Antirust coating for photovoltaic cell panel bracket
A technology for photovoltaic panels and anti-rust coatings, applied in anti-corrosion coatings, epoxy resin coatings, coatings, etc., can solve problems such as easy peeling of paint
Inactive Publication Date: 2015-04-29
SUZHOU RUNHONG TRADING
View PDF6 Cites 1 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0003] However, the general paint is very easy to fall off under conditions such as direct sunlight, rain, and temperature changes outdoors.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment
[0010] The rust-proof coating for photovoltaic panel support of the present embodiment comprises the following components by weight: 12 parts of dispersant, 22 parts of glycerin, 17 parts of epoxy resin, 3 parts of curing agent, 5 parts of talcum powder, 6 parts of nanoscale titanium dioxide parts, polystyrene 6 parts.
[0011] It also includes 11 parts of pigments and fillers; the pigments and fillers include components in parts by weight: 4 parts of graphite powder, 2 parts of aluminum powder and 9 parts of pigment.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention relates to an antirust coating for a photovoltaic cell panel bracket, and belongs to the technical field of preparation of high polymer materials. The coating comprises the following components in parts by weight: 12 parts of a dispersing agent, 22 parts of glycerol, 17 parts of epoxy resin, 3 parts of a curing agent, 5 parts of talcum powder, 6 parts of nanometer titanium dioxide and 6 parts of polystyrene. With glycerol as a solvent, the epoxy resin, nanometer titanium dioxide and polystyrene as main antirust components, the photovoltaic cell panel bracket provided by the invention can be kept stable in sunshine irradiation, rainwater, frost and day and night temperature change; and an aluminum alloy bracket of the photovoltaic cell panel can be relatively well protected.
Description
technical field [0001] The invention relates to an antirust paint for a photovoltaic battery panel support, which belongs to the technical field of polymer material manufacturing. Background technique [0002] Existing photovoltaic panel supports are mostly made of aluminum alloy, coated with paint so as to prevent rust and corrosion. [0003] But the general paint is very easy to fall off under conditions such as direct sunlight, rain, and temperature changes outdoors. Contents of the invention [0004] The technical problem to be solved by the invention is to propose an anti-rust paint for a photovoltaic panel support that can better prevent rust and corrosion in the natural environment. [0005] In order to solve the above-mentioned technical problems, the technical solution proposed by the present invention is: a kind of antirust paint for photovoltaic cell panel support, comprising the following components by weight: 12 parts of dispersant, 22 parts of glycerin, 17 p...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More IPC IPC(8): C09D163/00C09D7/12C09D5/08C09D5/10
CPCC09D163/00C09D5/103C09D7/61
Inventor 邢根海汤毅邢雪平
Owner SUZHOU RUNHONG TRADING