flint clay powder, attapulgite pottery clay powder having a function of air purification, hydrogen peroxide, lauryl dimethyl amine oxide, coconut diethanolamide, silicone resin polyether emulsion, polyether modified silicone oil and water; pasty ingredients of the flint clay compound type foaming agent are stirred to a paste, the ingredients of the flint clay compound type foaming agent are stirred to a finished product of the flint clay compound type foaming agent; and the flint clay compound type foaming agent has the characteristics of strong foaming capacity, high foam factor, large foam production amount per unit volume, delicate and uniform cells which are not easy to break, high product demoulding speed, good finish surface degree and high product long-term strength. The product produced by using the flint clay compound type foaming agent has the effects of heat preservation, thermal insulation and sound insulation, as well as the function of air purification, and the flint clay compound type foaming agent is suitable for producing a light plate, a light wall body and a product for sound attenuation and noise reduction.

Description

technical field [0001] The invention relates to a foaming agent, in particular to a burnt gem composite foaming agent. Background technique [0002] Foaming agents can be divided into three categories: chemical foaming agents, physical foaming agents and surfactants. Foaming agents with more uses include cement foaming agents, concrete foaming agents, plastic foaming agents, and polyurethane foaming agents. , rubber foaming agent, glass foaming agent, etc. [0003] Although there are many kinds of foaming agents and they are widely used, they have the disadvantages that their performance is not comprehensive enough to meet the needs of actual production and environmental protection, and the existing foaming agents do not have the function of purifying air. Contents of the invention [0004] The purpose of the present invention is to overcome the deficiencies in the prior art and provide a composite foaming agent for burnt gemstones. [0005] The coke gem compound foaming...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/02C04B24/42
Inventor 许庆华袁长兵许盛英袁欣蒋文兰
Owner 黄万辉
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap