Compatibility modifier used for ABS waste plate material, and use method thereof

A board material and modifier technology, which is applied in the field of compatible modifiers for ABS waste board materials, can solve the problems of low physical and chemical properties of products, cannot satisfy consumers, and limit the scope of application, and achieves improved physical and chemical properties and novel ideas. , easy to use effect

Inactive Publication Date: 2013-09-11
PLASTIC UNION NEW MATERIAL TECH HUBEI
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As we all know, the existing ABS waste board material processing methods are outdated and the technology is backward, and the products produced have low physical and chemical properties and poor quality, which cannot meet the needs of consumers, nor can they adapt to the needs of market development, thus limiting its application range

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] The compatibility modifier of the present invention is prepared by the following components and parts by weight: when detecting the melt flow index M1=0.5~0.8 of the ABS waste board material, take 2.0 parts of chlorinated polyethylene and 6.0 parts of high rubber powder , spare; its use is as follows:

[0013] Wash the ABS waste board material with water, remove sundries and dust, break it into materials of similar size, and take 100 parts for later use;

[0014] Put the above-mentioned 100 parts of processed ABS waste board materials into the mixer first, then mix the above-mentioned 2.0 parts of chlorinated polyethylene and 6.0 parts of high-grade rubber powder into the mixer, start it for 12 minutes at room temperature, stop it, and unload it. Material packaging can be.

Embodiment 2

[0016] This example is basically the same as Example 1, except that: when the melt flow index M1=0.8~1.5, then take 2.2 parts of chlorinated polyethylene and 7.0 parts of high rubber powder.

[0017] In the method of use, put the above-mentioned 100 parts of processed ABS waste board materials into the mixer, then mix the above-mentioned 2.2 parts of chlorinated polyethylene and 7.0 parts of high-grade rubber powder into the mixer, start it at room temperature for 13 minutes, and then stop it , unloading and packaging.

Embodiment 3

[0019] This example is basically the same as Example 1, except that: when the melt flow index M1=1.5~2.0, then take 2.5 parts of chlorinated polyethylene and 9.0 parts of high rubber powder.

[0020] In the method of use, put the above-mentioned 100 parts of processed ABS waste board materials into the mixer, then mix the above-mentioned 2.5 parts of chlorinated polyethylene and 9.0 parts of high-grade rubber powder into the mixer, start it at room temperature for 14 minutes, and then stop it. , unloading and packaging.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a compatibility modifier used for an ABS waste plate material, and a use method thereof. The compatibility modifier comprises 2.0-3.0 parts by weight of chlorinated polyethylene and 6.0-12.0 parts by weight of high-rubber powder. The use method of the compatibility modifier used for the ABS waste plate material comprises the following steps: 1, processing the ABS waste plate material; 2, detecting the melt flow index of the ABS waste plate material; 3, material burdening: burdening the ABS waste plate material, chlorinated polyethylene and the high-rubber powder according to a ratio of 100:2.0-3.0:6.0-12.0; and 4, material feeding and processing: adding the above prepared components to a mixer, starting at normal temperature for 12-15min, shutting down, discharging, and packaging. The compatibility modifier has the advantages of reasonable technology, simple processing, and effective improvement of the physical and chemical performances, the quality and the like of the ABS waste plate material, and can be widely used for the modification processing of the ABS waste plate material.

Description

technical field [0001] The invention relates to a compatible modifier for plastics and a usage method thereof, in particular to a compatibility modifier for ABS waste board materials and a usage method thereof. Background technique [0002] ABS is the English abbreviation for acrylonitrile-styrene-butadiene copolymer. As we all know, the existing ABS waste board material processing methods are outdated and the technology is backward. The products produced have low physical and chemical properties and poor quality, which cannot meet the needs of consumers or meet the needs of market development, thus limiting its application range. Contents of the invention [0003] The purpose of the present invention is to overcome the deficiency of the above-mentioned background technology, through the inventor's painstaking research and repeated verification through production practice, to provide a kind of compatibility modifier for ABS waste board material and its application method. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L55/02C08L23/28
Inventor 邓丽邓军邓忠权陈绪煌
Owner PLASTIC UNION NEW MATERIAL TECH HUBEI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com