Light-color NBR/PVC (nitrile butadiene rubber/poly vinyl chloride) oil-resistant rubber material with high acrylonitrile content

A technology of oil-resistant rubber and acrylonitrile, which is applied in the field of light-colored NBR/PVC oil-resistant rubber materials, and can solve the problems of little research on light-colored NBR/PVC

Inactive Publication Date: 2013-12-11
SHENYANG INSTITUTE OF CHEMICAL TECHNOLOGY
View PDF1 Cites 36 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although there has been some research on NBR and PVC blends, there are few studies on light-colored NBR / PVC, and there are few reports on the comprehensive research on the oil resistance of light-colored NBR / PVC with high acrylonitrile content. The study of light-colored NBR / PVC blended rubber materials with nitrile content is very meaningful

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Light-color NBR/PVC (nitrile butadiene rubber/poly vinyl chloride) oil-resistant rubber material with high acrylonitrile content
  • Light-color NBR/PVC (nitrile butadiene rubber/poly vinyl chloride) oil-resistant rubber material with high acrylonitrile content
  • Light-color NBR/PVC (nitrile butadiene rubber/poly vinyl chloride) oil-resistant rubber material with high acrylonitrile content

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The light-colored NBR / PVC oil-resistant rubber material with high acrylonitrile content described in this embodiment is made of NBR, PVC, filling reinforcing agent, plasticizer, anti-aging agent, coloring agent, vulcanizing agent, stabilizer and other rubber processing aids. agent composition.

[0022] This embodiment includes 70 parts of NBR, 30 parts of PVC, 30 parts of white carbon black, 50 parts of talcum powder, 20 parts of DOP, 25 parts of 3G8, 2.0 parts of antioxidant 1010, 1.8 parts of coloring agent, 0.8 parts of sulfur, 1.5 parts of CZ , 1.5 parts of DM, 1.6 parts of stabilizer, 2.0 parts of paraffin, 5.0 parts of zinc oxide, 1.5 parts of stearic acid, 3.0 parts of PEG2000.

[0023] The preparation method of the light-colored NBR / PVC oil-resistant rubber material with high acrylonitrile content of the present invention is a mechanical blending method, and the specific steps are as follows:

[0024] (1) NBR / PVC blending: Pre-plasticize PVC, plasticizers, ...

Embodiment 2

[0030] The composition of this example is basically the same as that of Example 1, except that 1.2 parts of sulfur, 1.2 parts of CZ, and 0.5 parts of TMTD are used instead of 0.8 parts of sulfur, 1.5 parts of CZ, and 1.5 parts of DM.

[0031] See Table 1 for the performance test results of the light-colored NBR / PVC oil-resistant rubber with high acrylonitrile content obtained in this example, and see Table 4 for the oil-resistant performance results.

Embodiment 3

[0033] The composition of this example is basically the same as that of Example 1, except that 1.5 parts of sulfur, 1.5 parts of DM, and 0.5 parts of TMTD are used instead of 0.8 parts of sulfur, 1.5 parts of CZ, and 1.5 parts of DM.

[0034] See Table 1 for the performance test results of the light-colored NBR / PVC oil-resistant rubber with high acrylonitrile content obtained in this example, and see Table 4 for the oil-resistant performance results.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a light-color NBR / PVC (nitrile butadiene rubber / poly vinyl chloride) oil-resistant rubber material with high acrylonitrile content and relates to a rubber material. The oil-resistant rubber material contains the following ingredients in parts by weight: 70 parts of NBR, 30 parts of PVC, 25-35 parts of precipitated silica, 50-80 parts of a filling agent, 40-50 parts of a plasticizer, 1.5-2.0 parts of an anti-aging agent, 1.5-2.5 parts of a colorant, 0.5-3.0 parts of a vulcanizing agent, 1.5-3.5 parts of an accelerant, 1.5-2.0 parts of a stabilizer, and 9.5 parts (in total) of other rubber processing auxiliaries such as a vulcanizing activator and a polar additive. The light-color NBR / PVC oil-resistant rubber material with high acrylonitrile content is excellent in oil resistance and can be used in places with strict requirements on oil resistance. The light-color NBR / PVC oil-resistant rubber material can be widely used in the industries such as fuel oil rubber tubes, electric wire and cable sleeves, printing rubber rolls and sealing articles, and especially in the industries of automobile sealing parts, spare parts and the like.

Description

technical field [0001] The invention relates to a rubber material, in particular to a light-colored NBR / PVC oil-resistant rubber material with high acrylonitrile content. Background technique [0002] Nitrile rubber (NBR) has excellent oil resistance, heat resistance and physical and mechanical properties, but its ozone aging resistance is poor; while general-purpose synthetic resin polyvinyl chloride (PVC) has excellent flame retardancy and self-extinguishing properties As well as ozone aging resistance, chemical corrosion resistance, electrical insulation, chemical stability and thermoplasticity, but its toughness is low, it is not impact resistant, and its heat resistance is poor. The composite material made of NBR and PVC blends combines the performance advantages of the two and makes up for their respective defects. It has become an important new rubber-plastic composite material and a pioneer of rubber-plastic composite materials. Both NBR and PVC are polar polyme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L9/02C08L27/06C08K13/02C08K3/36C08K3/34C08K3/26C08K3/06C08K5/14
Inventor 王重于丽郭翠翠宫小曼胡嘉文陈慧
Owner SHENYANG INSTITUTE OF CHEMICAL TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com