A gas-assisted rapid clamping ultra-high-strength steel hot stamping die

A technology of hot stamping die and ultra-high-strength steel, which is applied in the field of hot stamping forming, can solve the problems of fast cooling speed of sheet metal, uneven cooling, poor mechanical properties of workpiece, etc., achieve fast mold closing and avoid excessive temperature drop of sheet metal Effect

Inactive Publication Date: 2016-03-02
JILIN UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention designs a gas-assisted rapid clamping ultra-high-strength steel hot stamping die, which mainly solves the problem of excessive cooling of the sheet metal, uneven cooling, and poor mechanical properties of the workpiece caused by the slow clamping speed of the ordinary hydraulic press in the hot stamping forming process. And other issues

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A gas-assisted rapid clamping ultra-high-strength steel hot stamping die
  • A gas-assisted rapid clamping ultra-high-strength steel hot stamping die
  • A gas-assisted rapid clamping ultra-high-strength steel hot stamping die

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] The specific content of the present invention and its specific implementation will be further described below in conjunction with the accompanying drawings.

[0017] The mold refers to figure 2 , including: 1. Upper template, 2. Upper air pipe, 3. Cylinder, 4. Lower air pipe, 5. Fixed plate, 6. Punch die, 7. Lower die holder, 8. Die die, 9. Cooling pipe, 10. Positioning device and other main parts. First, put the heated and heat-preserved sheet 11 on the thermoforming mold, the hydraulic press starts the downward stroke, and its slider pushes the mold upper template 1 to go down, and at the same time, the air in the cylinder 3 pushes the punch 6 to go down quickly, and the sheet 11 is quickly stamped Forming and clamping with the die 8, the slider of the hydraulic press pushes the upper template 1 to continue downward (the gas in the cylinder 3 is compressed, and the piston rod retreats), until it reaches the bottom dead center of the press and stops, the punch 6 and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a super-strength steel hot stamping die capable of carrying out rapid spotting through gas assistance and belongs to the field of hot stamping forming. The die is mainly formed by an air cylinder (3), a male die (6), a female die (8), a fixing plate (5), an upper die plate (1), a lower die base (7) and other main parts. The male die (6) is arranged on the upper die plate (1) through the fixing plate (5). The air cylinder (3) is arranged in the fixing plate. A piston rod of the air cylinder is connected with the male die. In the stamping process, air enters to push the male die to rapidly descend through the air cylinder, a sheet metal (11) is rapidly stamped and formed, and the male die and the female die (8) rapidly carry out spotting. The super-strength steel hot stamping die mainly solves the problems that a used common hydraulic machine is too low in spotting speed, thus, the temperature of the sheet metal drops too fast, the cooling effect is uneven, and the mechanical properties of a workpiece is poor in the hot stamping forming process, and has importance guiding significance on utilizing an existing common hydraulic machine to produce super-strength steel hot stamping pieces for manufacturing enterprises.

Description

Technical field: [0001] The invention relates to a gas-assisted fast die-closing ultra-high-strength steel hot stamping die, which belongs to the technical field of hot stamping forming. Background technique: [0002] Hot stamping forming technology is a new technology used to manufacture ultra-high-strength steel sheet stamping parts for automobiles. The strength of the parts after forming is significantly improved, which can reach 1500MPa. Moreover, the formed parts have small springback and high precision at high temperatures, and are widely used in automobile bodies. In the manufacture of structural parts. The process principle of the hot stamping forming technology is to heat the boron alloy steel plate to 900-950°C, keep it warm for 4-5 minutes to make it completely austenitized, and then quickly move it to a mold with a cooling pipe for rapid stamping (to prevent the plate Excessive reduction of the material temperature), the formed part is cooled and quenched by the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B21D37/12
Inventor 谷诤巍吕萌萌陆冠含张眸睿徐虹李欣
Owner JILIN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com