Code spraying ink for tire and preparation method thereof

An ink and coding technology, applied in the direction of ink, application, household appliances, etc., can solve the problems of error-prone, increase in return glue, etc., and achieve the effect of not easily blocking the nozzle, ensuring the bonding force, and good adhesion.

Active Publication Date: 2014-08-06
上海锐炽化工科技有限公司
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The traditional contact roller printing method needs to adjust the printing when the specification is switched, which is prone to errors and leads to increased return glue

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A preparation method of inkjet printing ink for tires:

[0028] (1) 2.5KG polyurethane resin and 3.75KG titanium dioxide are compounded in the extruder

[0029] (2) Put 50KG of solvent into the reaction kettle according to the formula requirements, and stir;

[0030] (3) Keep stirring and put 0.75KG of additive resin into the reaction kettle in turn, and stir for 5-8 hours;

[0031] (4) Slowly drop the composite resin into the reactor;

[0032] (5) Add 0.75 anti-settling agent into the reaction kettle and stir for 2 to 3 hours

[0033] (6) When all the solids are dissolved and mixed evenly, shut down and settle for more than 12 hours;

[0034] (7) Measure the solid content and adjust to the theoretical value;

[0035] (8) Weigh the package.

Embodiment 2

[0037] A preparation method of inkjet ink for tires, the method comprises the following processing steps:

[0038] (1) Polyurethane resin 10kg and titanium dioxide 15kg are first compounded with an extruder to make a composite resin;

[0039] (2) All solvent toluene 150kg is put into reaction kettle earlier by formula requirement, and stir;

[0040] (3) Keep stirring and drop 0kg of additive resin acrylic resin into the reactor successively, stir for 5 hours;

[0041] (4) Slowly drop the composite resin into the reaction kettle after mixing evenly;

[0042] (5) Add 3kg of anti-settling agent into the reaction kettle and stir for 2 hours;

[0043] (6) When all the solids are dissolved and mixed evenly, shut down and settle for more than 12 hours;

[0044] (7) measure solid content, and adjust to theoretical value, theoretical value is 15%;

[0045] (8) Weigh the package.

Embodiment 3

[0047] A preparation method of inkjet ink for tires, the method comprises the following processing steps:

[0048] (1) 25kg of polyurethane resin and 50kg of titanium dioxide are first compounded with an extruder to make a composite resin;

[0049] (2) earlier all solvent butanone 500kg is dropped in the reaction kettle by formula requirement, and stir;

[0050] (3) Keep stirring and drop 10kg of additive resin petroleum resin into the reaction kettle successively, stir for 8 hours;

[0051] (4) Slowly drop the composite resin into the reaction kettle after mixing evenly;

[0052] (5) 10kg of anti-settling agent is added in the reactor, and stirred for 3 hours;

[0053] (6) When all the solids are dissolved and mixed evenly, shut down and settle for more than 12 hours;

[0054] (7) measure solid content, and adjust to theoretical value, theoretical value is 20%;

[0055] (8) Weigh the package.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to code spraying ink for a tire and a preparation method thereof. The ink comprises the following raw materials in parts by weight: 10-25 parts of polyurethane resin, 15-50 parts of titanium dioxide, 0-10 parts of additive resin, 3-10 parts of an anti-settling agent and 150-500 parts of a solvent. The preparation method comprises the following steps: compounding the polyurethane resin and the titanium dioxide by using an extruder and preparing composite resin; putting all the solvents into a reaction kettle according to the formula requirements and agitating; keep agitating, adding the additive resin into the reaction kettle in sequence and agitating for 5-8 hours; slowly putting the composite resin into the reaction kettle after uniform mixing; adding the anti-settling agent into the reaction kettle and agitating for 2-3 hours; stopping and settling for above 12 hours when all solids are dissolved and uniformly mixed; measuring the contents of the solids and adjusting the contents to theoretical values; and weighing and packaging. Compared with the prior art, the code spraying ink has the advantages of good binding force, clear writing, no ink flying and the like.

Description

technical field [0001] The invention relates to an ink and a preparation method thereof, in particular to a coding ink for tires and a preparation method thereof. Background technique [0002] Tires are one of the important parts of the car. They are in direct contact with the road surface, and work together with the car suspension to ease the impact of the car while driving, ensuring that the car has good seating comfort and smooth driving; ensuring that the wheels and the road are in good condition The adhesion of the tire improves the traction, braking and passability of the car; bearing the weight of the car, the important role played by the tire on the car has attracted more and more attention. The material of the tire is generally rubber. In order to improve the performance of the rubber tire, various patterns are printed on the surface of the tire. When the tire is extruded from the production material, it is necessary to roll the tire's specification model, producti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/30C09D11/322
Inventor 栗建民
Owner 上海锐炽化工科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com