Hardening and tempering process of alloy-steel pipe
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
An alloy steel pipe, quenching and tempering technology, applied in the direction of manufacturing tools, heat treatment equipment, furnaces, etc., can solve the problems of poor wear resistance, low hardness and large deformation, and achieve the effect of good wear resistance, high hardness and small deformation
Inactive Publication Date: 2014-04-16
佛山市统管金属制品有限公司
View PDF5 Cites 4 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] At present, general alloy steel pipes have weak plasticity, low strength, low pressure resistance, large deformation, low hardness, and poor wear resistance. It is necessary to make alloy steel pipes stronger in plasticity, higher in strength, larger in pressure, smaller in deformation, and harder in hardness. Quenching and tempering process with higher and better wear resistance
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0012] A quenching and tempering process for alloy steel pipes, comprising the steps of:
[0013] 1) Annealing treatment: heat up to 720°C at a rate of 55°C / min, hold for 2.5 hours, then cool to 570°C at a rate of 30°C / min, and then cool to room temperature at a rate of 5°C / min;
[0014] 2) Quenching treatment: heat up to 810°C at a rate of 25°C / min, hold for 3.5 hours, then spray with 35% salt water to rapidly cool to 260°C at a rate of 255°C / s, and then heat at 15°C / min The speed is cooled to 80°C;
[0015] 3) Tempering treatment: heat up to 710°C at a rate of 35°C / min, hold for 8 hours, and then cool to room temperature at a rate of 10°C / min.
Embodiment 2
[0017] A quenching and tempering process for alloy steel pipes, comprising the steps of:
[0018] 1) Annealing treatment: heat up to 700°C at a rate of 50°C / min, hold for 1.5 hours, then cool to 570°C at a rate of 30°C / min, and then cool to room temperature at a rate of 5°C / min;
[0019] 2) Quenching treatment: heat up to 800°C at a rate of 20°C / min, hold for 2.5 hours, then spray with 30% brine to rapidly cool to 250°C at a rate of 250°C / s, and then heat at 15°C / min The speed is cooled to 70°C;
[0020] 3) Tempering treatment: heat up to 700°C at a rate of 30°C / min, hold for 7 hours, and then cool to room temperature at a rate of 10°C / min.
Embodiment 3
[0022] A quenching and tempering process for alloy steel pipes, comprising the steps of:
[0023] 1) Annealing treatment: heat up to 710°C at a rate of 52°C / min, hold for 2 hours, then cool to 570°C at a rate of 30°C / min, and then cool to room temperature at a rate of 5°C / min;
[0024] 2) Quenching treatment: heat up to 804°C at a rate of 23°C / min, hold for 3 hours, then spray with 32% brine to rapidly cool to 257°C at a rate of 253°C / s, and then heat at 15°C / min The speed is cooled to 76°C;
[0025] 3) Tempering treatment: heat up to 702°C at a rate of 33°C / min, hold for 7.5 hours, and then cool to room temperature at a rate of 10°C / min.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention discloses a hardening and tempering process of an alloy-steel pipe. The process comprises the following steps: 1) conducting annealing treatment: heating to the temperature up to 700-720 DEG C at the speed of 50-55 DEG C / min, and conducting heat preservation for 1.5-2.5 hours, cooling the temperature down to 570 DEG C at the speed of 30 DEG C / min, and cooling the temperature down to the room temperature at the speed of 5 DEG C / min; 2) conducting quenching treatment: heating to the temperature up to 800-810 DEG C at the speed of 20-25 DEG C / min, conducting heat preservation for 2.5-3.5 hours, spraying by brine with the concentration of 30-35% to rapidly cool the temperature down to 250-260 DEG C at the speed of 250-255 DEG C / s, and cooling the temperature down to 70-80 DEG C at the speed of 15 DEG C / min; 3) conducting tempering treatment: heating to the temperature up to 700-710 DEG C at the speed of 30-35 DEG C / min, conducting heat preservation for 7-8 hours, and cooling the temperature down to the room temperature at the speed of 10 DEG C / min. Through the adoption of the hardening and tempering process of the alloy-steel pipe, the alloy-steel pipe being subjected to hardening and tempering is high in plasticity, strength, pressure resistance, and hardness, low in deformation, and good in abrasive resistance.
Description
technical field [0001] The invention relates to a quenching and tempering process for alloy steel pipes. Background technique [0002] At present, general alloy steel pipes have weak plasticity, low strength, low pressure resistance, large deformation, low hardness, and poor wear resistance. It is necessary to make alloy steel pipes stronger in plasticity, higher in strength, larger in pressure, smaller in deformation, and harder in hardness. Higher, better wear resistancequenching and tempering process. Contents of the invention [0003] The object of the present invention is to provide a quenching and tempering process for alloy steel pipes, which makes the quenched and tempered alloy steel pipes strong in plasticity, high in strength, high in pressure, small in deformation, high in hardness and good in wear resistance. [0004] In order to achieve the above object, the technical solution of the present invention is to design a quenching and tempering process for alloy...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More 