Preparation technology for melt for production of mineral wool, rock wool and cast stone products

A preparation process, slag wool technology, applied in the melt preparation process of rock wool, cast stone products, slag wool field, can solve the problems of poor composition uniformity, long adjustment time, environmental pollution, etc., to achieve energy saving and Cost, homogeneous melt composition, and the effect of reducing environmental pollution

Inactive Publication Date: 2014-02-19
WUHU XINXING DUCTILE IRON PIPES
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The composition in the furnace must be continuously adjusted, and the adjustment time is long, the efficiency is low, and the waste is large when producing products with different composition requirements.
Moreover, it is difficult for the temperature of the melt to exceed 1500°C, the melt in the furnace cannot be stirred, and the uniformity of the composition is poor
Melting ore and other raw materials will also cause a lot of energy consumption and serious environmental pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation technology for melt for production of mineral wool, rock wool and cast stone products

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0040] The specific implementation of the present invention will be described in further detail below by describing the embodiments with reference to the accompanying drawings, so as to help those skilled in the art have a more complete, accurate and in-depth understanding of the inventive concepts and technical solutions of the present invention.

[0041] Such as figure 1 The melt preparation process for the production of slag wool, rock wool, glass-ceramics and cast stone shown in the present invention, in order to solve the problems existing in the prior art and overcome its defects, realize the invention of improving product quality and energy utilization rate Purpose, the technical scheme that the present invention takes is:

[0042] Described melt preparation process is:

[0043] Collect hot slag from blast furnace or converter, add it to heating equipment, and mix the following raw materials: basalt, quartz stone or quartz sand (quartz sand), dolomite; adjust the acidi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation technology for melt for production of mineral wool, rock wool and cast stone products. The preparation technology comprises: collecting hot slag in a blast furnace or a converter, adding into an electromagnetic induction furnace; mixing with the following raw materials: basalt, quartzite, dolomite/quartz sand, and a nucleation agent; adjusting the acidity coefficient and the pH value of the slag; and heating and stirring the slag in the electromagnetic induction furnace until the fluidity, the superheat temperature and the component uniformity of the slag reach the standards, supplying the slag for a material molding apparatus by a melt flow control apparatus. According to the preparation technology, the electrothermal efficiency and the power factor of the electromagnetic induction furnace are high; raw materials and energy are subjected no extra waste; and the preparation technology helps to guarantee the product quality and improve the production efficiency and energy utilization rate.

Description

technical field [0001] The invention belongs to the technical field of inorganic material production technology. Specifically, the invention relates to a melt preparation process for the production of slag wool, rock wool and cast stone products. Background technique [0002] At present, in the production process of domestic slag wool and rock wool, most manufacturers use cupolas as melting equipment, melt basalt, slag, dolomite, etc. with coke in the cupola and supply them to fiber-forming equipment to make fibers. Melting ore and other raw materials will cause a lot of energy consumption and serious environmental pollution. [0003] The composition of the cupola furnace is controlled by the amount of charge into the furnace, and the reaction cycle is long; the control of the melt temperature and supply is adjusted by the coke ratio and the tuyere. There is a direct relationship between temperature and supply. When the temperature rises, the supply is reduced or the supply...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C6/10
Inventor 马冶肖太宝韩正良
Owner WUHU XINXING DUCTILE IRON PIPES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap