Environmental-friendly sound insulation building material

A building material and environmental protection technology, applied in the field of environmental protection sound insulation building materials, can solve the problems of no flame retardant effect, inability to prevent mosquitoes, poor low frequency sound absorption effect of glass fiber materials, etc., and achieve the effect of high sound insulation performance and good damping effect.

Inactive Publication Date: 2014-05-21
QINGDAO QIANXIANG ENVIRONMENTAL PROTECTION TECH
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing traditional sound insulation materials for architectural decoration are mainly glass fiber. Its disadvantages are that the glass fib

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0008] Example 1

[0009] An environmentally friendly soundproof building material, which is composed of the following components by weight: 1 part of adhesive, 10 parts of plant fibers, 20 parts of mixed solvent, 5 parts of inorganic thickener, 5 parts of toughening agent, and 5 parts of flame retardant , 5 parts of auxiliary flame retardant, 2 parts of mica powder, 1 part of diatomaceous earth, 0.5 part of ceramic powder, 3 parts of n-butanol, 6 parts of xylene, 0.3 part of montmorillonite clay thickener, 0.1 part of wetting agent , 0.3 part of dispersant, 0.1 part of antifungal agent, 0.1 part of preservative, 0.3 part of defoamer, 1.0 part of film-forming aid, 0.2 part of antifreeze, 1 part of rutile titanium dioxide.

Example Embodiment

[0010] Example 2

[0011] An environmentally friendly soundproof building material, which is composed of the following components by weight: 2 parts of adhesive, 15 parts of plant fibers, 50 parts of mixed solvent, 20 parts of inorganic thickener, 10 parts of toughening agent, and 15 parts of flame retardant , 15 parts of auxiliary flame retardant, 4 parts of mica powder, 6 parts of diatomaceous earth, 1.5 parts of ceramic powder, 10 parts of n-butanol, 9 parts of xylene, 0.5 part of montmorillonite clay thickener, 0.3 part of wetting agent , 0.5 part of dispersant, 0.2 part of antifungal agent, 0.2 part of preservative, 0.4 part of defoamer, 2.0 part of film-forming aid, 0.5 part of antifreeze, and 3 parts of anatase titanium dioxide.

Example Embodiment

[0012] Example 3

[0013] An environmentally friendly soundproof building material, which is composed of the following components by weight: 2 parts of adhesive, 15 parts of plant fibers, 50 parts of mixed solvent, 20 parts of inorganic thickener, 10 parts of toughening agent, and 15 parts of flame retardant , 15 parts of auxiliary flame retardant, 4 parts of mica powder, 6 parts of diatomaceous earth, 1.5 parts of ceramic powder, 10 parts of n-butanol, 9 parts of xylene, 0.5 part of montmorillonite clay thickener, 0.3 part of wetting agent , 0.5 part of dispersant, 0.2 part of antifungal agent, 0.2 part of preservative, 0.4 part of defoamer, 2.0 part of film-forming aid, 0.5 part of antifreeze, 1-3 parts of lithopone.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an environmental-friendly sound insulation building material which comprises the following components in parts by weight: 1-2 parts of binding agents, 10-15 parts of plant fibers, 20-50 parts of mixed solvents, 5-20 parts of inorganic thickening agents, 5-10 parts of toughening agents, 5-15 parts of fire retardants, 5-15 parts of auxiliary fire retardants, 2-4 parts of mica powder, 1-6 parts of diatomite, 0.5-1.5 parts of ceramic powder, 3-10 parts of n-butyl alcohol, 6-9 parts of dimethyl benzene, 0.3-0.5 part of montmorillonite clay thickening agents, 0.1-0.3 part of wetting agents, 0.3-0.5 part of dispersing agents, 0.1-0.2 part of mildew-proof agents, 0.1-0.2 part of preservative agents, 0.3-0.4 part of defoaming agents, 1.0-2.0 parts of film-forming auxiliary agents, 0.2-0.5 part of anti-freezing agents and 1-3 parts of pigments. The environmental-friendly sound insulation building material disclosed by the invention has the advantages of good damping effect and high sound insulation property, and can not generate the substance harmful to a human body and the environment after being combusted.

Description

technical field [0001] The invention relates to an environment-friendly and sound-insulating building material. Background technique [0002] The existing traditional sound insulation materials for architectural decoration are mainly glass fiber. Its disadvantages are that the glass fiber material has poor sound absorption effect at low frequencies, has no flame retardant effect, and cannot prevent mosquitoes. Harmful gases are also produced. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide an environment-friendly building material with good sound insulation effect and no harm to human body. [0004] In order to solve the problems of the technologies described above, the technical solution adopted in the present invention is: [0005] An environment-friendly and sound-insulating building material, which is composed of the following ingredients in parts by weight: 1-2 parts of adhesive, 10-15 parts of plant fiber...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/00C04B26/00
Inventor 田福祯高伟张劭朱兵建金海
Owner QINGDAO QIANXIANG ENVIRONMENTAL PROTECTION TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap