Multilayer adhesive article and adhesive sheet

A technology of adhesiveness and articles, applied in the direction of adhesive type, conductive adhesive, acidic copolymer adhesive, etc., can solve the problems of easy peeling and weak bonding force, and achieve the effect of inhibiting interlayer peeling

Inactive Publication Date: 2014-03-12
NITTO DENKO CORP
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, the pressure-sensitive adhesive tape in which the adhesive layer is formed into a multilayer structure as described above has the following disadvantages: the bonding force between the layers is weak, and the layers are easily peeled off due to external stress such as shear force.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multilayer adhesive article and adhesive sheet
  • Multilayer adhesive article and adhesive sheet
  • Multilayer adhesive article and adhesive sheet

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0153] (Synthesis of Acrylic Polymer (a))

[0154] Put 229 parts of ethyl acetate, 0.2 parts of azobisisobutyronitrile, 95 parts of n-butyl acrylate and 5 parts of acrylic acid into a reactor with a thermometer, a stirrer, a nitrogen gas inlet tube and a reflux condenser tube, and carry out at 60 ° C. Solution polymerization was carried out to obtain an acrylic polymer solution A having a concentration of the acrylic polymer (a) of 30% by weight. The weight average molecular weight of the said acrylic polymer (a) was 750,000.

[0155] (Synthesis of Acrylic Polymer (b))

[0156] In the reactor with thermometer, stirrer, nitrogen inlet pipe and reflux condenser, drop 146 parts of ethyl acetate, 0.2 part of azobisisobutyronitrile, 95 parts of 2-ethylhexyl acrylate and 5 parts of acrylic acid, Solution polymerization was performed at 60° C. to obtain an acrylic polymer solution B having a concentration of the acrylic polymer (b) of 40% by weight. The weight average molecular we...

Embodiment 2～14

[0163] [Examples 2 to 14, Comparative Example 1]

[0164] The types and amounts of the monomers used in the synthesis of the acrylic polymers (a) to (c), the amount of the crosslinking agent, and the thickness of each adhesive layer were changed to the values ​​described in Table 1 and Table 2 , except that, the same operation as in Example 1 was performed, and each adhesive tape was produced.

Embodiment 15

[0166] (Synthesis of Acrylic Polymer (a))

[0167] Put 229 parts of ethyl acetate, 0.2 parts of azobisisobutyronitrile, 95 parts of n-butyl acrylate and 5 parts of acrylic acid into a reactor with a thermometer, a stirrer, a nitrogen gas inlet tube and a reflux condenser tube, and carry out at 60 ° C. Solution polymerization was carried out to obtain an acrylic polymer solution A having a concentration of the acrylic polymer (a) of 30% by weight. The weight average molecular weight of the said acrylic polymer (a) was 750,000.

[0168] (Synthesis of Acrylic Polymer (b))

[0169] In the reactor with thermometer, stirrer, nitrogen inlet pipe and reflux condenser, drop 146 parts of ethyl acetate, 0.2 part of azobisisobutyronitrile, 95 parts of 2-ethylhexyl acrylate and 5 parts of acrylic acid, Solution polymerization was performed at 60° C. to obtain an acrylic polymer solution B having a concentration of the acrylic polymer (b) of 40% by weight. The weight average molecular we...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A multilayer adhesive article with a higher interlayer adhesive strength is provided. This multilayer adhesive article is provided with: an adhesive layer (A) formed from an adhesive composition (a) containing, as the main component, an acrylic polymer (a) obtained by polymerizing monomer compositions; an adhesive layer (B) formed from an adhesive composition (b) that contains, as the main component, an acrylic polymer (b) obtained by polymerizing monomer compositions; and an intermediate layer (C) that is positioned between the adhesive layer (A) and the adhesive layer (B). The acrylic polymer (a) and the acrylic polymer (b) contain an acidic group, and the intermediate layer (C) is formed from an intermediate layer composition (c) that contains a polymer (c) containing primary to tertiary amino groups.

Description

technical field [0001] The present invention relates to a multilayer adhesive article and an adhesive sheet obtained by forming the multilayer adhesive article into a sheet shape. This application claims the priority based on the JP Patent application 2011-147446 for which it applied on July 1, 2011, The content of this application is taken in into this specification as a reference. Background technique [0002] Conventionally, pressure-sensitive adhesive tapes such as double-sided adhesive tapes have been required to have contradictory properties such as high wettability to adherends, adhesiveness, and high cohesion at the same time. In addition, when bonding two adherends with different surface properties, it is difficult for a pressure-sensitive adhesive composed of the same composition to exert good adhesive properties on either of the two adherends. It is handled in a balanced way between the characteristics. [0003] In order to improve such aspects, it has been carr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/02C09J7/00C09J9/02C09J133/00C09J7/38C09J7/22
CPCC09J133/02C09J7/02C09J7/0246C09J7/00C09J2201/128C09J7/0217C09J133/00C09J2433/00C08K5/17C09J2433/006C09J2201/36C09J2205/102C09J9/02C09J7/38C09J7/22Y10T428/2848C09J2301/124
Inventor 白井光义船津绘里子每川英利
Owner NITTO DENKO CORP