Method for manufacturing unburned ceramic tile green body having permeable layer

A manufacturing method and technology of ceramic tiles, which are applied in the field of architectural ceramics, can solve problems such as poor three-dimensional effect and poor wear resistance of printed decorative layers, and achieve the effects of strong layer transition, easy operation, and rich colors

Inactive Publication Date: 2015-05-06
FOSHAN DONGPENG CERAMIC +2
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to solve the problems that the printed decorative layer formed by conventional inkjet printing is not wear-resistant and has poor three-dimensional effect in the prior art, and proposes a method for manufacturing a ceramic brick mud adobe with a permeable layer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] This embodiment provides a method for manufacturing a ceramic brick adobe with a permeable layer, and a ceramic brick manufactured using it.

[0039] A kind of manufacture method of the ceramic tile adobe with permeable layer, it comprises the steps:

[0040] A. Select the known base material and fabric for ceramic tiles. The fabric contains various components, such as some thread materials and particles. These thread materials and particles form textures in the fabric layer, and the bricks are formed by back-beating the cloth. The thickness of the fabric layer in the body is 1.2mm, and the adobe is dried;

[0041] B. After drying, the bricks are polished and polished. The blank throwing process uses 6-10 groups of 150-mesh emery grinding discs and 3-6 groups of wool felt grinding discs. The cutting amount of polishing and grinding is 0.3-1.2mm. Corresponding to this process, the cutting amount of polishing and grinding is 0.6-0.7mm. Of course, it can also be polished...

Embodiment 2

[0054] A kind of manufacture method of the ceramic tile adobe with permeable layer, it comprises the steps:

[0055] A, select known base material and lining for ceramic tiles, the lining is made of various powders, which contains line material, and the brick is formed through the cloth being punched, and the thickness of the lining layer in the green body is 2mm, and the brick is dried;

[0056] B. After drying, the bricks are polished and polished. The blank throwing process uses 6-10 groups of 150-mesh emery grinding discs and 3-6 groups of wool felt grinding discs. The cutting amount of polishing and grinding is 0.3-1.2mm. Corresponding to this process, the cutting amount of polishing and grinding is 0.5-0.7mm. Of course, it can also be polished and then dried. Through polishing, the texture in the fabric layer can be revealed. At the same time, after polishing, the capillary pores on the surface of the green body are also opened, which is more conducive to subsequent pene...

Embodiment 3

[0068] A kind of manufacture method of the ceramic tile adobe with permeable layer, it comprises the steps:

[0069] A. Select the known base material and lining for ceramic tiles. The lining is made of various powders, which contain thread materials. The bricks are formed by beating the cloth. The thickness of the lining layer in the green body is 0.8mm, and the bricks are dried;

[0070] B. After drying, the bricks are polished and polished. The blank throwing process uses 6-10 groups of 150-mesh emery grinding discs and 3-6 groups of wool felt grinding discs. The cutting amount of polishing and grinding is 0.3-1.2mm. Corresponding to this process, the cutting amount of polishing and grinding is 0.5-0.8mm. Of course, it can also be polished and then dried. Through polishing, the texture in the fabric layer can be revealed. At the same time, after polishing, the capillary pores on the surface of the green body are also opened, which is more conducive to subsequent penetration...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
penetration depthaaaaaaaaaa
penetration depthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a method for manufacturing an unburned ceramic tile green body having a permeable layer. The method comprises the following steps: A, polishing a dried unburned ceramic tile green body; B, carrying out ink-jet printing on organic permeable colored glaze ink; C, carrying out ink-jet printing on organic permeation-promoter ink; and D, drying for 10-60 minutes at a temperature of 50-200 DEG C. According to the invention, permeable layer formed on the ceramic tile brick prepared by using the unburned ceramic tile green body has a certain thickness, the permeated permeable layer is mutually combined with a precoat having a clear textured pattern after permeation to jointly constitute a three-dimensional decorative effect so that the decorative pattern is wear resistant, and the problems that the printed decorative layer formed by the conventional ink jet printing is free of three-dimensional layered sense and is not wear resistant and the like in the prior art are solved.

Description

technical field [0001] The invention relates to the technical field of building ceramics, in particular to a method for manufacturing a ceramic brick mud adobe with a permeable layer. Background technique [0002] Ceramic inkjet printing technology is a technology widely used in the production of ceramic tiles in recent years. It prints ink on the surface of bricks through nozzles instead of traditional screen printing, roller printing and other decorative methods. Because it is a non-contact printing, It can "print" concave-convex products without physical plate making, simple and rapid plate transfer, personalized production can be realized, and the production repeatability is good, so the scope of use is getting wider and wider. But its disadvantage is that the printed decorative layer is too shallow. At the same time, the ink has poor wear resistance after firing. With the extension of use time, the decorative effect will be greatly reduced. The process of applying tran...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/88
Inventor 曾权周燕谢穗
Owner FOSHAN DONGPENG CERAMIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap