An orange color crystal bead embryo and its preparation method

A technology for crystal bead embryo and color, applied in the field of orange-red color crystal bead embryo and its preparation, can solve the problems of uneven color, environmental pollution, poor coloring and the like, and achieve good colorability, good production efficiency and good gloss. Effect

Active Publication Date: 2016-03-23
浙江鑫伟兴水晶有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Orange-colored crystal bead embryos are semi-finished products used to prepare orange-red-colored crystal products. The existing orange-red color crystal bead embryos are manufactured in a crucible, which has poor coloring, uneven colors, patterns, and unstable product quality. Low efficiency, not suitable for continuous mass production, and burning with coal causes environmental pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A kind of orange-red color crystal bead embryo of the present invention, this orange-red color crystal bead embryo is made up of following proportioning composition by weight: 200 parts of quartz sands, 20 parts of zinc oxides, 55 parts of soda ash, 30 parts of potassium carbonate, 20 parts of boric acid 6 parts of calcium carbonate, 2.5 parts of aluminum hydroxide, 2.5 parts of table salt, 2.6 parts of cadmium yellow, 2 parts of selenium powder and 5.5 parts of cadmium red.

[0018] The preparation process of described orange color crystal bead embryo is as follows:

[0019] 1) Extract 200 parts of quartz sand, 20 parts of zinc oxide, 55 parts of soda ash, 30 parts of potassium carbonate, 20 parts of boric acid, 6 parts of calcium carbonate, 2.5 parts of aluminum hydroxide, 2.5 parts of table salt, and 2.6 parts of cadmium yellow according to the weight ratio , 2 parts of selenium powder and 5.5 parts of cadmium red are mixed evenly;

[0020] 2) Granulate the uniforml...

Embodiment 2

[0025] It differs from Example 1 in that the orange-red color crystal bead embryo is made up of the following proportioning ingredients in parts by weight: 300 parts of quartz sand, 60 parts of zinc oxide, 100 parts of soda ash, 50 parts of potassium carbonate, 45 parts of boric acid, 12 parts of calcium carbonate, 5 parts of aluminum hydroxide, 5 parts of table salt, 3.5 parts of cadmium yellow, 3.5 parts of selenium powder and 10 parts of cadmium red.

Embodiment 3

[0027] It differs from Example 1 in that the orange-red color crystal bead embryo is made up of the following proportioning ingredients in parts by weight: 250 parts of quartz sand, 40 parts of zinc oxide, 80 parts of soda ash, 45 parts of potassium carbonate, 30 parts of boric acid, 8 parts of calcium carbonate, 4 parts of aluminum hydroxide, 4 parts of table salt, 3 parts of cadmium yellow, 3 parts of selenium powder and 7 parts of cadmium red.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses an orange color crystal pearl blank and a preparation method thereof. The orange color crystal pearl blank comprises, by weight, 200-300 parts of quartz sand, 20-60 parts of zinc oxide, 40-100 parts of soda ash, 10-50 parts of potassium carbonate, 15-45 parts of boric acid, 2-12 parts of calcium carbonate, 0,8-5 parts of aluminum hydroxide, 1-5 parts of gravy salt, 1-3.5 parts of cadmium yellow, 0.5-3.5 parts of selenium powder, and 0.9-10 parts of cadmium red. According to the present invention, during orange color crystal pearl blank preparing, oxidation reduction balance of copper ions during a melting process maintains a stable state so as to obtain good colorability; and the lead-containing raw material is not used, and advantages of good gloss, bright and uniform color, no color difference, no pattern, high yield, no lead, no pollution and good production benefit are provided.

Description

technical field [0001] The invention relates to an orange-red color crystal bead embryo and a preparation method thereof. Background technique [0002] Orange color crystal bead embryos are semi-finished products used to prepare orange color crystal products. The existing orange color crystal bead embryo technology is manufactured in a crucible, which has poor coloring, uneven colors, patterns, and unstable product quality. The efficiency is low, it is not suitable for continuous mass production, and the burning of coal causes environmental pollution. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide an orange-red color crystal bead embryo with good coloring reproducibility, consistent color, no color difference, no pattern, stable product quality, high production efficiency, and suitable for continuous tank kiln production operations. [0004] In order to solve the above problems, the present invention is achieve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C6/06C03C4/02
Inventor 杨鑫法
Owner 浙江鑫伟兴水晶有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com