Environmentally-friendly high-flame-retardant composite material used for air-conditioned bus tube wall

A composite material and high flame retardant technology, which is applied in the field of environment-friendly and high-flame-retardant vehicle roof composite materials and their preparation, can solve the problems of human health hazards, unenvironmental sources, etc., to ensure safety, high flame retardant performance, and not easy to deform. sexual effect

Inactive Publication Date: 2015-03-11
YANGZHONG TIANZHENG SYNTHETIC MATERIAL RES CENT
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Moreover, the sources of raw materials for many car interiors are not environmentally friendly, and some toxic and harmful substances are often volatilized. People will inhale these toxic and harmful substances in the car, which will cause greater harm to human health in the long run.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The following components are reacted to prepare the combined material, in parts by mass:

[0031] Polyether polyol 1 35 parts

[0032] Polyether polyol 2 10 parts

[0033] Polyether polyol 3 10 parts

[0034] Polyester polyol 1 10 parts

[0035] Polyester polyol 2 10 parts

[0036] Polyurethane silicone oil 3 parts

[0037] Catalyst DY828 1.8 parts

[0038] Catalyst A33 1.5 parts

[0039] 2.2 parts of water

[0040] Flame retardant DMMP 35 parts.

[0041] Put it into the reaction kettle for mixing reaction, the stirring speed is 180r / min, and the stirring time is 3h, and the composite material can be obtained; then the composite material and isocyanate are mixed evenly according to the mass ratio of 1.6:1, and the composite material of the present invention can be obtained .

Embodiment 2

[0043] The following components are reacted to prepare the combined material, in parts by mass:

[0044] Polyether polyol 1 38 parts

[0045] Polyether polyol 2 15 parts

[0046] Polyether polyol 3 16 parts

[0047] Polyester polyol 1 16 parts

[0048] Polyester polyol 2 15 parts

[0049] Polyurethane silicone oil 3.1 parts

[0050] Catalyst DY828 1.8 parts

[0051] Catalyst A33 1.5 parts

[0052] 2.57 parts of water

[0053] Flame retardant DMMP 38 parts.

[0054] Add it into the reaction kettle for mixed reaction, the stirring speed is 190r / min, and the stirring time is 4h, and then the combined material can be obtained; then the combined material and isocyanate MR100 are mixed evenly according to the mass ratio of 1.6:1, and the composite compound of the present invention can be obtained. Material.

Embodiment 3

[0056] The following components are reacted to prepare the combined material, in parts by mass:

[0057] Polyether polyol 1 35 parts

[0058] Polyether polyol 2 15 parts

[0059] Polyether polyol 3 20 parts

[0060] Polyester polyol 1 15 parts

[0061] Polyester polyol 2 10 parts

[0062] Polyurethane silicone oil 3 parts

[0063] Catalyst DY828 2.7 parts

[0064] Catalyst A33 1.8 parts

[0065] 2.8 parts of water

[0066] Flame retardant DMMP 40 parts.

[0067] Put it into the reaction kettle for mixed reaction, the stirring speed is 110r / min, and the stirring time is 8h, and then the combined material can be obtained; then the combined material and isocyanate MR300 are mixed evenly according to the mass ratio of 1.8:1, and the composite compound of the present invention can be obtained. Material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environmentally-friendly high-flame-retardant composite material used for an air-conditioned bus tube wall, the composite material comprises a combined material and isocyanate, the mass ratio of the combined material: isocyanate is 1.6: 1, the composite material has high flame retardant properties, and is not easy to burn when meeting a fire, thus ensuring the safety of the whole vehicle and the safety of passengers, the composite material has the advantages of deformation resistance, even if the composite material is used for a long term, the composite material may not deform, and raw materials used in the composite material are environmentally friendly, so that no substances toxic and harmful to the human body may be released.

Description

technical field [0001] The invention relates to a composite material and a preparation method thereof, in particular to an environment-friendly high flame-retardant vehicle roof composite material and a preparation method thereof. Background technique [0002] The pipe walls of air-conditioned vehicles in the prior art are usually plastic products, but plastic products usually have poor flame retardancy, and are prone to fires in the event of failures or accidents, thereby causing serious loss of life and property. During the transportation of automobiles, due to electrical short circuit, engine failure, traffic accidents and other reasons, it is very easy to cause fire, resulting in property loss and casualties. And flammable car interior decorations tend to aggravate the degree of fire in accidents. Moreover, the sources of raw materials for many car interiors are not environmentally friendly, and some toxic and harmful substances are often volatilized. People will inhale...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G18/48C08G18/42C08K5/521
CPCC08G18/4018C08G18/4202C08G18/4804C08K5/521C08G2110/0083
Inventor 朱章弟纪新根
Owner YANGZHONG TIANZHENG SYNTHETIC MATERIAL RES CENT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com