Double-sided reinforced mica tape with films and method for manufacturing double-sided reinforced mica tape

A technology of mica tape and film, which is applied in the direction of chemical instruments and methods, lamination, insulators, etc., can solve the problems of high or low surface wear resistance, low strength and elongation, damage to the insulation of mica paper, etc., and achieve low production cost, The effect of high surface wear resistance

Active Publication Date: 2013-12-04
晟大科技(南通)有限公司
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The surface wear resistance of the disclosed double-sided film mica tape products in the prior art is relatively low, and the insulation of the mica paper will be destroyed after burning, and the strength and elongation are low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0064] A double-sided reinforced film mica tape, the mica tape comprises from bottom to top: a first organic film layer, a first adhesive layer, mica paper, a second adhesive layer and a second organic film layer.

[0065] The mica paper is selected from natural muscovite paper.

[0066] The quantitative of described mica paper is 50g / m 2 .

[0067] The material of the first organic thin film layer is selected from PI thin film.

[0068] The material of the second organic film layer is selected from PE film.

[0069] The materials of the first adhesive layer and the second adhesive layer are both selected from silicone resins.

[0070] The glue content of the double-sided reinforced film mica tape is 4%.

[0071] The thickness of the double-sided reinforcing film mica tape is 0.015-0.02mm.

[0072] The width of the double-sided reinforcing film mica tape is 10mm.

[0073] The preparation method of double-sided reinforcing film mica tape as mentioned above, comprises the ...

Embodiment 2

[0084] A double-sided reinforced film mica tape, the mica tape comprises from bottom to top: a first organic film layer, a first adhesive layer, mica paper, a second adhesive layer and a second organic film layer.

[0085] The mica paper is selected from natural phlogopite paper.

[0086] The quantification of described mica paper is 200g / m 2 .

[0087] The first organic film layer is selected from PET film.

[0088] The material of the second organic film layer is selected from OPE film.

[0089] The materials of the first adhesive layer and the second adhesive layer are both selected from epoxy resin.

[0090] The glue content of the double-sided reinforced film mica tape is 12%.

[0091] The thickness of the double-sided reinforcing film mica tape is 0.015-0.02mm;

[0092] The width of the double-sided reinforcing film mica tape is 10mm.

[0093] The preparation method of double-sided reinforcing film mica tape as mentioned above, comprises the steps:

[0094] (1) Af...

Embodiment 3

[0104] A double-sided reinforced film mica tape, the mica tape comprises from bottom to top: a first organic film layer, a first adhesive layer, mica paper, a second adhesive layer and a second organic film layer.

[0105] The mica paper is selected from artificially synthesized fluorophlogopite paper.

[0106] The quantification of described mica paper is 120g / m 2 .

[0107] The first organic film layer is selected from OPE films.

[0108] The material of the second organic film layer is selected from OPE film.

[0109] The materials of the first adhesive layer and the second adhesive layer are both selected from polyester resin.

[0110] The glue content of the double-sided reinforced film mica tape is 7%.

[0111] The thickness of the double-sided reinforcing film mica tape is 0.015-0.02mm;

[0112] The width of the double-sided reinforcing film mica tape is 10mm.

[0113] The preparation method of double-sided reinforcing film mica tape as mentioned above, comprises ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
widthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a double-sided reinforced mica tape with films. The mica tape sequentially comprises a first organic film layer, a first adhesive layer, mica paper, a second adhesive layer and a second organic film layer from bottom to top. The double-sided reinforced mica tape with the films has the advantages that the double-sided reinforced mica tape is low in manufacturing cost, high in surface abrasion resistance, sufficient in strength and proper in elongation, and an insulating property of the mica paper cannot be destroyed even when the double-sided reinforced mica tape is burned; as tested by experiments, the tensile strength of the mica tape is higher than or equal to 30N, the breaking strength of the mica tape is higher than or equal to 100N, and the mica tape can be used for motors.

Description

technical field [0001] The invention belongs to the technical field of mica tape preparation, and in particular relates to a double-sided reinforced film mica tape and a preparation method thereof. Background technique [0002] Mica tape, also known as refractory mica tape, is a fire-resistant insulating material, which can be divided into: mica tape for motors and mica tape for cables. According to the structure, it is divided into: double-sided belt, single-sided belt, three-in-one belt, double-film belt, single-film belt, etc. [0003] The development of modern large and medium-sized high-voltage motor technology has put forward higher and higher requirements for the insulation performance of the motor. The operating temperature, rated power, capacitance and volume of the motor have increased significantly, and the insulation structure has to bear higher electrical stress, mechanical stress, thermal stress and environmental stress, and the working environment of the moto...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B19/04B32B27/06B32B37/14H01B17/60H01B19/00
Inventor 卢儒
Owner 晟大科技(南通)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com