Anti-static PVC sole material and manufacturing method thereof

A sole material and antistatic technology, which is applied in the field of sole materials, can solve the problem that antistatic shoes cannot be applied, and achieve the effect of preventing the sole from becoming soft and improving the antistatic performance.

Inactive Publication Date: 2014-12-24
SUZHOU JINGRO TECH
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Anti-static shoes use PU or PVC material to make soles, and ordinary PVC sole materials cannot be used for anti-static shoes

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-static PVC sole material and manufacturing method thereof
  • Anti-static PVC sole material and manufacturing method thereof
  • Anti-static PVC sole material and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A kind of antistatic PVC sole material, its parts by weight consist of:

[0026]

[0027] Its manufacturing method comprises the following steps:

[0028] (1) drying: select the quaternary ammonium salt type cationic surfactant according to the formula, and dry it;

[0029] (2) Mixing: According to the formula, the dried quaternary ammonium salt type cationic surfactant and other components in the formula are mixed to obtain a uniformly mixed material;

[0030] (3) extrude: the material that step (2) obtains is added extruder, extrudes and obtains antistatic PVC grain;

[0031] (4) Injection molding: the antistatic PVC pellet obtained in step (3) is added to an injection molding machine, and injection molding is performed to obtain an antistatic PVC sole material.

Embodiment 2

[0033] A kind of antistatic PVC sole material, its parts by weight consist of:

[0034]

[0035] Its manufacturing method comprises the following steps:

[0036] (1) drying: select the quaternary ammonium salt type cationic surfactant according to the formula, and dry it;

[0037] (2) Mixing: According to the formula, the dried quaternary ammonium salt type cationic surfactant and other components in the formula are mixed to obtain a uniformly mixed material;

[0038] (3) extrude: the material that step (2) obtains is added extruder, extrudes and obtains antistatic PVC grain;

[0039] (4) Injection molding: the antistatic PVC pellet obtained in step (3) is added to an injection molding machine, and injection molding is performed to obtain an antistatic PVC sole material.

Embodiment 3

[0041] A kind of antistatic PVC sole material, its parts by weight consist of:

[0042]

[0043]

[0044] Its manufacturing method comprises the following steps:

[0045] (1) drying: select the quaternary ammonium salt type cationic surfactant according to the formula, and dry it;

[0046] (2) Mixing: According to the formula, the dried quaternary ammonium salt type cationic surfactant and other components in the formula are mixed to obtain a uniformly mixed material;

[0047] (3) extrude: the material that step (2) obtains is added extruder, extrudes and obtains antistatic PVC grain;

[0048] (4) Injection molding: the antistatic PVC pellet obtained in step (3) is added to an injection molding machine, and injection molding is performed to obtain an antistatic PVC sole material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an anti-static PVC sole material, and the anti-static PVC sole material comprises the components in parts by weight as follows; 55-65 parts of PVC, 3-5 parts of quaternary ammonium salt cationic surface active agent, 1-3 parts of carbon fiber powder, 20-30 parts of plasticizer, 2-5 parts of foaming agent, 3-8 parts of white carbon black and 5-10 parts of filler. The manufacturing method for anti-static PVC sole material is also provided. The anti-static PVC sole material has good anti-static performance applied to the anti-static shoes.

Description

Technical field: [0001] The invention relates to a shoe sole material, in particular to an antistatic PVC shoe sole material and a manufacturing method thereof. Background technique: [0002] Anti-static shoes are the production workshops of the microelectronics industry such as Electronic semiconductor devices, The electronic computer, Electronic communication equipment and integrated circuits A kind of work shoes worn by advanced laboratories to reduce or eliminate electrostatic hazards. Anti-static shoes can guide static electricity from the human body to the ground, thereby eliminating static electricity on the human body, and at the same time effectively suppress the dust generated by people walking in the clean room. They are suitable for clean workshops and laboratories in pharmaceutical factories, food factories, and electronics factories. Wait. Anti-static shoes use PU or PVC material to make soles, and ordinary PVC sole materials cannot be used for anti-static sh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08K13/04C08K7/06C08K3/04C08K3/36C08K3/30C08K3/34C08J9/10A43B13/04
Inventor 黄超
Owner SUZHOU JINGRO TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com