Process for forming aramid copolymers

A technology for polymers and polymer solutions, which is applied in the field of preparing aromatic polyamide polymers, and can solve problems such as not allowing the preparation of aromatic polyamide polymers

Active Publication Date: 2017-05-10
DUPONT SAFETY & CONSTR INC
View PDF17 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The prior art does not allow the preparation of aramid polymers comprising DAPBI in high solids content reactions while obtaining polymers with high inherent viscosity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process for forming aramid copolymers
  • Process for forming aramid copolymers
  • Process for forming aramid copolymers

Examples

Experimental program
Comparison scheme
Effect test

example

[0057] NMP, CaCl 2 , DAPBI, PPD and TCl were obtained from commercial sources.

example 1

[0059] Add 5.38% CaCl to the FM130D Littleford reactor 2 31.82 kg of NMP solvent ("c" value 5.38). Then 2180 g of DAPBI ("b" value 70) was added. The contents were then cooled to 10°C. 707 g of terephthaloyl chloride was added to form a prepolymer solution. The prepolymer solution was then cooled to 10°C, and 455 g of PPD ("y" value 30) was dissolved in the prepolymer mixture. Then 2122 g of terephthaloyl dichloride were added. The product of (b×c) of the polymer is equal to 377.

[0060] The reaction had 12% solids on a polymer basis and 14.7% solids on a total monomer basis. The final inherent viscosity was 6.5 dl / g.

example 2

[0068] Example 1 was repeated, however adding terephthaloyl dichloride to DAPBI in three additions. After each addition, the mixture was cooled to 10 °C. The result was a polymer solution and polymer similar to Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to a method of forming polymer crumbs comprising 2-(4-aminophenyl)-5(6)-aminophenylbenzimidazole (DAPBI), p-phenylenediamine (PPD) and the residue of terephthaloyl dichloride (TCl), the method comprising the steps of: i) forming a slurry of b mole % DAPBI in a solvent system comprising an organic solvent and c weight % of an inorganic salt , wherein the inorganic salt is present in an amount of at least 5% by weight of the organic solvent; ii) contacting the slurry with a substoichiometric amount of terephthaloyl chloride to form a prepolymer solution; and iii) making The prepolymer solution is contacted with y mole % of PPD and additional TCL to form a polymer solution; wherein the total amount of TCL added in steps ii) and iii) is equal to the amount of DAPBI added in steps i) and iii) and A stoichiometric amount based on the total amount of PPD; the DAPBI and PPD are added in an amount sufficient to provide a polymer-based polymer solution having a weight percent solids of 12% or greater; and wherein the sum of y+b is 100 , and the product of b×c is 225 or greater.

Description

technical field [0001] This patent application relates to a process for the preparation of aromatic polyamide polymers derived from 5(6)-amino-2-(p-aminophenyl)benzimidazole (DAPBI), p-phenylenediamine (PPD) and terephthaloyl dichloride (TCl), capable of forming fibers with excellent physical properties. Background technique [0002] Derived from 5(6)-amino-2-(p-aminophenyl)benzimidazole (DAPBI), p-phenylenediamine (PPD) and terephthaloyl dichloride (TCl, also commonly known as terephthaloyl dichloride Acyl chloride) fibers are known in the art. Such copolymers are Russian-made high-strength fibers (for example under the trade name and )Foundation. See Russian Patent Application 2,045,586. U.S. Patent 4,172,938 discloses a process for preparing aramid polymers using N-methyl-2-pyrrolidone (NMP) containing at least 1.5 but less than 5% by weight CaCl 2 solvent. [0003] The prior art does not allow the preparation of aramid polymers comprising DAPBI in high solids co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G69/32C08G69/04C08G73/18
CPCC08G69/04C08G69/32C08G73/18
Inventor F.K.马伦
Owner DUPONT SAFETY & CONSTR INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com