Infiltration method of high compaction density anode power battery

A power battery, high-pressure compaction technology, applied in battery electrodes, secondary battery manufacturing, circuits, etc., can solve the problems of difficult infiltration of low-porosity negative electrode sheets and high liquid loss of battery cells, achieve enhanced calendar life, and improve battery life. , the effect of high efficiency

Active Publication Date: 2015-05-27
WANXIANG 123 CO LTD
View PDF5 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the defects that the low-porosity negative electrode sheet is generally difficult to infiltrate and the liquid loss of the battery cell is high due to the room temperature infiltration method of the current power battery, the present invention provides a method for infiltration of a high-pressure negative electrode power battery

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Infiltration method of high compaction density anode power battery
  • Infiltration method of high compaction density anode power battery

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The flow chart of infiltration method of the present invention sees figure 1 ,Specific steps are as follows:

[0025] A. Vacuum shelving: Place the battery cell that has just been injected with electrolyte but has not been sealed once in a vacuum box. The battery cell is placed at an angle of 60-90 degrees. Time 10 minutes to 15 minutes;

[0026] B. Shelving at high temperature: Aging the battery core after vacuum shelving and sealing once at a temperature of 33°C-38°C, placing the battery cell at an angle of 30-60 degrees, with the air bag of the battery cell upward, and the shelf time is 10 hours to 12 hours;

[0027] C. Degassing: Take out the battery cell after high temperature storage, and perform air extraction and edge sealing on the vacuum pumping equipment. The vacuum degree is -0.092MPa, and the pumping time is 2 seconds to reduce the internal pressure of the cell The liquid loss of the cell after gas is 0.2g~0.8g, while the liquid loss of the normal temper...

Embodiment 2

[0034] The flow chart of infiltration method of the present invention sees figure 1 ,Specific steps are as follows:

[0035] A. Vacuum shelving: Place the battery cell that has just been injected with electrolyte but has not been sealed once in a vacuum box. The battery cell is placed at an angle of 60-90 degrees. Time 10 minutes to 15 minutes;

[0036] B. Shelving at high temperature: Aging the battery core after vacuum shelving and sealing once at a temperature of 33°C-38°C, placing the battery cell at an angle of 30-60 degrees, with the air bag of the battery cell upward, and the shelf time is 10 hours;

[0037] C. Degassing: Take out the battery cell after high temperature storage, and perform air extraction and edge sealing on the vacuum pumping equipment. The vacuum degree is -0.092MPa, and the pumping time is 2 seconds to reduce the internal pressure of the cell The liquid loss of the cell after gas is 0.2g, while the liquid loss of the normal temperature immersion me...

Embodiment 3

[0044] The flow chart of infiltration method of the present invention sees figure 1 ,Specific steps are as follows:

[0045] A. Vacuum shelving: Place the battery cell that has just been injected with electrolyte but has not been sealed once in a vacuum box. The battery cell is placed at an angle of 60-90 degrees. Time 10 minutes to 15 minutes;

[0046] B. Shelving at high temperature: Aging the batteries after vacuum shelving and sealing once at a temperature of 33°C-38°C, placing the batteries at an angle of 30-60 degrees, with the airbag of the batteries facing upwards, and placing them for 12 hours;

[0047] C. Degassing: Take out the battery cell after high temperature storage, and perform air extraction and edge sealing on the vacuum pumping equipment. The vacuum degree is -0.092MPa, and the pumping time is 2 seconds to reduce the internal pressure of the cell The liquid loss of the cell after gas is 0.8g, while the liquid loss of the normal temperature immersion metho...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an infiltration method of a high compaction density anode power battery. The infiltration method comprises following steps: A, vacuum shelving, wherein before one time sealing, an electrical core which is processed via electrolyte injection is delivered into a vacuum chamber, and is disposed with an angle of 60 to 90 DEG C, vacuum degree of the vacuum chamber is controlled to be -0.085 to -0.09MPa, and shelving time ranges from 10 to 15min; B, high-temperature shelving; C, degassing; D, rolling; E, secondary high-temperature shelving; F, precharging, wherein the electrical core processed via step E is subjected to precharging on a charging equipment with currents of 0.007C, 0.01C, 0.1C, and 0.2 C respectively, charging upper limited voltages are 3.17V, 3.17V, 3.17V, and 3.47V respectively, and charging time is controlled to be 50min, 70min, 120min, and 300min respectively; G, degassing; H, secondary rolling, wherein the electrical core processed via step G is subjected to secondary rolling based on step D so as to complete high compaction density anode power battery infiltration. The infiltration method is capable of simplifying low porosity anode plate general infiltration, and reducing electrical core liquid loss.

Description

technical field [0001] The invention relates to a method for preparing a battery, in particular to an infiltration method for a high-pressure negative electrode power battery. Background technique [0002] At present, the infiltration method of the power battery includes the following steps: 1. Infiltration at room temperature: After the cell is injected with liquid, it is left at 23°C to 28°C for 40 to 48 hours to allow the electrolyte to penetrate into the cell, and then through pre-charging, Make the electrolyte infiltrate the inside of the pole piece coating; 2. High temperature infiltration: After the cell is injected, it is left at 33°C to 38°C for 30 hours to 38 hours, so that the electrolyte penetrates into the inside of the cell, and then pre-charged , so that the electrolyte infiltrates the inside of the pole piece coating. [0003] Such as the application number: 201210581823.9 application date: 2012-12-27, a Chinese invention discloses a diaphragm infiltration m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H01M10/04
CPCH01M4/04H01M4/139H01M10/04Y02E60/10Y02P70/50
Inventor 李凡群苏文俊谭歌朱修锋高新宝陈军
Owner WANXIANG 123 CO LTD