Method for manufacturing decoration plate

A technology for decorative boards and pear wood, which is applied in the pretreatment of molding materials, flat products, manufacturing tools, etc., and can solve the problems of easy to leave fire, poor fire resistance, poor strength of decorative boards, etc.

Inactive Publication Date: 2015-05-13
ANHUI ROYAL JOHNNIE WOODEN PROD
View PDF10 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the progress of the times, people pay more and more attention to the decorative panels. While paying attention to the aesthetics of the panels, people also pay more and more attention to the safety of the panels, especially the strength and fire performance of the panels. However, the existing The strength of the decorative board is relatively poor, and the fire performance is also relatively poor, so it is easy to leave hidden dangers such as fire

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0013] The invention discloses a method for preparing a decorative plate, the specific steps are as follows:

[0014] Step 1: Peel the peeled pear wood into pieces with a peeler, and then put it into the cooking chamber for pre-cooking. The cooking time is 2-4 minutes, and the cooking temperature is 65°C-75°C;

[0015] Step 2: further cooking the precooked wood chips in step 1, the cooking time is 2-4min, and the cooking temperature is 175°C-180°C;

[0016] Step 3: Put the steamed wood chips in step 2 into the heat and grind them into pear wood fibers;

[0017] Step 4: Make molds of the same size according to the size of the decorative plate to be processed;

[0018] Step 5: Add magnesium oxychloride, magnesium bonding material modifier, pigment, and pear wood fiber into the mold, then add 12 times the mass of water and stir to form a slurry;

[0019] Step 6: Add phenolic resin into the mold, then add basalt fiber, roll and level it under a pressure of 1kg / cm 2 , drain the m...

Embodiment 1

[0022] The invention discloses a method for preparing a decorative plate, the specific steps are as follows:

[0023] Step 1: Peel the peeled pear wood into pieces with a peeler, and then put it into the cooking chamber for pre-cooking. The cooking time is 4 minutes, and the cooking temperature is 75°C;

[0024] Step 2: further cooking the pre-cooked wood chips in step 1, the cooking time is 3min, and the cooking temperature is 180°C;

[0025] Step 3: Put the steamed wood chips in step 2 into the heat and grind them into pear wood fibers;

[0026] Step 4: Make molds of the same size according to the size of the decorative plate to be processed;

[0027] Step 5: Add 50% magnesium oxychloride, 2% magnesium bonding material modifier, 3% pigment, and 15% pear wood fiber into the mold, then add 12 times the quality of water and stir to form a slurry;

[0028] Step 6: Add 5% phenolic resin into the mold, then add 25% basalt fiber, and roll it flat under a pressure of 1kg / cm 2 to d...

Embodiment 2

[0030] Step 1: Peel the peeled pear wood into pieces with a peeler, and then put it into the cooking chamber for pre-cooking. The cooking time is 3 minutes, and the cooking temperature is 70°C;

[0031] Step 2: further cooking the precooked wood chips in step 1, the cooking time is 2min, and the cooking temperature is 180°C;

[0032] Step 3: Put the steamed wood chips in step 2 into the heat and grind them into pear wood fibers;

[0033] Step 4: Make molds of the same size according to the size of the decorative plate to be processed;

[0034] Step 5: Add 50% magnesium oxychloride, 1% magnesium bonding material modifier, 4% pigment, and 20% pear wood fiber into the mold, then add 12 times the quality of water and stir to form a slurry;

[0035] Step 6: Add 5% phenolic resin into the mold, then add 20% basalt fiber, and roll it flat under a pressure of 1kg / cm 2 to drain the moisture in the mold. After curing at 45°C, the plate is formed.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for manufacturing a decoration plate. The method particularly includes the steps that pearwood without peel is cut into sheets through a peeling machine, and then the sheets are placed into a stewing bin for pre-stewing; the pre-stewed wood sheets are further stewed; hot grinding is carried out on the stewed wood sheets to form pearwood fibers; a mold is manufactured; magnesium oxychloride, a magnesium binding material modifying agent, pigments and the pearwood fibers are added into the mold, 12-fold water is added to form sizing agents in a stirring mode; phenolic resin is added into the mold, then basalt fibers are added, rolling and leveling are carried out, moisture in the mold is discharged, and the plate is molded after solidification is carried out. The method has the advantages that the manufactured decoration plate is high in strength, and the fireproof performance is good.

Description

technical field [0001] The invention relates to a method for preparing a decorative plate, which is applied in the field of decorative plate processing. Background technique [0002] With the progress of the times, people pay more and more attention to the decorative panels. While paying attention to the aesthetics of the panels, people also pay more and more attention to the safety of the panels, especially the strength and fire performance of the panels. However, the existing The strength of the decorative board is relatively poor, and the fire performance is also relatively poor, so it is easy to leave hidden dangers such as fire. Contents of the invention [0003] In order to solve the defects of the prior art solutions, the invention discloses a preparation method of the prepared decorative board with high strength and good fireproof performance. [0004] The invention discloses a method for preparing a decorative plate, the specific steps are as follows: [000...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B27N3/08B27N3/04
CPCB27N3/12B27N1/00
Inventor 常明金家虎陈伦发
Owner ANHUI ROYAL JOHNNIE WOODEN PROD