Insulation column for power equipment

A technology for power equipment and insulating columns, applied in the field of insulating columns, can solve problems such as creepage, pollution flashover, and poor effect

Inactive Publication Date: 2014-07-30
甘肃兴通电力安装工程有限公司
View PDF6 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The current insulation column has poor creepage prevention effect and is prone to creepage and pollution flashover accidents

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Insulation column for power equipment

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Insulating coating composition formula is as follows in parts by weight:

[0030] Film-forming resin: 40 parts of brominated bisphenol A epoxy resin; modifier: 6 parts of methylphenyl silicone resin; filler: 20 parts of porcelain powder; diluent: 15 parts of xylene; curing agent: aliphatic amine 9 parts of primary amine; plasticizer: 10 parts of dibutyl phthalate.

[0031] The preparation method is as follows:

[0032] (1) Add the film-forming resin, modifier, diluent and plasticizer into the dispersion tank according to the proportion, stir and disperse evenly;

[0033] (2) Add the mixture and filler in step (1) into the paint grinding tank, stir and grind until the fineness is less than or equal to 45um;

[0034] (3) Fully stir the mixture in step (2) and curing agent to form an insulating coating.

[0035] The method of use is as follows:

[0036] The insulating coating is applied to the outer surface of the ceramic insulator by conventional methods such as spray...

Embodiment 2

[0039] Insulating coating composition formula is as follows in parts by weight:

[0040] Film-forming resin: 45 parts of brominated bisphenol A epoxy resin; modifier: 8 parts of methylphenyl silicone resin; filler: 15 parts of porcelain powder; diluent: 15 parts of xylene; curing agent: aliphatic amine 8 parts of primary amine; plasticizer: 9 parts of dibutyl phthalate.

[0041] The preparation method is as follows:

[0042] (1) Add the film-forming resin, modifier, diluent and plasticizer into the dispersion tank according to the proportion, stir and disperse evenly;

[0043] (2) Add the mixture and filler in step (1) into the paint grinding tank, stir and grind until the fineness is less than or equal to 45um;

[0044] (3) Fully stir the mixture in step (2) and curing agent to form an insulating coating.

[0045] The method of use is as follows:

[0046] The insulating coating is applied to the outer surface of the ceramic insulator by conventional methods such as sprayi...

Embodiment 3

[0049] Insulating coating composition formula is as follows in parts by weight:

[0050] Film-forming resin: 36 parts of brominated bisphenol A epoxy resin; modifier: 5 parts of methylphenyl silicone resin; filler: 25 parts of porcelain powder; diluent: 15 parts of xylene; curing agent: aliphatic amine 10 parts of primary amine; plasticizer: 9 parts of dibutyl phthalate.

[0051] The preparation method is as follows:

[0052] (1) Add the film-forming resin, modifier, diluent and plasticizer into the dispersion tank according to the proportion, stir and disperse evenly;

[0053] (2) Add the mixture and filler in step (1) into the paint grinding tank, stir and grind until the fineness is less than or equal to 45um;

[0054] (3) Fully stir the mixture in step (2) and curing agent to form an insulating coating.

[0055] The method of use is as follows:

[0056] The insulating coating is applied to the outer surface of the ceramic insulator by conventional methods such as spray...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an insulation column for power equipment. The insulation column for the power equipment comprises a ceramic insulator. The two ends of the ceramic insulator are respectively provided with a threaded hole. The ceramic insulator comprises an insulator body (1) and an insulation umbrella (2) arranged on the insulator body (1). The inclination angle (a) of the umbrella skirt of the insulation umbrella (2) ranges from 12 degrees to 15 degrees. The thickness (h) of the root of the umbrella skirt ranges from 8 mm to 10 mm. The outer surface of the ceramic insulator is coated with a layer of insulating paint. The insulation column for the power equipment can prevent the creepage phenomenon.

Description

technical field [0001] The invention relates to an insulating column for electric equipment. Background technique [0002] The insulating column is a special component that provides the use requirements, installation methods and surrounding application environment requirements for related equipment in the fields of communication cabinets, electric power, lightning protection, machinery, medical treatment, wind energy, and frequency conversion equipment. It mainly functions as fixed support, connection and insulation. The role of insulators, also known as insulators, insulating spacers. Creepage phenomenon refers to the slight discharge phenomenon on the surface of the insulator between the two stages, causing the surface of the insulator (generally) to appear as branches or meridian-like discharge traces of leaves. The current insulating columns have poor creepage prevention effect, and are prone to creepage and pollution flashover accidents. Contents of the invention ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H01B17/50H01B17/40H01B17/14C09D163/00C09D5/25C09D7/12
Inventor 尤晓群孙立伟吕斌李时捷王伟军葛志峰周肖钧邬云霞
Owner 甘肃兴通电力安装工程有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com