A kind of imitation stone wallboard coated with anti-ultraviolet coating and preparation method thereof

An anti-ultraviolet coating, imitating stone technology, applied in covering/lining, architecture, building structure, etc., can solve the problems of long construction period, complicated operation, complicated procedures, etc., and achieve easy operation, low process cost and light weight Effect

Active Publication Date: 2016-01-20
王东彬
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the field of construction, block building materials are generally used for masonry in the production of exterior walls, and then thermal insulation, plastering, puttying, painting or exterior wall bricks, or keels and curtain walls are added to the outside of the exterior walls. The operation of the type of work can finally complete the complete construction of the exterior wall, which leads to complicated procedures, complicated operations, and long construction periods

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of imitation stone wallboard coated with anti-ultraviolet coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A stone imitation wallboard coated with an anti-ultraviolet coating, which includes an imitation stone slab base 1, an imitation slate forming layer 2 and an anti-ultraviolet coating 3, the outer surface of the imitation slate base 1 contains an imitation slate forming layer 2, the imitation slate forming A layer of anti-ultraviolet coating 3 is sprayed on the layer 2;

[0028] The described stone-like molding layer 2 is an imitation marble texture layer; the anti-ultraviolet coating 3 is a commercially available anti-ultraviolet paint; the described stone-like base layer 1 is composed of 50% (weight) coal gangue fiber particles, 35 % (weight) polymer fire-resistant modified material, 10% (weight) silicon-aluminum clinker and 5% (weight) stearic acid are mixed and then added with pigments imitating the color of marble.

[0029] A preparation method of a stone-like wallboard coated with an anti-ultraviolet coating, comprising the following steps:

[0030] (1) 50% (weigh...

Embodiment 2

[0037] A stone imitation wallboard coated with an anti-ultraviolet coating, which includes an imitation stone slab base 1, an imitation slate forming layer 2 and an anti-ultraviolet coating 3, the outer surface of the imitation slate base 1 contains an imitation slate forming layer 2, the imitation slate forming A layer of anti-ultraviolet coating 3 is sprayed on the layer 2;

[0038] The described stone-like molding layer 2 is an imitation granite texture layer; the anti-ultraviolet coating 3 is a commercially available anti-ultraviolet paint; the described stone-like base layer 1 is composed of 75% (weight) coal gangue fiber particles, 15 % (weight) polymer fire-resistant modified material, 8% (weight) silicon-aluminum clinker and 2% (weight) stearic acid are mixed and then added with pigments imitating the color of granite.

[0039] A preparation method of a stone-like wallboard coated with an anti-ultraviolet coating, comprising the following steps:

[0040] (1) 75% (weig...

Embodiment 3

[0047] A stone imitation wallboard coated with an anti-ultraviolet coating, which includes an imitation stone slab base 1, an imitation slate forming layer 2 and an anti-ultraviolet coating 3, the outer surface of the imitation slate base 1 contains an imitation slate forming layer 2, the imitation slate forming A layer of anti-ultraviolet coating 3 is sprayed on the layer 2;

[0048] The described imitation stone slab forming layer 2 is an imitation sandstone texture layer; the described anti-ultraviolet coating 3 is a commercially available anti-ultraviolet paint; It is made by mixing % (weight) polymer fireproof modified material, 15% (weight) silicon-aluminum clinker and 5% (weight) stearic acid and adding pigments with imitation sandstone color.

[0049] A preparation method of a stone-like wallboard coated with an anti-ultraviolet coating, comprising the following steps:

[0050] (1) 60% (weight) coal gangue fiber particles, 20% (weight) polymer fireproof modified mater...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flame retardantaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to an imitation stone wallboard with thermal insulation and anti-ultraviolet coating and a preparation method thereof, which comprises an imitation stone slab base (1), an imitation stone slab forming layer (2) and an anti-ultraviolet coating (3), an imitation stone slab base (1) ) is provided with an imitation stone slab forming layer (2) on the outer surface, and a layer of anti-ultraviolet coating (3) is sprayed on the imitation stone slab forming layer (2); the imitation stone slab base layer (1) is added with imitation stone color pigments. The process steps are: mix coal gangue fiber particles, polymer fire-resistant modified materials, silicon-aluminum clinker and stearic acid, then add pigments with imitation stone colors according to production needs, dry and stir at 150°, and mix for 20 minutes. It is injected into a mold with imitation stone texture, and the outer decorative surface of the formed product is sprayed with anti-ultraviolet paint. The invention has the advantages of simple and convenient operation, simplified process, beautiful appearance, environmental protection and energy saving.

Description

technical field [0001] The invention belongs to the field of building boards, and in particular relates to a stone imitation wall board coated with an anti-ultraviolet coating and a preparation method thereof. Background technique [0002] In the field of construction, block building materials are generally used for masonry in the production of exterior walls, and then thermal insulation, plastering, puttying, painting or exterior wall bricks, or keels and curtain walls are added to the outside of the exterior walls. The operation of the type of work can finally complete the complete construction of the outer wall, which leads to complicated procedures, complicated operations, and long construction periods. Contents of the invention [0003] The technical problem to be solved by the present invention is to propose a kind of imitation stone wallboard coated with an anti-ultraviolet coating and a preparation method thereof, which is convenient in operation, simplified in pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): E04F13/075
Inventor 程凤岐王东彬
Owner 王东彬
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products