Polyvinylidene fluoride modified polyvinyl chloride coating

A polyvinylidene fluoride, polyvinylidene fluoride resin technology, applied in anti-corrosion coatings, coatings and other directions, can solve the problems of short service life, low adhesion, poor corrosion resistance and so on

Active Publication Date: 2016-08-17
ZHEJIANG YONGGUWEIHUA COATING
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the anti-corrosion coatings commonly used in the market include perchlorethylene coatings, high-chlorinated polyethylene coatings, PF-01 Yingdan polyvinyl chloride coatings, chlorinated rubber coatings, etc. They have their own advantages, some have better corrosion resistance, and some have better corrosion resistance. The flexibility is good, etc., but there are generally shortcomings such as thin and brittle paint film, low adhesion, many coats, short service life, and some poor corrosion resistance. Based on the existence of these problems, Zhejiang Yonggu Weihua Coatings Co., Ltd., together with anticorrosion coating experts from Tsinghua University and Zhejiang University of Technology, has developed a new type of anticorrosion coating - polyvinylidene fluoride modified polyvinylidene fluoride Vinyl chloride coating, that is, FVC anti-corrosion coating, has been well received by users and has achieved good social and economic benefits

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] (1) Preparation of polyvinylidene fluoride resin glue: put 13.5 parts of dimethylacetamide into a reaction kettle with a kettle temperature of 85°C, slowly and evenly add 4.0 parts of polyvinylidene fluoride at a stirring speed of 250 rpm Vinyl fluoride resin, continue to stir for 30 minutes after adding, when the material is colorless and transparent, it is polyvinylidene fluoride resin glue;

[0014] (2) Preparation of modified polyvinyl chloride resin glue: first plasticize polyvinyl chloride resin: put 7.0 parts of polyvinyl chloride resin into a batching cylinder with a high-speed centrifugal device, and add 0.7 parts of dioctyl phthalate at the same time Plasticizer, the resin is plasticized under high-speed centrifugation. When the temperature rises to 80°C, the centrifuge is shut down, and the cooled material is plasticized polyvinyl chloride resin; another 33.0 parts of cyclohexanone is put into the reaction kettle, and the temperature is raised to 80°C, put th...

Embodiment 2

[0019] (1) Preparation of polyvinylidene fluoride resin glue: put 13.5 parts of dimethylacetamide into a reaction kettle with a kettle temperature of 85°C, slowly and evenly add 4.0 parts of polyvinylidene fluoride at a stirring speed of 250 rpm Vinyl difluoride resin, continue to stir for 30 minutes after adding, when the material is colorless and transparent, it is polyvinylidene fluoride resin glue;

[0020] (2) Preparation of modified polyvinyl chloride resin glue: first plasticize polyvinyl chloride resin: put 7.0 parts of polyvinyl chloride resin into a batching cylinder with a high-speed centrifugal device, and add 0.7 parts of dioctyl phthalate at the same time Plasticizer, the resin is plasticized under high-speed centrifugation. When the temperature rises to 80°C, the centrifuge is shut down, and the cooled material is plasticized polyvinyl chloride resin; another 33.0 parts of cyclohexanone is put into the reaction kettle, and the temperature is raised to 80°C, put ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses polyvinylidene fluoride modified polyvinyl chloride paint, which is composed of two components A and B, wherein component A mainly consists of polyvinyl chloride resin, dioctyl phthalate, polyvinylidene fluoride It is developed from vinyl resin, dimethylformamide, modified high-chlorinated polyethylene resin, xylene formaldehyde resin, fluorocarbon modified polysiloxane and other materials; component B is isocyanate adduct; before use, according to weight Ratio of component A: component B = 100.0:9.0-12.0 is formulated into polyvinylidene fluoride modified polyvinyl chloride coating, referred to as FVC anti-corrosion coating. This coating has good matrix binding force, super high weather resistance, outstanding Chemical medium resistance and high temperature resistance, long-term service temperature between 120-150 ° C, widely used in chemical, petroleum, pharmaceutical, food and other industries as anti-corrosion protective coatings in engineering buildings, equipment components and production devices layer, its service life can reach more than 10 years, it is very popular among users and has high economic and social benefits.

Description

1. Technical field [0001] The invention belongs to the field of polymer material science and industrial anti-corrosion engineering. It is a two-component solvent-based polyvinylidene fluoride modified polyvinyl chloride anti-corrosion coating, referred to as FVC anti-corrosion coating, which has temperature resistance, weather resistance and chemical resistance. Medium corrosion and other characteristics. 2. Technical Background [0002] At present, the commonly used anti-corrosion coatings in the market include perchlorethylene coatings, high-chlorinated polyethylene coatings, PF-01 Yingdan polyvinyl chloride coatings, chlorinated rubber coatings, etc. They have their own advantages, some have better corrosion resistance, and some have better corrosion resistance. The flexibility is good, etc., but there are generally shortcomings such as thin and brittle paint film, low adhesion, many coats, short service life, and some poor corrosion resistance. Based on the existence of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D127/06C09D127/16C09D5/08C09D7/12
Inventor 金辉金如朋
Owner ZHEJIANG YONGGUWEIHUA COATING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com