A welding process, stainless steel technology, applied in the direction of welding equipment, manufacturing tools, workpiece edge, etc., can solve the problems that stainless steel cannot be realized, and achieve the effect of reducing corrosion resistance

Active Publication Date: 2013-10-23
DALIAN SAGE GROUP
View PDF5 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of the above problems, the present invention researches and designs a stainless steel composite pipe welding process, which is used to solve the shortcomings that the existing welding process can not be realized by traditionally welding carbon steel first and then stainless steel for steel pipes with inner stainless steel and outer carbon steel.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Welding technology for stainless steel composite tubes

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] Such as figure 1 Shown, a stainless steel clad pipe welding process, comprises the following steps:

[0021] (1) Weld the cladding layer 1 of the stainless steel composite pipe to form a weld bead 4; the welding of the weld bead 4 should adopt TIG, MIG, and laser welding methods, which can ensure that the weld bead is free of dross and is conducive to the welding of the next weld bead .

[0022] (2) A transition layer 2 is welded between the cladding layer 1 and the base layer 3 of the stainless steel composite pipe to form a weld bead 25; the welding of the weld bead 25 should use electrodes with high chromium and nickel content, such as: A302, A307 , can reduce the impact on the cladding material when welding the base material.

[0023] (3) Weld the base layer 3 of the stainless steel composite pipe to form the third bead 6; the welding of the third bead 6 should adopt the submerged arc welding method, and the welding material can be the same material as the base ma...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a welding technology for stainless steel composite tubes, which comprises the following steps: (1) conducting welding on the stainless steel composite tube overlying layer to form a welding path I; (2) welding a transition layer between the stainless steel composite tube overlying layer and the substrate layer to form a welding path II; (3) conducting welding on the stainless steel composite tube substrate layer to form a welding path III. According to the welding technology for stainless steel composite tubes provided by the invention, the overlying layer stainless steel (inner layer) of the composite tube is welded first and the substrate carbon steel (outer layer) is welded later, so as to effectively solve the problem that the conventional technology, namely welding carbon steel first and welding stainless steel later, can not weld a composite tube with a diameter smaller than 325, and the welding of the transition layer (welding path II) between the overlying layer and the substrate layer better solves the problem that, in the process of welding overlying layer, the increase of overlying carbon leads to the decrease of overlying layer corrosion, and the problem that, in the process of welding substrate layer, the increase of alloy (chromium and nickel) content leads to the forming of hard organization in the welding line is solved as well.

Description

technical field [0001] The invention relates to the field of composite material welding technology of two or more different metals, and relates to a stainless steel composite pipe welding technology. Background technique [0002] At present, the welding of composite materials of two or more different metals is a relatively complicated welding process problem. The composite material of stainless steel and carbon steel is used as an example to illustrate (hereinafter referred to as composite material). [0003] The current existing composite material welding process is to weld carbon steel first and then stainless steel, but this process cannot be realized in some cases, such as the welding of inner stainless steel and outer carbon steel steel pipes, which is a headache, and this patented technology It can be well applied to this field and solve this problem. [0004] For steel pipes with inner stainless steel and outer carbon steel, the stainless steel is located in the inne...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B23K28/02B23K33/00
Inventor 马丽高国鸿
Owner DALIAN SAGE GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka