Titanium alloy coil rod and production method thereof
A production method, titanium alloy technology, applied in the field of non-ferrous metal material processing and forming, can solve the problems of low production efficiency, complicated process, labor and time-consuming, etc., to improve rolling speed and rolling capacity, improve production efficiency and product yield rate effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0036] A. Put the turned titanium alloy billet with a side length of 130mm and a length of 5m, including the following components and their weight percentages, in a conventional resistance heating furnace for heating at a heating rate of 5°C / min , when heated to 900°C, keep warm for 80 minutes:
[0037] Al 5.0wt%
[0038] V 3.0wt%
[0039] Fe 0.21wt%
[0040] C 0.05wt%
[0041] N 0.05wt%
[0042] H 0.010wt%
[0043] O 0.15wt%
[0044] The rest is Ti and unavoidable impurities;
[0045] B. Send the titanium alloy square billet obtained in step A to a conventional rolling mill for rolling. Under the condition that the starting rolling temperature is 800°C and the rolling speed is 0.2m / s, rough rolling is carried out for 6 passes to obtain a rough rolled piece; Cut the head to improve the biting condition of the rolled piece and ensure the smooth progress of rolling; then, under the condition of temperature of 750°C and rolling speed of 1.0m / s, the roug...
Embodiment 2
[0049] A. Place the turned titanium alloy billet with a side length of 150mm and a length of 5.5m, including the following components and their weight percentages, in a conventional resistance heating furnace for heating at a heating rate of 6°C / min Rate, when heated to 950°C, hold for 100 minutes:
[0050] Al 5.6wt%,
[0051] V 3.5wt%,
[0052] Fe 0.18wt%,
[0053] C 0.04wt%,
[0054] N 0.02wt%,
[0055] H 0.007wt%,
[0056] O 0.09wt%,
[0057] The rest is Ti and unavoidable impurities;
[0058] B. Send the titanium alloy square billet obtained in step A to a conventional rolling mill for rolling. Under the condition that the rolling start temperature is 850°C and the rolling speed is 0.3m / s, rough rolling is carried out for 6 passes to obtain a rough rolled piece; Cut the head to improve the biting condition of the rolled piece and ensure the smooth progress of rolling; then, under the condition of temperature of 800°C and rolling speed of 1.5m / s, the rough rolled pie...
Embodiment 3
[0062] A. Put the turned titanium alloy billet with a side length of 160mm and a length of 10m, including the following components and their weight percentages, in a conventional resistance heating furnace for heating at a heating rate of 7°C / min , when heated to 980°C, keep warm for 120 minutes:
[0063] Al 6.0wt%,
[0064] V 3.3wt%,
[0065] Fe 0.09wt%,
[0066] C 0.02wt%,
[0067] N 0.01wt%,
[0068] H 0.006wt%,
[0069] O 0.14wt%,
[0070] The rest is Ti and unavoidable impurities;
[0071] B. Send the titanium alloy square billet obtained in step A to a conventional rolling mill for rolling. Under the condition that the rolling start temperature is 880°C and the rolling speed is 0.5m / s, rough rolling is carried out 6 times to obtain a rough rolled piece; Cut the head to improve the biting condition of the rolled piece and ensure the smooth progress of rolling; then, under the conditions of temperature 830 ℃ and rolling speed 2.0m / s, the rough rolled piece was rolle...
PUM
Property | Measurement | Unit |
---|---|---|
length | aaaaa | aaaaa |
length | aaaaa | aaaaa |
diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com