A cleaning agent and anti-fogging technology, applied in the field of cleaning agents and glass anti-fogging cleaners, can solve the problems of affecting vision and sight, easy fogging of glass, etc., and achieve the effect of fast drying, long anti-fogging effect and effective cleaning
Inactive Publication Date: 2015-04-01
CHENGDU SHUNFA DISINFECTANT & WASHING TECH
View PDF3 Cites 4 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] Although the glass cleaner composition in the above-mentioned patent can clean the glass, it will make the glass easy to fog after cleaning, affecting the field of view and line of sight
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0028] A glass anti-fog cleaner, comprising the following raw materials in parts by weight:
[0029] Sorbitan Monolaurate 10 parts
[0030] Orthophosphoric acid 15 parts
[0031] 9 parts zinc chromate
[0032] Sulfated castor oil 5 parts
[0033] Sodium polypropoxybutyl ether sulfate 5 parts
[0034] Quick-drying agent 2 parts
[0035] 60 parts of water.
Embodiment 2
[0037] A glass anti-fog cleaner, comprising the following raw materials in parts by weight:
[0038] Sorbitan Monolaurate 30 parts
[0039] Orthophosphoric acid 25 parts
[0040] 18 parts zinc chromate
[0041] Sulfated castor oil 18 parts
[0042] Sodium polypropoxybutyl ether sulfate 18 parts
[0043] Quick-drying agent 12 parts
[0044] 90 parts of water.
Embodiment 3
[0046] A glass anti-fog cleaner, comprising the following raw materials in parts by weight:
[0047] Sorbitan Monolaurate 20 parts
[0048] Orthophosphoric acid 20 parts
[0049] 14 parts zinc chromate
[0050] Sulfated castor oil 12 parts
[0051] Sodium polypropoxybutyl ether sulfate 13 parts
[0052] Quick-drying agent 7 parts
[0053] 75 parts of water.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a glass antifogging detergent, belonging to the technical field of fine chemical engineering. The glass antifogging detergent is prepared from the following raw materials in parts by weight: 10-30 parts of sorbitan monolaurate, 15-25 parts of orthophosphoric acid, 9-18 parts of zinc chromate, 5-18 parts of sulfated castor oil, 5-18 parts of polypropoxybutyl ether sodium sulfate, 2-12 parts of quick-drying agent and 60-90 parts of water. By reasonably combining the sorbitan monolaurate and other raw materials, the detergent can quickly and effectively clean the glass, can be quickly dried, and can form an antifogging film on the glass surface to perform the antifogging function; and the antifogging efficacy time can reach one week and even longer.
Description
technical field [0001] The invention relates to a cleaning agent, more specifically, the invention relates to a glass anti-fog cleaning agent, which belongs to the technical field of fine chemicals. Background technique [0002] Glass is a transparent semi-solid and semi-liquid substance that forms a continuous network structure when it is melted, and is a silicate non-metallic material that gradually increases in viscosity and hardens during cooling. The composition of ordinary glass chemical oxides (Na2O·CaO·6SiO2), the main component is silicon dioxide. Widely used in buildings, used for wind and light transmission, belongs to the mixture. There are also colored glass that is mixed with certain metal oxides or salts to show color, and tempered glass made by a special method. Sometimes some transparent plastics (such as polymethyl methacrylate) are also called plexiglass. If the glass is washed directly with water, it will leave water marks, so it needs to be cleaned wi...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more