A kind of collector of zinc oxide ore dressing and preparation method thereof
A zinc oxide and collector technology, applied in flotation, solid separation and other directions, can solve the problems of large consumption of chemicals, high cost of flotation, narrow selection range, etc. The effect of grade and recovery
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0021] The weight components of a zinc oxide mineral beneficiation collector are:
[0022] Dodecyl amine 200g, hexadecyl amine 300g, octadecyl amine 450g, sodium dodecyl sulfonate 50g.
[0023] A preparation method of zinc oxide mineral beneficiation collector: Dodecameric primary amine, hexadecyl primary amine, eighteen primary amine and the active agent are weighed according to the above ratio and then poured into a heated and stirred reactor, and then poured into the weight Dissolved in 80-100g ethanol.
[0024] Slowly add 200g of water to the reaction kettle and heat it to 130°C. At this time, add 80g of sodium hydroxide and stir continuously for 2 to 3 hours. During the stirring process, keep the temperature at 130°C, and the mass concentration of sodium hydroxide is 30%. After cooling, a paste-like mixture is formed to obtain a paste-like new collector product.
Embodiment 2
[0026] The weight components of a zinc oxide mineral beneficiation collector are:
[0027] Dodecyl amine 250g, hexadecyl amine 300g, octadecyl amine 400g, sodium hexadecyl sulfonate 50g.
[0028] A preparation method of zinc oxide mineral beneficiation collector: Dodecameric primary amine, hexadecyl primary amine, eighteen primary amine and the active agent are weighed in proportion and poured into a heated and stirred reactor, and then poured into a weight 80-100g ethanol dissolves.
[0029] Slowly add 150-200g of water into the reaction kettle. When heated to 140°C, add 90g of sodium hydroxide and stir continuously for 2 to 3 hours. During the stirring process, keep the temperature at 140°C, and the mass concentration of sodium hydroxide is 32%. After cooling, a paste-like mixture is formed to obtain a new paste-like collector product.
Embodiment 3
[0031] The weight components of a zinc oxide mineral beneficiation collector are:
[0032] Dodecyl primary amine 180g, hexadecyl primary amine 300g, octadecyl primary amine 450g, dodecyltrimethylammonium chloride 70g.
[0033] A preparation method of zinc oxide mineral beneficiation collector: Dodecameric primary amine, hexadecyl primary amine, eighteen primary amine and the active agent are weighed in proportion and poured into a heated and stirred reactor, and then poured into a weight 80-100g ethanol dissolves.
[0034] Slowly add 150-200g of water into the reaction kettle. After heating to 150°C, add 90g of sodium hydroxide and stir continuously for 2 to 3 hours. During the stirring process, keep the temperature at 150°C, and the mass concentration of sodium hydroxide is 36%. After cooling, a paste-like mixture is formed to obtain a new paste-like collector product.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap