Self-lubricating rubber bushing and preparation method thereof

A rubber bushing, self-lubricating technology, applied in other household appliances, applications, household appliances, etc., can solve the problems of low temperature resistance of rubber materials, inability to give high radial stiffness to inner and outer double-barrel bushings, etc. High radial stiffness, good elasticity and wear resistance, good use effect

Inactive Publication Date: 2015-03-25
TENNECO SUZHOU CO LTD
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the existing vulcanized bushes of conventional rubber materials have the following disadvantages: 1) when the rubber is at low temperature, the dynamic elastic coefficient will rise sharply, so the low temperature resistance of the rubber material is low; 2) the existing bushes are not used To the self-lubricating rubber, that is, the existing rubber material cannot give the inner and outer double-tube type bushes high radial stiffness and zero torsional stiffness

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A self-lubricating rubber bushing, the self-lubricating rubber bushing formula includes the following weight: natural rubber SIR20, 1.2kg, butadiene rubber BUNACB22, 1kg, zinc oxide 0.08kg, stearic acid SA, 0.2kg, antioxidant RD , 0.06kg, carbon black N550, 1.2kg, naphthenic oil Nytex820, 0.08kg, oleic acid amide KEMAMIDEU, 0.2kg, ultra-high molecular weight polyethylene XM220, 0.24kg, paraffin Antilux 654, 0.08kg, accelerator CBS, 0.02kg , sulfur S200-1, 0.02kg.

[0020] The natural rubber SIR20 originates from Indonesia, the butadiene rubber BUNACB22 is produced by Lanxess Rubber Company of Germany, the zinc oxide is produced by Jinhua Zinc Oxide Factory in Hanshan County, Anhui Province, and the stearic acid SA is PT.MUSIM Produced by MAS, the anti-aging agent RD is produced by Shandong Sunnic Chemical Technology Co., Ltd., the carbon black N550 is produced by Cabot Company, the naphthenic oil Nytex820 is produced by Chemtura Corporation of the United States, and the...

Embodiment 2

[0033] A self-lubricating rubber bushing, the self-lubricating rubber bushing formula includes the following weight: natural rubber SIR20, 1.1kg, butadiene rubber BUNACB22, 1.1kg, zinc oxide 0.08kg, stearic acid SA, 0.2kg, anti-aging agent RD, 0.06kg, carbon black N550, 1.2kg, naphthenic oil Nytex820, 0.08kg, oleic acid amide KEMAMIDE U, 0.2kg, ultra-high molecular weight polyethylene XM220, 0.24kg, paraffin Antilux 654, 0.08kg, accelerator CBS, 0.02kg, Sulfur S200-1, 0.02kg.

[0034] The preparation method is the same as in Example 1.

Embodiment 3

[0036] A self-lubricating rubber bushing, the self-lubricating rubber bushing formula includes the following weight: natural rubber SIR20, 1.2kg, butadiene rubber BUNACB22, 1kg, zinc oxide 0.08kg, stearic acid SA, 0.2kg, antioxidant RD , 0.06kg, carbon black N550, 1.1kg, naphthenic oil Nytex820, 0.1kg, oleic acid amide KEMAMIDEU, 0.3kg, ultra-high molecular weight polyethylene XM220, 0.25kg, paraffin Antilux 654, 0.08kg, accelerator CBS, 0.02kg , sulfur S200-1, 0.02kg.

[0037] The preparation method is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a self-lubricating rubber bushing and a preparation method thereof and particularly relates to a self-lubricating rubber bushing for an automobile and a preparation method of the self-lubricating rubber bushing. The self-lubricating rubber bushing comprises natural rubber SIR20, butadiene rubber BUNACB22, zinc oxide, stearic acid SA, an anti-aging agent RD, carbon black N550, naphthenic oil Nytex820, oleamide KEMAMIDEU, ultra-high molecular weight polyethylene XM220, paraffin Antilux654, an accelerant CBS and sulphur S200-1. The rubber bushing disclosed by the invention has high radial rigidity and approximately-zero torsional rigidity so as to be suitable for a special service condition with large torsional angle for a long term; and if being used for a long term, the bushing is low in abrasion and long in service life and can still be favorably used under a low-temperature condition.

Description

technical field [0001] The invention relates to a self-lubricating rubber bush and a preparation method thereof, in particular to a self-lubricating rubber bush for automobiles and a preparation method thereof. Background technique [0002] In the suspension guide mechanism of modern automobiles, such as swing arms, rear axles, etc., more and more hinge points connected to the body are connected by rubber bushings. With its good vibration isolation performance, elastic characteristics and attenuation characteristics, rubber bushings have become an indispensable and important component in automobiles. The characteristics of the bushing after vulcanization of the existing conventional rubber material: 1) The shape of the rubber part has more freedom to choose, and can provide stiffness in three directions (axial, radial, torsional); 2) It can be vulcanized firmly with the metal Together, the structure of fixing and supporting is simplified. Therefore, any direction in the th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L9/00C08L23/06C08K13/02C08K5/20C08K3/22C08K5/09C08K3/04C08K5/01C08K3/06
CPCC08L7/00B29B7/005B29D22/00C08L9/00C08L2205/02C08L2205/035C08L2207/068C08L91/00C08L23/06C08L91/06C08K13/02C08K2003/2296C08K5/09C08K3/04C08K5/20C08K3/06
Inventor 姜文华
Owner TENNECO SUZHOU CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com