Viscose glue, viscose glue plaster prepared from viscose glue, and making method and application of viscose glue plaster

A production method and adhesive technology, which are applied in the field of adhesive stickers, can solve the problems of unsafe use, cannot be reused, and have residues, and achieve the effects of easy tearing, large application scope, market prospects, and good adhesion.

Active Publication Date: 2014-06-04
SHENZHEN BENKS TECH
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In order to overcome the technical problems that the existing adhesive paste has residue, cannot be reused, and is unsafe to use, the present invention provides a traceless, repeatable and safe adhesive and an adhesive paste prepared by using the adhesive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Viscose glue, viscose glue plaster prepared from viscose glue, and making method and application of viscose glue plaster
  • Viscose glue, viscose glue plaster prepared from viscose glue, and making method and application of viscose glue plaster

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0065] Embodiment 1, the sticking object is a smooth sticking surface.

[0066] Raw materials are provided, and the proportioning ratio of various raw materials is as follows (the content described below is the ratio of the total weight of the raw materials):

[0067] Solid silicone rubber (40%-50%),

[0068] Tackifier (50%-60%),

[0069] Vulcanizing agent (1-5%),

[0070] Snake glue (0.1%-1%);

[0071] or,

[0072] Solid synthetic resin (40%-50%),

[0073] Tackifier (50%-60%),

[0074] Vulcanizing agent (1-5%),

[0075] Snake glue (0.1%-1%);

[0076] or,

[0077] Solid silicone resin (40%-50%),

[0078] Tackifier (50%-60%),

[0079] Vulcanizing agent (1-5%),

[0080] Snake gum (0.1%-1%).

[0081] Mix the above materials at room temperature and put them into an open mixer for kneading to make the materials diffuse or infiltrate each other. The mixing temperature is selected to be carried out at normal temperature, the mixing time is 0.5-2 hours, and the best effec...

Embodiment 2

[0084] In the second embodiment, the sticking object is a rough sticking surface.

[0085] Raw materials are provided, and the proportioning ratio of various raw materials is as follows (the content described below is the ratio of the total weight of the raw materials):

[0086] Solid silicone rubber (50%-60%),

[0087] Tackifier (40%-50%),

[0088] Vulcanizing agent (1-5%),

[0089] Snake glue (0.1%-1%);

[0090] or,

[0091] Solid synthetic resin (50%-60%),

[0092] Tackifier (40%-50%),

[0093] Vulcanizing agent (1-5%),

[0094] Snake glue (0.1%-1%);

[0095] or,

[0096] Solid silicone resin (50%-60%),

[0097] Tackifier (40%-50%),

[0098] Vulcanizing agent (1-5%),

[0099] Snake gum (0.1%-1%).

[0100] Mix the above materials at room temperature and put them into an open mixer for kneading to make the materials diffuse or infiltrate each other. The mixing temperature is selected to be carried out at normal temperature, the mixing time is 0.5-2 hours, and the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a viscose glue and a viscose glue plaster prepared from the viscose glue, wherein the viscose glue is capable of realizing non-trace adhesion and being repeatedly used for multiple times. The main components of the viscose glue include silica gel and a tackifier, the silica gel weight accounts for 40%-60% of the overall weight of the viscose glue, and the tackifier weight accounts for 40%-60% of the overall weight of the viscose glue. The viscose glue has high activity groups, and when in use, the viscose glue can fill gaps on the glued material surface to exclude air inside the gaps so as to enable the viscose glue to attach to the glued material surface. The viscose glue mainly depends on adsorption type adhesive force for attaching, so that the viscose glue is convenient to tear off, and no residual excess viscose glue may be left on an attached material. The viscose glue plaster prepared from the viscose glue, which has a certain pattern, can be widely applied to sticky hooks, hanging pasters, electronic product pasting films and other various home furnishing, advertising and printing products, and has a great applicable range and market prospect.

Description

【Technical field】 [0001] The invention relates to an adhesive material, in particular to an adhesive that realizes traceless bonding and can be used repeatedly, and an adhesive sticker prepared by using the adhesive. 【Background technique】 [0002] Traditional object fixing methods mainly include nailing, gluing, and adsorption. The fixation of relatively solid objects generally adopts the method of nailing, and its disadvantages are: nail marks will be left, and the nail marks cannot be repaired, and will cause damage to the fixed body, and at the same time increase the difficulty of fixing. Generally, this fixing method is not selected. For the fixing of relatively light objects, the fixing method of glue or adsorption is generally adopted. [0003] If the adsorption method is used, electrostatic materials must be used. Since electrostatic materials are new materials developed in recent years, this new material itself is not environmentally friendly. At the same time, du...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J183/04C09J193/04C09J145/00C09J161/14C09J193/00C09J193/02C09J145/02C09J11/06C09J7/02
Inventor 黄斐
Owner SHENZHEN BENKS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap