High-adhesion powder coating

A powder coating, high adhesion technology, applied in the direction of powder coating, polyester coating, epoxy resin coating, etc., can solve the problems of coating film adhesion not meeting the requirements, coating cracking, coating peeling, etc., to achieve production cost Low, high-efficiency adhesion, strong scratch resistance effect

Inactive Publication Date: 2014-12-24
JIANGSU CHANGSONG SCI & TECH DEV
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] General powder coatings are a compromise of various properties. For some applications that require punching after the coating film is baked and formed, the adhesion of the coating film cannot meet the requirements, which often leads to cracking of the coating at the edge of the hole after punching. , and even peeling of the coating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] A kind of high adhesion powder coating, it is made up of following components, and the parts by weight of each component are:

[0022] Outdoor polyester resin 560-620 parts

[0023] Curing agent TGIC 42-45 parts

[0024] Universal leveling agent 8-10 parts

[0025] Benzoin 3 parts

[0026] Curing accelerator 5-10 parts

[0027] Micropowder wax 3-5 parts

[0028] Auxiliary dispersant 5-10 parts

[0029] 20-50 parts of epoxy resin

[0030] Pigment 5-250 parts

[0031] Filling 80-350 parts,

[0032] The outdoor type polyester resin is a low molecular weight polyester resin, the curing agent is TEPIC from Japan, the curing accelerator is Cytec CC964, the auxiliary dispersant is B30H, the epoxy resin is E-12, and the pigments are selected according to the color It needs to be prepared, and the filler is precipitated barium sulfate;

[0033] The manufacturing process is batching-mixing-extrusion-grinding into powder, an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a powder coating, and in particular relates to a high-adhesion powder coating which comprises the following components in parts by weight: 560-620 parts of outdoor polyester resin, 42-45 parts of a curing agent TGIC, 8-10 parts of a universal leveling agent, 3 parts of benzoin, 5-10 parts of a curing accelerant, 3-5 parts of micro powder wax, 5-10 parts of a dispersing agent aid, 20-50 parts of epoxy resin, 5-250 parts of pigment and 80-350 parts of packing. The power coating provided by the invention is simple in formula, low in production cost, high in adhesion and relatively high in scraping resistance.

Description

technical field [0001] The invention relates to a powder coating, in particular to a high adhesion powder coating. Background technique [0002] General powder coatings are a compromise of various properties. For some applications that require punching after the coating film is baked and formed, the adhesion of the coating film cannot meet the requirements, which often leads to cracking of the coating at the edge of the hole after punching. , and even peeling of the coating. Contents of the invention [0003] In view of the above defects, the object of the present invention is to provide a kind of high adhesion powder coating with simple process formula, strong coating adhesion and relatively scratch resistance. [0004] The technical scheme that the present invention adopts for this reason is: [0005] A kind of high adhesion powder coating, it is made up of following components, and the parts by weight of each component are: [0006] Outdoor polyester resin 560-620 pa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/00C09D163/00C09D5/03
Inventor 张磊
Owner JIANGSU CHANGSONG SCI & TECH DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com