UV-radiation-resistant water-based paint for glass sliding doors and preparation method thereof

A water-based paint, glass sliding door technology, applied in anti-fouling/underwater paint, epoxy resin paint, coating and other directions, can solve the problems of cell membrane and gene influence, large damage to skin and objects, reduced skin elasticity, etc. The effect of reducing aging, good decoration and not easy to peel off

Inactive Publication Date: 2015-02-11
凤阳徽亨商贸有限公司
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since UV-A has a longer wavelength in ultraviolet rays, UV-A is easier to pass through clouds and glass, and it is more harmful to skin and objects. Although UV-A penetrates the skin less deeply than UV-B, UV-A B scatters on the skin surface and is absorbed by the skin to make the skin tan easily, while UV-A can penetrate into the subcutaneous tissue layer and generate free radicals in the skin tissue. The generated free radicals cause skin aging and wrinkles, and make the skin elastic reduce
In addition, some effects on cell membranes and genes

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] Specific implementation plan

[0016] The following is a detailed explanation of the present invention through specific instances.

[0017] A water -proof glass door -proofing glass door water -based coating, which is prepared by the following weights (kg) raw materials: water -based epoxy resin emulsion 56, water -based amino resin 15, epoxy soluble germine 1. Removal water 15, 15, 15, 15, 15, 15, 15, 15, 15.Polyol monoclonetl ether 2, alcohol -titanium titanium titanate 0.4, modified pure propyle emulsion 10, polyether modified polycotic siliconane 0.3, hydroxyetoin cellulose 0.6, polyoxy acrylic gly gly ether 0.4, amino triathina, ammonia base triteriorAyoxyxane 0.4, dihydramine, ethanol 3, polyethylene wax emulsion 1, zinc acid zinc, titanium white powder 0.6, benzalzazole 0.8, carbon black 0.5, pigment 2;

[0018] The modified pure propylene emulsion is made of raw materials of the following weight (kilograms): nano -titanium dioxide 5, nano -silica dioxide 2, nanoccal...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a UV-radiation-resistant water-based paint for glass sliding doors. The invention is characterized in that the water-based paint is prepared from the following raw materials in parts by weight: 50-58 parts of water-based epoxy resin emulsion, 13-17 parts of water-based amino resin, 1-2 parts of epoxy octyl stearate, 10-15 parts of deionized water, 1-2 parts of propanediol monobutyl ether, 0.3-0.6 part of alkylol amine fatty acid titanate, 7-10 parts of modified pure acrylic emulsion, 0.2-0.5 part of polyether modified polyorganosiloxane, 0.4-0.7 part of hydroxyethyl cellulose, 0.2-0.4 part of polyoxypropylene glycerol ether, 0.3-0.5 part of aminopropyl trimethoxy silane, 2-3 parts of dimethylethanolamine, 1-2 parts of polyethylene wax emulsion, 0.3-0.5 part of zinc stearate, 0.4-0.8 part of titanium white, 0.5-1.0 part of benzotriazole, 0.3-0.7 part of carbon black and 2-4 parts of pigment. The film of the water-based glass paint has the advantages of high hardness, high smoothness, favorable decoration property and low peeling tendency; the added modified pure acrylic emulsion has the characteristics of excellent dirt resistance, excellent bactericidal property, excellent scrub resistance, excellent weather resistance and the like; and the added carbon black and benzotriazole effectively absorb the ultraviolet rays, reduce the aging action of the ultraviolet rays on the paint film and furniture, and lower the injury to the human body.

Description

Technical field [0001] The present invention involves a coating and preparation method, especially a glass -moving water -migraphic coatings and preparation methods for anti -UV radiation. Background technique [0002] With the continuous improvement of people's living standards, the pursuit of beauty is also stronger. Colorful glass coatings meet the market demand with their unique and colorful decorative effects.Perfume bottles, lighting glass, art glass and other daily glass products make it colorful.The energy of ultraviolet rays can cause skin aging and even easily lead to skin cancer, and can also cause the fading of various curtains and floors, plastics and printed materials.The wavelength range that irradiated on the ground was 290-400nm ultraviolet rays accounted for about 6 % of the total energy of the solar, of which the 290-320nm short-wavelength UV-B range accounted for about 0.5 %, which belongs to the wavelength range of 320-400NMUV-Avoa.5.5 %.Therefore, UV-A accou...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D163/00C09D161/20C09D151/10C09D5/16C09D7/12C08F292/00C08F220/14C08F220/18
CPCC08F220/14C08K2201/011C08K2201/014C08L2201/08C08L2205/035C09D5/1637C09D7/61C09D7/62C09D7/63C09D7/65C09D163/00C08L61/20C08L33/12C08L83/12C08L1/284C08L71/02C08L23/06C08K13/06C08K9/06C08K9/04C08K2003/2241C08K3/36C08K2003/265C08K3/04C08K5/3475C08F220/1804C08F220/06
Inventor 张波
Owner 凤阳徽亨商贸有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products