A kind of preparation method of ceramic lace

A lace and ceramic technology, applied in the field of inorganic non-metallic materials (ceramics), can solve the problems that the folding can no longer be realized, and the three-dimensional ceramic lace has not yet appeared, and achieves the effects of strong plasticity, tight integration and low production cost.

Active Publication Date: 2016-03-30
景德镇市隆祥陶瓷有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the characteristics of the ceramic material, the folded effect cannot be realized after setting the mesh. So far, although there are ceramic lace for flat decoration on the market, there has not been a three-dimensional ceramic lace that can be used for skirt decoration.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The first step is to configure lace mud

[0020] Configure 1000g of lace mud according to the weight percentage of the following lace mud formula:

[0021] Calcined kaolin 70g, clay 180g, quartz 150g, feldspar 260g, mica 240g, maltose 40g, epoxy resin 60g;

[0022] Then pass the configured mud through a 200-mesh vibrating screen and pass through a magnetic separator to remove iron, then crush the mud into a volume of 2cm 3 , Then soak in water for 9 hours, then ball mill for 13 hours to control the specific gravity of the grinding mud to be 58kg / cm 3 .

[0023] The second step is to configure the viscous agent and add it to the lace mud

[0024] Stir 330g of viscous agent and 1650g of 60℃ hot water to make a liquid, and adjust its specific gravity to 42kg / cm 3 Then, add it to the lace slurry after ball milling, and continue ball milling for 7 hours to control the specific gravity of the lace slurry to 59kg / cm 3 .

[0025] The composition of 330 g of the viscous agent is: a mixture...

Embodiment 2

[0046] The first step is to configure lace mud

[0047] Configure 1000g of lace mud according to the weight percentage of the following lace mud formula:

[0048] 120g calcined kaolin, 190g clay, 170g quartz, 220g feldspar, 200g mica, 30g maltose, 70g acrylic resin;

[0049] Then pass the configured mud through a 200-mesh vibrating screen and pass through a magnetic separator to remove iron, then crush the mud into a volume of 2cm 3 , Then soak in water for 11 hours, then ball mill for 15 hours to control the specific gravity of the grinding slurry to be 63kg / cm 3 .

[0050] The second step is to configure the viscous agent and add it to the lace mud

[0051] Stir 330g of viscous agent and 1650g of hot water at 60°C into a liquid state, and adjust its specific gravity to 43kg / cm 3 Then, add it to the lace slurry after ball milling, and continue to ball mill for 11 hours to control the specific gravity of the lace slurry to be 64kg / cm 3 .

[0052] The composition of 330 g of the viscous a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for preparing ceramic lace. Natural minerals and chemical raw materials are used. The weight percentage of the lace mud formula is: calcined kaolin 5-15%, clay 18-22%, quartz 15-20%, feldspar 22~26%, mica 20~25%, maltose 3~7%, resin 5~10%; after batching, sieving, iron removal, ball milling, adding viscous agent, making lace body, decorating ceramic body, firing Products are obtained, and the firing temperature range is: 1280-1300°C. The ceramic lace of the present invention is closely combined with the ceramic body after being fired in a reducing atmosphere, has clear mesh and strong three-dimensional effect, significantly improves the artistic effect of the ceramic product, and thus has broad market prospects.

Description

technical field [0001] The invention belongs to the field of inorganic non-metallic materials (ceramics), and in particular relates to a preparation method of ceramic lace. Background technique [0002] Lace first appeared in the United States. It is a hand-knitted product composed of many meshes knitted with silk threads or yarns according to a certain pattern. It is generally used on women's clothing, especially evening dresses and wedding dresses, to highlight the Noble and elegant status. Since the production of lace is a very complicated process, besides the need to set the mesh, it also needs to be consciously folded when decorating the skirt, so that it has a three-dimensional effect like water waves. But due to the self characteristic of ceramic material, can't realize the folding effect again after mesh is set, therefore although there is the ceramic lace that planar decoration is used on the market so far, the three-dimensional ceramic lace that can be used for sk...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/13C04B33/22C04B33/24C04B35/16C04B35/622
Inventor 阮礼祥
Owner 景德镇市隆祥陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com