Manufacturing method of decorating plate

A manufacturing method and technology for decorative panels, which are applied in chemical instruments and methods, lamination devices, manufacturing tools, etc., can solve the problem that man-made panels are not resistant to water, heat and shock, do not have combat properties, and have high combat production costs. problem, to achieve the effect of low production cost, low emission and good pollution resistance

Active Publication Date: 2014-02-12
江苏天润盛凯新材料股份有限公司
View PDF9 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing process requires a large amount of kraft paper, and the papermaking process needs to be carried out before production. The papermaking process has high energy consumption and heavy pollution, which has a great impact on the environment and is also the main reason for the high production cost of Combet
In addition, solid wood composite Combet has not yet appeared in the market. Generally, decorative paper is used as the surface, and the color is relatively cold. There are no pollution-free, natural patterns, elegant and heavy-duty, rich texture, and real elasticity.
There are wood-based panels such as solid wood plywood on the market, but these wood-based panels are not water-resistant, heat-resistant, and impact-resistant, and do not have Combet performance. In addition, the surface is mostly protected with paint, which is both troublesome to operate and scratch-resistant

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The manufacturing method of the decorative panel of the present embodiment comprises the following steps in turn:

[0027] (1) Fiber preparation: use branches, trunks or branches as raw materials, wash the peeled branches and branches with water, crush the chips into 5mm size, and then cook and grind them to make uniform fibers;

[0028] (2) Sizing treatment: firstly dry the fiber prepared in step (1), weigh the fiber and adhesive in a weight ratio of 3:2 for later use, then add the adhesive gradually by spraying and mix it evenly with the fiber. The injection pressure is 6MPA, and there are 4 nozzles;

[0029] Preparation of the adhesive: get 85% phenolic resin, 12% methanol diluent, 0.5% carbon black, and 2.5% kaolin by weight, add diluent, carbon black, and kaolin to the phenolic resin, stir and mix Uniform and heated to 50°C to prepare adhesive;

[0030] (3) Pre-pressing and hot-pressing: the fibers after sizing treatment are paved, pre-pressed, and hot-pressed to...

Embodiment 2

[0037] The manufacturing method of the decorative panel of the present embodiment comprises the following steps in turn:

[0038](1) Fiber preparation: use branches and branches as raw materials, wash the peeled branches and branches with water, crush the chips into 5mm size, and then cook and heat them to make uniform fibers;

[0039] (2) Sizing treatment: firstly dry the fiber prepared in step (1), weigh the fiber and adhesive in a weight ratio of 2:3 for later use, then add the adhesive gradually by spraying and mix it evenly with the fiber, and then The injection pressure is 6MPA, and there are 3 nozzles;

[0040] Preparation of the adhesive: get 80% phenolic resin, 16% alcohol diluent, 1% carbon black, and 3% kaolin by weight, add diluent, carbon black, and kaolin to the phenolic resin, stir and mix Uniform and heated to 50°C to prepare adhesive;

[0041] (3) Pre-pressing and hot-pressing: the fiber after sizing treatment is paved, pre-pressed, and hot-pressed to make a...

Embodiment 3

[0048] The manufacturing method of the decorative panel of the present embodiment comprises the following steps in turn:

[0049] (1) Fiber preparation: use branches and branches as raw materials, wash the peeled branches and branches with water, crush the chips into 5mm size, and then cook and heat them to make uniform fibers;

[0050] (2) Sizing treatment: firstly dry the fiber prepared in step (1), weigh the fiber and adhesive in a weight ratio of 1:1 for later use, then add the adhesive gradually by spraying and mix it evenly with the fiber, and then The injection pressure is 6MPA, and there are 4 nozzles;

[0051] The preparation of the adhesive: get 87% phenolic resin, 10% methanol-alcohol mixture diluent, 0.7% carbon black, 2.3% kaolin by weight, wherein the methanol-alcohol weight ratio is 1:1, diluent , carbon black, and kaolin are added to the phenolic resin, mixed evenly and heated to 50°C to prepare an adhesive;

[0052] (3) Pre-pressing and hot-pressing: the fib...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a manufacture method for composite wood anti-bending specific plate. The manufacture method comprises the following steps of: manufacturing fibre, preparing adhesive, applying glue, performing pre-pressing and hot-pressing, treating wood veneer, manufacturing wearable bond paper and surface bond paper, and pressing a decorative board. The manufacture method for the composite wood anti-bending specific plate provided by the invention has the technical effects that: the production cost is low; the manufactured composite wood anti-bending specific plate has excellent performance, better water resistance, fire resistance, antibacterial property, and strain resistance; the energy consumption and emission are low; the wood and the anti-bending specific plate are integrally combined, so as to achieve the warm feeling of the wood and the special performance of the anti-bending specific plate; the wearable paper surface is used, so as to not affect the wood effects, achieve super-strong anti-scratch and wear-resisting properties, and abandon the paint surface treatment; and impregnated surface papers with much glue are firmly connected with the veneer and core materials to enable the structure to be firmer.

Description

technical field [0001] The invention relates to a method for making a decorative board, in particular to a method for making a composite solid wood kangbet. Background technique [0002] Combate, also known as Kangbeite, composite solid wood Combate is a one-piece decorative panel produced by dissolution and irreversible aging hardening under high temperature and high pressure. And smoke-resistant characteristics, widely used in indoor and outdoor decoration, kitchen cabinets, office furniture, laboratories and other fields. Composite solid wood Combet, as a special high-pressure decorative fire-resistant board, has become an astonishing advanced concept building material in the construction industry. It is widely used in cabinets, walls, decorations, etc. , inspiration for accessories and the best materials. [0003] At present, the raw material of Combate is kraft paper, which is made of multi-layer kraft paper soaked in phenolic resin and then dried under high temperatu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B27N3/08B27N3/12B27M1/08B27K5/00
CPCB27N1/00B27N1/0209B27N3/12B32B5/02B32B7/12B32B21/06B32B21/10B32B21/13B32B21/14B32B29/02B32B37/02B32B37/06B32B37/10B32B37/12B32B37/15B32B38/08B32B38/164B32B2250/02B32B2307/3065B32B2307/554B32B2307/7145B32B2307/73C09J11/04C09J161/06E04F13/0866
Inventor 孙学民
Owner 江苏天润盛凯新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.