Flame-retardant and fireproof fabric, and processing technology and textile thereof

A technology of fire-resistant fabrics and processing technology, which is applied in textiles, yarns, fabrics, etc., can solve problems such as complex production processes, and achieve the effects of promoting blood circulation, better flame-retardant effect, and strong strength

Active Publication Date: 2015-02-04
SHANGHAI ZANRAY IND
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, its production process has always been relatively complicated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A processing technology for flame-retardant and fire-resistant fabrics, comprising the following steps:

[0024] (1) Preparation of functional yarn lines: the warp yarn is made of flame-retardant acrylic fiber, flame-retardant viscose, fine denier polyester, and aramid 1313 fiber blended tops, and the weft yarn is made of seaweed fiber, polyphenylene sulfide, polysulfone fiber, and phenolic The wool top is made of fiber blending, and then the warp and weft yarns are prepared by cleaning, opening, drawing, roving, spun yarn, winding and twisting. The weight percentages of the flame-retardant acrylic fiber, flame-retardant viscose, fine denier polyester, and aramid 1313 fibers used in the warp are 20%: 15%: 30%: 35%. The percentage by weight of the seaweed fiber, polyphenylene sulfide, sulfone fiber and phenolic fiber used in the weft yarn is 30%: 15%: 25%: 30%.

[0025] (2) Dyeing, color fixing, and washing: Use reactive dyes to dye functional yarns, firstly perform pre...

Embodiment 2

[0034] A processing technology for flame-retardant and fire-resistant fabrics, comprising the following steps:

[0035] (1) Preparation of functional yarn lines: the warp yarn is made of flame-retardant acrylic fiber, flame-retardant viscose, fine denier polyester, and aramid 1313 fiber blended tops, and the weft yarn is made of seaweed fiber, polyphenylene sulfide, polysulfone fiber, and phenolic The wool top is made of fiber blending, and then the warp and weft yarns are prepared by cleaning, opening, drawing, roving, spun yarn, winding and twisting. The weight percentages of the flame-retardant acrylic fiber, flame-retardant viscose, fine denier polyester, and aramid 1313 fibers used in the warp are 20%: 15%: 30%: 35%. The percentage by weight of the seaweed fiber, polyphenylene sulfide, sulfone fiber and phenolic fiber used in the weft yarn is 30%: 15%: 25%: 30%.

[0036] (2) Dyeing, color fixing, and washing: Use reactive dyes to dye functional yarns, firstly perform pre...

Embodiment 3

[0045]A processing technology for flame-retardant and fire-resistant fabrics, comprising the following steps:

[0046] (1) Preparation of functional yarn lines: the warp yarn is made of flame-retardant acrylic fiber, flame-retardant viscose, fine denier polyester, and aramid 1313 fiber blended tops, and the weft yarn is made of seaweed fiber, polyphenylene sulfide, polysulfone fiber, and phenolic The wool top is made of fiber blending, and then the warp and weft yarns are prepared by cleaning, opening, drawing, roving, spun yarn, winding and twisting. The weight percentages of the flame-retardant acrylic fiber, flame-retardant viscose, fine denier polyester, and aramid 1313 fibers used in the warp are 20%: 15%: 30%: 35%. The percentage by weight of the seaweed fiber, polyphenylene sulfide, sulfone fiber and phenolic fiber used in the weft yarn is 30%: 15%: 25%: 30%.

[0047] (2) Dyeing, color fixing, and washing: Use reactive dyes to dye functional yarns, firstly perform pret...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
limiting oxygen indexaaaaaaaaaa
Login to View More

Abstract

The invention relates to flame-retardant and fireproof fabric, and a processing technology and textile thereof. Warp yarns adopt wool tops formed by blending flame-retardant acrylic, flame viscose, fine-denier polyester and aramid fiber 1313 fiber; weft yarns adopt wool tops formed by blending alginate fiber, polyphenylene sulfide, polysulfonamide and phenolic fiber; then the warp yarns and the weft yarns form the flame-retardant and fireproof fabric through steps of dyeing, fixation, rinsing, sizing, weaving, desizing, rinsing, drying, baking, full decatizing and the like. The fabric has the characteristics of simple processing technology, good flame-retardant effect and the like, and can be applied to apparel, home textile, sports goods, medical care and fireproof fabric.

Description

technical field [0001] The invention relates to the field of fire-resistant fabrics, in particular to a flame-retardant and fire-resistant fabric, its processing technology and its application on the fabric. Background technique [0002] With the development of the economy and the improvement of the national legal system, the promotion and application of flame-retardant textiles will definitely attract the attention of the whole society. There are many developments and researches on flame-retardant fabrics in foreign countries. Some industrially developed countries have formulated flame-retardant regulations on textiles as early as the mid-1970s, and in recent years, the requirements have become higher and higher, and the regulations have become more and more detailed. In recent years, the research and development of flame-retardant textiles in my country has gradually increased, and considerable progress has been made. With the acceleration of urban modernization, the dev...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D03D15/00D03D1/00D04B1/14D04B21/00D02G3/04D02G3/44D06P3/85D06P1/38D06M15/263D06M11/71D06L1/00D03D15/20D03D15/225D03D15/283D03D15/47D03D15/513D06L1/14D06L1/16
Inventor 杨小波
Owner SHANGHAI ZANRAY IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com