A sliding and wear-resistant, rubber technology, applied in the field of anti-skid and wear-resistant rubber, can solve the problems of poor anti-skid performance and poor wear resistance of soles, and achieve the effect of good anti-skid performance.
Inactive Publication Date: 2014-01-01
昆山纯柏精密五金有限公司
View PDF2 Cites 4 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] Sports shoes have special purposes, most of which are worn during sports, and the rubber used for the soles is required to be wear-resistant, wet-slip resistant, and also required to have good impact resistance. The existing sports shoes have poor anti-skid performance and poor abrasiveness
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0049] A kind of anti-slip and wear-resistant rubber, the rubber comprises the following components in parts by weight:
[0050] The rubber comprises the following components in parts by weight:
[0051] EPDM rubber: 10 parts
[0052] Butyl rubber: 27 parts
[0053] Stearic acid: 3 parts
[0054] White carbon black: 11 parts;
[0055] Light calcium carbonate: 8 parts
[0056] Antiager MB: 10 parts
[0057] Vulcanizing agent PDM: 1 part
[0058] DEHP: 6 servings.
Embodiment 2
[0060] A kind of anti-slip and wear-resistant rubber, the rubber comprises the following components in parts by weight:
[0061] The rubber comprises the following components in parts by weight:
[0062] EPDM rubber: 20 parts
[0063] Butyl rubber: 14 parts
[0064] Stearic acid: 7 parts
[0065] White carbon black: 6 parts;
[0066] Light calcium carbonate: 10 parts
[0067] Antiager RD: 8 parts
[0068] Vulcanizing agent double 25: 3 parts
[0069] DEHP: 3 parts.
Embodiment 3
[0071] A kind of anti-slip and wear-resistant rubber, the rubber comprises the following components in parts by weight:
[0072] The rubber comprises the following components in parts by weight:
[0073] EPDM rubber: 15 parts
[0074] Butyl rubber: 21 parts
[0075] Stearic acid: 6 parts
[0076] White carbon black: 7 parts;
[0077] Light calcium carbonate: 9 parts
[0078] Antiager 264: 8 parts
[0079] Vulcanizing agent TEC: 2 parts
[0080] DEHP: 4 parts.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses an antiskid abrasion-resistant rubber which comprises the following components in parts by weight: 10-20 parts of ethylene propylene diene monomer, 14-27 parts of butyl rubber, 3-7 parts of stearic acid, 6-11 parts of silica white, 8-10 parts of auxiliary reinforcing agent, 4-8 parts of anti-aging agent, 1-3 parts of vulcanizing agent and 3-6 parts of plasticizer. The shoe sole prepared by the antiskid abrasion-resistant rubber disclosed by the invention has the advantages of abrasion resistance and favorable wet skid resistance.
Description
technical field [0001] The invention relates to a rubber, in particular to an anti-slip and wear-resistant rubber for shoe soles. Background technique [0002] The sole is an important part of the shoe material field. The main function of the sole is to protect the feet, prevent slipping, shock absorption, ensure the comfort of the wearer's feet, and reduce the chance of sports injuries. The material of the sole is mostly rubber sole, such as ordinary rubber sole, thermoplastic molding, divided into natural rubber and recycled rubber. [0003] Sports shoes have special purposes, most of which are worn during sports, and the rubber used for the soles is required to be wear-resistant, wet-slip resistant, and also required to have good impact resistance. The existing sports shoes have poor anti-skid performance and Not very abrasive. [0004] Therefore this field needs to provide a kind of anti-skid wear-resistant rubber that is used for shoe sole with good wear resistance an...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more