Antistatic PP/ABS composite material and preparation method thereof
A composite material and antistatic technology, applied in the field of preparation of PP/ABS composite materials, can solve the problems of large filling amount, glossiness, shrinkage rate is not considered, glossiness mechanical properties are not considered, etc., to achieve good compatibility, Effect of high gloss improvement, enhanced antistatic properties
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0036] 100 parts of polypropylene, 50 parts of acrylonitrile-butadiene-styrene copolymer, 6 oleic acid polyethylene glycol ester, 2 parts of sodium polyacrylate, 10 parts of polypropylene grafted maleic anhydride, 20 parts of glass fiber, 2 parts 1 part of antioxidant 1010, 1 part of vinyl bisstearamide, 1 part of 3-aminopropyltriethoxysilane, 0.5 part of ethylene-octene copolymer were added to a high-speed mixer and mixed for 5 minutes at a mixing speed of 120 RPM, mixing temperature is 40°C; then put the mixed material into the extruder for melt extrusion, stranding, cooling, pelletizing, and packaging. The temperature of the extruder is 180°C-225°C from the feeding section to the machine head.
Embodiment 2
[0038] 100 parts of polypropylene, 100 parts of acrylonitrile-butadiene-styrene copolymer, 20 parts of polyethylene glycol oleate, 8 parts of sodium polyacrylate, 10 parts of acrylonitrile-butadiene-styrene copolymer grafted horse Add acid anhydride, 50 parts of talc powder, 1 part of antioxidant 1010, 1 part of antioxidant 168, 0.5 parts of 3-aminopropyltriethoxysilane, and 10 parts of ethylene-octene copolymer into the high-speed mixer in sequence Mix in medium for 10 minutes, the mixing speed is 200 rpm, and the mixing temperature is 60°C; then the mixed material is put into the extruder for melt extrusion, drawing, cooling, pelletizing, and packaging. The temperature of the extruder is 180°C, 200°C, 200°C, 210°C, 210°C, 220°C, 220°C, 220°C, 220°C, 225°C from the feeding section to the machine head, the screw diameter is 75mm, and the screw length The diameter ratio is 50:1.
Embodiment 3
[0040] 100 parts of polypropylene, 80 parts of acrylonitrile-butadiene-styrene copolymer, 16 parts of polyethylene glycol oleate, 4 parts of sodium polyacrylate, 4 parts of polypropylene grafted maleic anhydride, 4 parts of acrylonitrile-butylene Diene-styrene copolymer grafted maleic anhydride, 20 parts of glass fiber, 10 parts of talc, 0.5 part of antioxidant 1010, 0.5 part of antioxidant 168, 0.5 part of antioxidant 1076, 0.1 part of vinyl double hard Fatty amide and 30 parts of ethylene-octene copolymer were sequentially added to a high-speed mixer and mixed for 12 minutes, the mixing speed was 160 rpm, and the mixing temperature was 55°C; then the mixed material was added to the extruder for melt extrusion , Stranding, cooling, dicing, packing. The temperature of the extruder is 180°C, 200°C, 200°C, 210°C, 210°C, 220°C, 220°C, 220°C, 220°C, 225°C from the feeding section to the machine head, the screw diameter is 50mm, and the screw length The diameter ratio is 35:1.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap