Wood formwork restoration agent and its preparation and use method

A repairing agent and wood formwork technology, applied in lignin coatings, coatings, epoxy resin coatings, etc., can solve problems such as accelerated formwork damage, and achieve the effects of small shrinkage, good brightness, and flat surface without unevenness

Inactive Publication Date: 2017-01-04
广西林安木业有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When there is a small amount of damage on the surface of the formwork and there is no suitable repair agent for repair, water will easily enter the formwork from here, further accelerating the damage of the formwork

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The composition and weight of the wooden template restoration agent provided by the present embodiment are as follows:

[0023] Epoxy resin 0.18kg, acetone 0.15kg, lignin 0.3kg,

[0024] Wood carbon powder 0.3kg, quartz powder 0.05kg, pigment 0.02kg.

[0025] The preparation method is as follows:

[0026] A, add the acetone of 0.15kg in the epoxy resin of 0.18kg, stir;

[0027] B, get lignin and charcoal and carry out rolling, cross 180 mesh screens, get the lignin of 0.3kg and the charcoal powder of 0.3kg and add above-mentioned mixture;

[0028] C. Stir after adding 0.05kg of quartz powder and 0.02kg of pigment corresponding to the color of the template.

[0029] How to use: Clean up the parts that need to be repaired, take an appropriate amount of repairing agent, add 2.5kg of polyamide, stir evenly, fill to the parts that need to be repaired, and remove the excess repairing agent on the repaired part.

Embodiment 2

[0031] The composition and weight of the wooden template restoration agent provided by the present embodiment are as follows:

[0032] Epoxy resin 0.6kg, acetone 0.24kg, lignin 0.54kg,

[0033] Wood carbon powder 0.52kg, quartz powder 0.06kg, pigment 0.04kg.

[0034] The preparation method is as follows:

[0035] A, add the acetone of 0.24kg in the epoxy resin of 0.6kg, stir;

[0036] B, get lignin and charcoal and carry out rolling, cross 180 mesh screens, get the lignin of 0.54kg and the charcoal powder of 0.52kg and add above-mentioned mixture;

[0037] C. Stir after adding 0.06kg of quartz powder and 0.04kg of pigment corresponding to the color of the template.

[0038] How to use: Clean up the part that needs to be repaired, take an appropriate amount of repair agent, add polyamide with a weight of 2kg, stir evenly, fill it to the part that needs to be repaired, and remove the excess repair agent on the repaired part.

Embodiment 3

[0040] The composition and weight of the wooden template restoration agent provided by the present embodiment are as follows:

[0041] Epoxy resin 1.41kg, absolute ethanol 0.3kg, lignin 0.6kg,

[0042] Wood carbon powder 0.6kg, quartz powder 0.06kg, pigment 0.03kg.

[0043] The preparation method is as follows:

[0044] A, in the epoxy resin of 1.41kg, add the dehydrated alcohol of 0.3kg, stir;

[0045] B, get lignin and charcoal and carry out rolling, cross 180 mesh screens, get the lignin of 0.6kg and the charcoal powder of 0.6kg and add above-mentioned mixture;

[0046] C. Stir after adding 0.06kg of quartz powder and 0.03kg of pigment corresponding to the color of the template.

[0047] How to use: Clean up the parts that need to be repaired, take an appropriate amount of repair agent, add polyamide with a weight of 3kg, stir evenly, fill it to the parts that need to be repaired, and remove the excess repair agent on the repaired part.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention aims to provide a wood template restoration agent, its composition and weight percentage are as follows: epoxy resin 18%-47%, diluent 10%-15%, lignin 20%-30%, wood carbon powder 20%- 30%, quartz powder 2%‑5%, pigment 1%‑2%. Also provide the preparation method of the repairing agent: A, adding 10-15% diluent by weight into epoxy resin with 18%-47% by weight, stirring; B, taking lignin and charcoal for grinding Pressing, screening, getting the lignin of 20%-30% by weight and wood charcoal powder of 20%-30% by weight to add the above-mentioned mixture; C, adding the quartz powder and the weight percentage of 2%-5% Stir after adding 1%‑2% pigment. The invention also provides a method for using the restoration agent. The wood formwork restoration agent provided by the invention has strong adhesion and good gluing performance, and can effectively repair formwork wounds.

Description

technical field [0001] The invention relates to the field of wood treatment, in particular to a wood template restoration agent and its preparation and use methods. Background technique [0002] At present, high-end buildings, bridges, viaducts, tunnels, and culverts need to use film-coated panels with clear water film on the surface. The surface of clear-water film-coated panels is smooth and flat, and the concrete surface does not need to be scraped and trimmed again; but The film-coated board is made of wood, and the environment of the construction site is relatively poor. It is inevitable that the film-coated board will be damaged by being smashed, bumped, or scratched. Once the fair-faced formwork is damaged, it cannot be used as a formwork for fair-faced concrete, but can only be used as a general formwork, and the price of the clear-water film-coated board is about 35% higher than that of a general formwork, which causes unnecessary waste. [0003] In addition, other...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D163/00C09D197/00C09D7/12
Inventor 林东平谭钢张志伟赵志华郑小颂杨清华秦志东黄德智韦春秀
Owner 广西林安木业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com