Preparation method of light-peach-colored crystal bead blanks

A technology of crystal bead embryos and shallow peach, applied in glass pressing, glass manufacturing equipment, manufacturing tools and other directions, can solve the problems of poor coloring reproducibility, unstable product quality, low production efficiency, etc., to improve efficiency and productivity, Good reproducibility, non-volatile effect

Active Publication Date: 2014-07-30
浙江鑫伟兴水晶有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a method for the disadvantages of poor coloring reproducibility, unstable product quality, low production efficiency, and unsuitability for continuous tank kiln production operations in the existing technology for preparing light peach-colored crystal bead embryos. A method for preparing light peach-colored crystal bead embryos with good coloring reproducibility, stable product quality, and high production efficiency, which is suitable for continuous tank kiln production operations

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A preparation method of light peach-colored crystal bead embryos, the preparation method of light peach-colored crystal bead embryos comprises the following steps:

[0020] (1) Weigh out the raw materials of the light peach-colored crystal bead embryos according to the weight ratio and mix them evenly. Wherein, the raw material formula (weight ratio) of the light peach-colored crystal bead embryos is: 50 parts of quartz sand, 8 parts of soda ash, potassium carbonate 7 parts, 2 parts potassium nitrate, 2 parts boric acid, 45 parts lead silicate, 1 part antimony trioxide, 6 parts cerium oxide, 1 part, 2 parts barium carbonate, 10 parts titanium dioxide, 1 part zinc oxide, erbium oxide 10 copies;

[0021] (2) the light peach-colored crystal bead embryo raw material that mixes uniformly is granulated by a granulator;

[0022] (3) Put the granulated light peach-colored crystal bead embryo raw material into a glass crystal pool furnace for melting. During melting, the temper...

Embodiment 2

[0025] A preparation method of light peach-colored crystal bead embryos, the preparation method of light peach-colored crystal bead embryos comprises the following steps:

[0026] (1) Weigh out the raw materials of the light peach-colored crystal bead embryos according to the weight ratio and mix them evenly. Wherein, the raw material formula (weight ratio) of the light peach-colored crystal bead embryos is: 70 parts of quartz sand, 15 parts of soda ash, potassium carbonate 16 parts, 9 parts of potassium nitrate, 5 parts of boric acid, 55 parts of lead silicate, 3 parts of antimony trioxide, 8 parts of cerium oxide, 5 parts of barium carbonate, 5 parts of titanium dioxide, 3 parts of zinc oxide, 7 parts of erbium oxide;

[0027] (2) the light peach-colored crystal bead embryo raw material that mixes uniformly is granulated by a granulator;

[0028] (3) Put the granulated light peach-colored crystal bead embryo raw material into a glass crystal pool furnace for melting. During ...

Embodiment 3

[0031] A preparation method of light peach-colored crystal bead embryos, the preparation method of light peach-colored crystal bead embryos comprises the following steps:

[0032] (1) Weigh out the raw materials of the light peach-colored crystal bead embryos according to the weight ratio and mix them evenly, wherein the raw material formula (weight ratio) of the light peach-colored crystal bead embryos is: 60 parts of quartz sand, 10 parts of soda ash, potassium carbonate 14 parts, 6 parts of potassium nitrate, 4 parts of boric acid, 63 parts of lead silicate, 2 parts of antimony trioxide, 1 part of cerium oxide, 2 parts of barium carbonate, 9 parts of titanium dioxide, 1 part of zinc oxide, 13 parts of erbium oxide;

[0033] (2) the light peach-colored crystal bead embryo raw material that mixes uniformly is granulated by a granulator;

[0034] (3) Put the granulated light peach-colored crystal bead embryo raw material into a glass crystal pool furnace for melting. During me...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of light-peach-colored crystal bead blanks. Aiming at defects of poor coloring reproducibility, poor product stability, low production efficiency, and unsuitability for continuous tank furnace production of prior art for preparing light-peach-colored crystal bead blanks, the invention provides a light-peach-colored crystal bead blank preparation method with good coloring reproducibility, stable product quality, high production efficiency, and suitability for continuous tank furnace production. According to the light-peach-colored crystal bead blank preparation method, the light-peach-colored crystal bead blanks are prepared from raw materials of, by weight: 50-70 parts of quartz sand, 5-15 parts of soda ash, 7-16 parts of potassium carbonate, 2-9 parts of potassium nitrate, 2-5 parts of boric acid, no more than 45-65 parts of lead silicate, no more than 3 parts of antimony trioxide, no more than 8 parts of cerium oxide, no more than 5 parts of barium carbonate, no more than 10 parts of titanium pigment, no more than 3 parts of zinc oxide, and no more than 15 parts of erbium oxide.

Description

technical field [0001] The invention relates to the field of artificial crystal products, in particular to a method for preparing light peach-colored crystal bead embryos. Background technique [0002] Light peach-colored crystal bead embryos are semi-finished products used to prepare light peach-colored crystal products. In the existing process of preparing light peach-colored crystal bead embryos, erbium ions are used for coloring. Erbium ions are provided by erbium trioxide. The products produced by the light peach color crystal bead embryo technology generally have the disadvantages of poor coloring reproducibility, unstable product quality, low production efficiency, and are not suitable for continuous tank kiln production operations. In addition, in the existing technology for preparing light peach-colored crystal bead embryos, there is red lead component in the raw material formula of light peach-colored crystal bead embryos, and red lead is volatile and will cause en...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C6/04C03C4/02C03B11/00
CPCY02P40/57
Inventor 杨鑫法
Owner 浙江鑫伟兴水晶有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com