High-altitude mark paint and preparation method thereof

A technology of marking paint and active solvent, which is applied in the field of paint and coatings, can solve the problems of surface corrosion, foul corrosion, short life, atmospheric aging, etc., achieve good atmospheric aging resistance, excellent gloss and color retention, and reduce construction costs. effect of difficulty

Inactive Publication Date: 2015-05-20
MAANSHAN NIUZE TECH SERVICE
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The sign protection on concrete structures such as concrete chimneys and transmission poles is at high altitude, the phenomenon of atmospheric aging is serious, and it is often corroded by acidic environments. The surface corrosion, attached organisms and dirty corrosion are very serious and prone to danger
When general anti-corrosion paints are used in concrete structures such as concrete chimneys and transmission poles, the film formation is thin, the adhesion is low, the surface treatment requirements are strict, the construction process is complicated, there are technical problems such as atmospheric corrosion, serious environmental pollution and short life, so it cannot be used very well. Meet the needs of the market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A high-altitude marking paint is prepared by the following raw materials in parts by mass:

[0028] 20 parts of chlorosulfonated polyethylene resin;

[0029] 5 parts of synthetic resin;

[0030] 10 parts weather-resistant filler;

[0031] 1 part vulcanizing agent;

[0032] 10 parts of curing agent;

[0033] Accelerator 1 part;

[0034] Active solvent 100 parts.

[0035] The preparation steps of a kind of preparation method of high-altitude marking paint are as follows:

[0036] Preparation of Component A: Take 70 parts of active solvent, heat it to 50°C, add chlorosulfonated polyethylene resin and synthetic resin weighed according to the ratio while stirring the active solvent, make it miscible, transfer it into a stirring container, keep The rotation speed is 1200r / min. After it is fully mixed, add weather-resistant fillers, keep the rotation speed at 1500r / min and continue to stir for 20min, let it stand, and filter to obtain component A;

[0037] Preparation o...

Embodiment 2

[0039] A high-altitude marking paint is prepared by the following raw materials in parts by mass:

[0040] 25 parts of chlorosulfonated polyethylene resin;

[0041] 8 parts of synthetic resin;

[0042] 13 parts of weather-resistant filler;

[0043] 2 parts of vulcanizing agent;

[0044] 13 parts of curing agent;

[0045] Accelerator 2 parts;

[0046] Active solvent 100 parts.

[0047] The preparation steps of a kind of preparation method of high-altitude marking paint are as follows:

[0048] Preparation of Component A: Take 70 parts of active solvent, heat it to 50°C, add chlorosulfonated polyethylene resin and synthetic resin weighed according to the ratio while stirring the active solvent, make it miscible, transfer it into a stirring container, keep The rotation speed is 1200r / min. After it is fully mixed, add weather-resistant fillers, keep the rotation speed at 1500r / min and continue stirring for 20min, let it stand, and filter to obtain component A;

[0049] Prep...

Embodiment 3

[0051] A high-altitude marking paint is prepared by the following raw materials in parts by mass:

[0052] 25 parts of chlorosulfonated polyethylene resin;

[0053] 8 parts of synthetic resin;

[0054] 15 parts weather-resistant filler;

[0055] 3 parts of vulcanizing agent;

[0056] 13 parts of curing agent;

[0057] Accelerator 3 parts;

[0058] Active solvent 120 parts.

[0059] The preparation steps of a kind of preparation method of high-altitude marking paint are as follows:

[0060] Preparation of Component A: Take 80 parts of active solvent, heat it to 50°C, add chlorosulfonated polyethylene resin and synthetic resin weighed according to the ratio while stirring the active solvent, make it miscible, transfer it into a stirring container, keep The rotation speed is 1500r / min. After it is fully mixed, add weather-resistant fillers, keep the rotation speed at 1800r / min and continue stirring for 20min, let it stand, and filter to obtain component A;

[0061] Prepara...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses high-altitude mark paint. The paint is prepared from the following raw materials in parts by mass: 20-35 parts of chlorosulfonated polyethylene resin, 5-15 parts of synthesized resin, 10-20 parts of weather-resistance filler, 1-5 parts of a vulcanizing agent, 10-20 parts of a curing agent, 1-5 parts of accelerant and 100-150 parts of active solvent. The high-altitude mark paint has the characteristics of strong atmospheric aging resistance, good resistance to acid, alkali and salt.

Description

technical field [0001] The invention relates to a high-altitude marking paint and a preparation method thereof, which are applied to paints and coatings. Background technique [0002] The sign protection on concrete structures such as concrete chimneys and transmission poles is at high altitude, the phenomenon of atmospheric aging is serious, and they are often corroded by acidic environments. When general anti-corrosion paints are used in concrete structures such as concrete chimneys and transmission poles, the film formation is thin, the adhesion is low, the surface treatment requirements are strict, the construction process is complicated, there are technical problems such as atmospheric corrosion, serious environmental pollution and short life, so it cannot be used very well. Meet the needs of the market. Contents of the invention [0003] The present invention is to avoid the disadvantages of the above-mentioned prior art, and provides a kind of high-altitude marking...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D123/34C09D163/00C09D7/12C09D5/08
CPCC09D123/34C08L2201/08C09D5/08C09D7/61C09D7/63C08L63/00C08K13/02C08K2003/265C08K2003/325C08K3/34C08K2003/3045
Inventor 王晓娜
Owner MAANSHAN NIUZE TECH SERVICE