Preparation method of polyester blanket

A technology for polyester and blankets, applied in the processing of textile materials, heating/cooling fabrics, printing, etc., can solve the problems of large floor space and achieve the effect of small floor space, low cost, puffed uniform gloss

Active Publication Date: 2016-08-24
连云港飞雁毛毯有限责任公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Its disadvantage is that it occupies a large area
A high temperature setting machine needs 4-5 people to operate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Embodiment 1, a kind of puffing method of polyester blanket, the puffing operation adopts electric heating stainless steel puffing heat roll, the surface of the stainless steel puffing heat roll body is provided with grooves, the suede surface of the polyester gray cloth is in direct contact with the surface of the puffing heat roll body, and the surface of the puffing heat roll body of the polyester gray cloth The cloth running direction is the same as the rotating direction of the puffing hot roller; during puffing operation, the surface temperature of the puffing hot roller is 120°C, the speed is 200 rpm, and the cloth running speed of the polyester gray cloth is 20 m / min.

Embodiment 2

[0033] Embodiment 2, a kind of puffing method of polyester blanket, puffing operation adopts electric heating stainless steel puffing heat roll, the surface of stainless steel puffing heat roll body is provided with groove, polyester gray fabric suede and puffing heat roll body surface contact directly, and polyester gray cloth The cloth running direction is the same as the rotating direction of the puffing hot roll; during puffing operation, the surface temperature of the puffing hot roll is 210°C, the speed is 400 rpm, and the running speed of the polyester gray cloth is 15m / min.

Embodiment 3

[0034] Embodiment 3, a kind of puffing method of polyester blanket, the puffing operation adopts electric heating stainless steel puffing heat roll, the surface of stainless steel puffing heat roll body is provided with groove, the suede surface of polyester gray cloth is directly contacted with the surface of puffing heat roll body, and the polyester gray cloth The cloth running direction is the same as the rotating direction of the puffing hot roller; during the puffing operation, the surface temperature of the puffing hot roller is 180°C, the rotating speed is 300 rpm, and the cloth running speed of the polyester gray cloth is 18 m / min.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
widthaaaaaaaaaa
Login to View More

Abstract

The invention provides a swelling method of a polyester blanket. An electrothermal stainless steel swelling hot roller is adopted for swelling operation. A groove is formed in the surface of the stainless steel swelling hot roller, polyester greige cloth suede makes direct contact with the surface of the stainless steel swelling hot roller, and the cloth moving direction of greige cloth is the same as the rotation direction of the swelling hot roller. During swelling operation, the surface temperature of the swelling hot roller ranges from 120 DEG C to 210 DEG C, the rotation speed is 200-400 turns per minute, and the cloth moving speed of the greige cloth is 15-20 m / min. The invention further relates to a manufacturing method of the polyester blanket using the swelling method. The manufacturing method sequentially comprises the steps of weaving and cutting, swelling, brushing, lustring and printing, permeating, drying, steaming and washing, shaping, drying, after treatment and obtaining of the product. Polyester low-elastic yarn is swelled, and the functions of warm keeping and increasing the thickness of the blanket are achieved. The manufactured method is simple, low in equipment manufacturing cost, small in occupied area and good in swelling effect.

Description

technical field [0001] The invention relates to an expanding method for a polyester blanket, and also relates to a preparation method for a polyester blanket using the expanding method. Background technique [0002] Raschel polyester blanket is a gray fabric woven by a rasher warp knitting machine with polyester low elastic yarn as a face yarn. After the gray fabric is cut by a cutting machine, it is puffed and shrunk by a high-temperature setting machine, and then brushed, ironed, printed, and steamed. It is processed by steaming, washing, drying and shaping, finishing, wrapping and packaging. The wool height of Raschel blanket is usually 6MM-12MM, and it is divided into upper yarn and lower yarn when weaving. The upper yarn is usually polyester low elastic yarn, also known as DTY, which has 5%-8% elasticity. Low yarn is generally made of polyester full-drawn yarn, also known as FDY, with almost zero elasticity. The thermal expansion and shrinkage process in the current p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06C7/02D04B21/04D06C11/00D06C15/00D06B3/18B41M1/26B41M1/12
CPCD04B21/04D06B3/18D06C7/02D06C11/00D06C15/00
Inventor 范保勇冯扬陈厚虎赵霞
Owner 连云港飞雁毛毯有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products