Ceramsite recycled concrete as well as hollow block masonry and preparation method thereof

A technology of recycled concrete and ceramsite, which is applied in the field of building materials, can solve the problems of blank research on recycled concrete and few research on concrete, and achieve the effect of sustainable social development, resource saving and ecological environment protection.

Inactive Publication Date: 2014-11-19
GUANGXI UNIV
View PDF4 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The basic properties of recycled concrete and lightweight aggregate concrete have been studied at home and abroad, but there are few studies on concrete combined with lightweight aggregate and recycled aggregate, and the research on recycled concrete with ceramsite as light coarse aggregate Research is still blank

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramsite recycled concrete as well as hollow block masonry and preparation method thereof
  • Ceramsite recycled concrete as well as hollow block masonry and preparation method thereof
  • Ceramsite recycled concrete as well as hollow block masonry and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] 1.1 The ceramsite recycled concrete of the present invention is made up of the raw material of following weight parts (Kg):

[0033] Ceramsite 360, recycled fine aggregate 860, cement 400, water 200.

[0034] 1.2 The preparation method of ceramsite recycled concrete of the present invention:

[0035] (1) Soak the ceramsite and the regenerated fine aggregate in water for 1 hour, then remove and dry until there is no accumulated water on the surface for later use;

[0036] (2) Mix and stir the pre-wetted ceramsite and regenerated sand for 30 seconds, so that the regenerated sand can fill the voids of the ceramsite, then add cement and stir for 30 seconds, so that the cement is evenly distributed in the coarse and fine aggregates, and finally add water Stir for another 2 minutes to prepare ceramsite recycled concrete.

[0037] 1.3 The method of making hollow block masonry by using the ceramsite recycled concrete of this embodiment:

[0038] (1) For the second mold loadi...

Embodiment 2

[0044] 2.1 The ceramsite recycled concrete of the present invention is composed of the following raw materials in parts by weight (Kg):

[0045] Ceramsite 440, recycled fine aggregate 660, cement 520, water 150.

[0046] 2.2 The preparation method of ceramsite recycled concrete of the present invention:

[0047] (1) Soak the ceramsite and the regenerated fine aggregate in water for 1 hour, then remove and dry until there is no accumulated water on the surface for later use;

[0048] (2) Mix and stir the pre-wetted ceramsite and regenerated sand for 30 seconds, so that the regenerated sand can fill the voids of the ceramsite, then add cement and stir for 30 seconds, so that the cement is evenly distributed in the coarse and fine aggregates, and finally add water Stir for another 2 minutes to prepare ceramsite recycled concrete.

[0049] 2.3 The method of using the ceramsite recycled concrete of this embodiment to manufacture hollow block masonry:

[0050] (1) For the second mo...

Embodiment 3

[0056] 3.1 The ceramsite recycled concrete of the present invention is composed of the following raw materials in parts by weight (Kg):

[0057] Ceramsite 402, recycled fine aggregate 760, cement 400, water 180.

[0058] 3.2 The preparation method of ceramsite recycled concrete of the present invention:

[0059] (1) Soak the ceramsite and the regenerated fine aggregate in water for 1 hour, then remove and dry until there is no accumulated water on the surface for later use;

[0060] (2) Mix and stir the pre-wetted ceramsite and regenerated sand for 30 seconds, so that the regenerated sand can fill the voids of the ceramsite, then add cement and stir for 30 seconds, so that the cement is evenly distributed in the coarse and fine aggregates, and finally add water Stir for another 2 minutes to prepare ceramsite recycled concrete.

[0061] 3.3 The method of using the ceramsite recycled concrete of this embodiment to manufacture hollow block masonry:

[0062] (1) For the second ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses ceramsite recycled concrete, a hollow block masonry and a preparation method of the hollow block masonry. The ceramsite recycled concrete consists of the following raw materials in parts by weight: 360-440 parts of ceramsite, 660-860 parts of a recycled fine aggregate, 400-520 parts of cement and 150-200 parts of water. The ceramsite recycled concrete disclosed by the invention adopts the ceramsite as a light-weight coarse aggregate, adopts waste concrete as the recycled fine aggregate, integrates the characteristics of a lightweight aggregate and recycled aggregate concrete, and ensures that the ceramsite recycled concrete has the advantages of energy conservation, waste utilization, environmental protection, light weight, heat preservation, heat insulation and the like. A hollow block manufactured by adopting the ceramsite recycled concrete disclosed by the invention is a green wall material which has the performances of light weight, environmental protection, heat preservation and heat insulation, and has good physical, mechanical and thermotechnical performances.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a ceramsite recycled concrete and hollow block masonry and a preparation method. Background technique [0002] With the rapid development of my country's construction industry, the problem of resource shortage is becoming more and more serious. High-quality natural aggregates have been exhausted in some areas. Large-scale quarrying and large-scale discarding of construction waste have seriously damaged the natural landscape and ecological environment. , deviated from the sustainable development strategy of my country's economy and environment. Therefore, from the perspective of recycling construction waste, saving natural resources and promoting ecological environment coordination, it will be of great practical significance to study and utilize waste concrete. Aggregate made of waste concrete after cleaning, crushing, grading and mixing in a certain proportion is calle...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B18/16
CPCY02W30/91
Inventor 邓志恒王金燕杨海峰王文杰唐光暹
Owner GUANGXI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap