A kind of preparation method of nanocellulose/chitosan composite foam

A nanocellulose and composite foam technology, applied in the field of cellulose composite materials, can solve the problems of brittle texture, low thermal stability, poor biocompatibility, etc., achieve large porosity, small thermal conductivity and thermal expansion coefficient, high The effect of specific surface area

Active Publication Date: 2018-03-09
NORTHEAST FORESTRY UNIVERSITY
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a nanocellulose / chitosan composite foam in order to solve the problems of poor biocompatibility, brittle texture and low thermal stability of chitosan composite materials such as traditional foams and aerogels. Preparation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of nanocellulose/chitosan composite foam
  • A kind of preparation method of nanocellulose/chitosan composite foam

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0019] Specific embodiment one: the preparation method of nanocellulose / chitosan composite foam of the present embodiment is implemented according to the following steps:

[0020] 1. Carrying out chemical treatment on biomass raw materials containing cellulose to obtain purified cellulose, and then performing mechanical defibrillation treatment on the purified cellulose to prepare nanocellulose aqueous suspension;

[0021] Two, glacial acetic acid and distilled water are mixed, obtain glacial acetic acid solution, then add chitosan, magnetically stir evenly, obtain chitosan mixed solution;

[0022] 3. The nanocellulose aqueous suspension obtained in step one is mixed with the chitosan mixed solution obtained in step two, and the nanocellulose / chitosan composite solution is obtained after stirring;

[0023] 4. Carry out low-temperature freezing treatment to the nanocellulose / chitosan composite solution at -20° C. to obtain a frozen mixed solution;

[0024] 5. Drying the frozen...

specific Embodiment approach 2

[0027] Embodiment 2: This embodiment differs from Embodiment 1 in that the cellulose-containing biomass raw material in step 1 is wood, bamboo, cotton, hemp, bacterial cellulose or ascidian cellulose. Other steps and parameters are the same as those in Embodiment 1.

specific Embodiment approach 3

[0028] Embodiment 3: The difference between this embodiment and Embodiment 1 or 2 is that the chemical treatment in step 1 is sequentially treated with sodium chlorite solution and alkali solution. Other steps and parameters are the same as those in Embodiment 1 or Embodiment 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

A preparation method of nanocellulose / chitosan composite foam, the invention relates to the field of cellulose composite materials, it aims to solve the problem of poor biocompatibility of materials such as traditional foams and aerogels and low thermal stability of chitosan composite materials question. The preparation method of the composite foam: 1. Carry out chemical treatment and mechanical defibrillation treatment on the biomass raw material containing cellulose to prepare the nano-cellulose aqueous suspension; 2. Add chitosan to the glacial acetic acid solution to prepare a chitosan mixed solution 3. Mix the nanocellulose aqueous suspension with the chitosan mixed solution to obtain a nanocellulose / chitosan composite solution; 4. Carry out low-temperature freezing treatment to the composite solution; 5. Dry the frozen mixed solution , to obtain nanocellulose / chitosan composite foam. The raw materials used in the invention are all natural polymer materials, have good biocompatibility, low thermal volume shrinkage rate and good thermal stability.

Description

technical field [0001] The invention relates to the field of cellulose composite materials, in particular to a preparation method of nanocellulose / chitosan composite foam. Background technique [0002] At present, commonly used foam materials mainly include benzene board (EPS), polyurethane foam, pearl cotton, etc. Foam materials are widely used in thermal insulation materials, sound insulation materials, packaging materials, Vehicle and ship hulls and other fields. Although these foam materials have many advantages, due to the problems of non-renewable raw materials, poor biocompatibility and non-degradability, the existing foam materials are more or less harmful to the natural environment during the manufacturing and application process or after being discarded. The impact of the material, which in turn limits the application of the material in some fields. Cellulose and chitosan are the world's first and second largest natural renewable resources respectively. They are ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08J9/28C08L1/02C08L5/08
Inventor 陈文帅王宇舒于海鹏张奇刘一星
Owner NORTHEAST FORESTRY UNIVERSITY