Transparent impact-resistance polystyrene and preparation method thereof

A polystyrene, impact-resistant technology, applied in the field of thermoplastic materials, can solve the problems that affect the service life and application range of transparent high-impact polystyrene materials, low hardness and rigidity, poor transparency, etc., to achieve good durability Folding and tear resistance, good dimensional stability, good formability

Active Publication Date: 2014-10-08
DONGGUAN DECHENG PLASTIC TECH
View PDF5 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In the above-mentioned documents related to transparent high-impact polystyrene, there are generally defects such as poor transparency, low toughness, hardness and rigidity of the...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Transparent impact-resistance polystyrene and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] (1) Prepare raw materials according to the following percentages by weight:

[0038] GPPS25%, K glue 69.1%, SMA0.5%, toughening agent 5%, lubricant 0.2%, coupling agent 0.1%, antioxidant 0.1%;

[0039] The GPPS is Chimei’s PG-383; the K glue is Zhonghe’s SL-803G; the SMA is SMA-700 from Shanghai Huawen Electronic New Material Co., Ltd.; the toughening agent is SBS produced by Yueyang Petrochemical -792; The lubricant is Clariant wax powder PE520; The coupling agent is a silane coupling agent; The antioxidant is BASF antioxidant 168;

[0040] (2) Mix GPPS, K glue and SMA in a high mixer, then add toughening agent, lubricant, coupling agent and antioxidant, and mix well;

[0041] (3) A twin-screw extruder is used for melt extrusion and granulation.

[0042] Through detection and calculation, the light transmittance of the transparent impact-resistant polystyrene of the present invention is 93.3%.

Embodiment 2

[0044] (1) Prepare raw materials according to the following percentages by weight:

[0045] GPPS32%, K glue 62%, SMA0.5%, toughening agent 5%, lubricant 0.2%, coupling agent 0.15%, antioxidant 0.15%;

[0046] The GPPS is GP5500 of Taihua; the K glue is KR-03 of Chevron; the SMA is SMA-700 of Shanghai Huawen Electronic New Material Co., Ltd.; the toughening agent is 3540 produced by Taiwan Li Changrong The lubricant is Clariant wax powder PE520; the coupling agent is a silane coupling agent; the antioxidant is BASF antioxidant 168;

[0047] (2) Mix GPPS, K glue and SMA in a high mixer, then add toughening agent, lubricant, coupling agent and antioxidant, and mix well;

[0048] (3) A twin-screw extruder is used for melt extrusion and granulation.

[0049] Through detection and calculation, the light transmittance of the transparent impact-resistant polystyrene of the present invention is 95.1%.

Embodiment 3

[0051] (1) Prepare raw materials according to the following percentages by weight:

[0052] GPPS36%, K glue 57%, SMA0.5%, toughening agent 6%, lubricant 0.25%, coupling agent 0.15%, antioxidant 0.1%;

[0053]The GPPS is GP150 of Kumho, Korea; the K glue is KR-05 of Chevron; the SMA is SMA-700 of Shanghai Huawen Electronic New Material Co., Ltd.; the toughening agent is Taiwan Rubber 6150; The lubricant is Honeywell6A wax; The coupling agent is a titanate coupling agent; The antioxidant is BASF antioxidant 1010;

[0054] (2) Mix GPPS, K glue and SMA in a high mixer, then add toughening agent, lubricant, coupling agent and antioxidant, and mix well;

[0055] (3) A twin-screw extruder is used for melt extrusion and granulation.

[0056] Through detection and calculation, the light transmittance of the transparent impact-resistant polystyrene of the present invention is 93.8%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a transparent impact-resistance polystyrene and a preparation method thereof, particularly a transparent high-impact-resistance polystyrene and a preparation method thereof. The polystyrene comprises the following components in percentage by weight: 25-40% of GPPS (general purpose polystyrene), 50-70% of K gum, 0.5-1% of SMA (styrene maleic anhydride), 5-10% of toughener, 0.2-0.5% of lubricant, 0.1-0.3% of coupling agent and 0.1-0.3% of antioxidant, totaling 100%. The preparation method comprises the following steps: proportionally and uniformly mixing the materials with a high-speed mixer, and extruding and granulating with a double screw extruder. The polystyrene has the advantages of high transparency, favorable product formability, favorable dimensional stability, high bending resistance and high tear resistance.

Description

technical field [0001] The invention relates to the field of thermoplastic materials, in particular to a polystyrene and a preparation method thereof, in particular to a transparent impact-resistant polystyrene and a preparation method thereof. Background technique [0002] Polystyrene (PS) is a resin polymerized from styrene (SM), which is mainly divided into general-purpose polystyrene (GPPS), high-impact polystyrene (HIPS) and expanded polystyrene (EPS). ), is one of the five general-purpose thermoplastic synthetic resins. [0003] General-purpose polystyrene (GPPS) resin is limited due to poor impact resistance and fragile products. Adding rubber to styrene monomer for free radical polymerization can produce chemically grafted high-impact polystyrene (HIPS). However, the opacity of HIPS due to the addition of rubber components makes it more demanding on transparency. High packaging areas are limited. Since the mid-1970s, foreign countries began to develop transparent ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L25/06C08L9/06C08L35/06C08L53/02
Inventor 王玉庭邹全亮
Owner DONGGUAN DECHENG PLASTIC TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap